A kind of algal calcium inorganic ecological paint and preparation method thereof

An inorganic and ecological technology, applied in coatings and other directions, can solve problems such as VOC volatile pollution, and achieve the effect of increasing the gloss of the coating film, using safety, and improving the hiding power of the coating film.

Active Publication Date: 2018-05-11
湖北格林森绿色环保材料股份有限公司
View PDF20 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The characteristics of the above five disclosed technologies are mainly based on shell powder, mixed with nano-titanium dioxide, tourmaline powder, etc., using environmentally friendly shells as raw materials to solve functional problems and sustainability, but still retain the use of organic synthetic polymers. Improvement of film-forming substances or adhesives and various additives, potential VOC volatile pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of algal calcium inorganic ecological paint and preparation method thereof
  • A kind of algal calcium inorganic ecological paint and preparation method thereof
  • A kind of algal calcium inorganic ecological paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 1, a kind of raw material component of calcium algae inorganic ecological paint (substance measurement unit is all by weight percentage):

[0041] (1) Algae: 5.5% of white diatomite, which is loaded with titanium dioxide or bleached, and its particle size is 600 mesh;

[0042] (2) Calcium-containing inorganic matrix: calcium sulfate hemihydrate 18%, shell calcium carbonate 22%, the whiteness of the calcium-containing inorganic matrix is ​​> 85, the calcium oxide content > 40%, and its particle size is 400 mesh;

[0043] (3) Environmental mineral micropowder: 2.4% of negative ion powder, the environmental mineral micropowder is the environmental mineral micropowder after coating and loading treatment with doping elements or transition elements, its whiteness > 78, and particle size is 600 mesh;

[0044] (4) Nano titanium dioxide: 1.5%;

[0045] (5) Silicate stimulating colloid: 10.3%, the preparation method of this silicate stimulating colloid: first mix 34% potassium s...

Embodiment 2

[0058] 1, a kind of raw material component of calcium algae inorganic ecological paint (substance measurement unit is all by weight percentage):

[0059] (1) Algae: 8.0% of white diatomite, which is loaded with titanium dioxide or bleached, and its particle size is 400 mesh;

[0060] (2) Calcium-containing inorganic matrix: 20% of shell calcium carbonate, 20% of shell calcium oxide, the whiteness of the calcium-containing inorganic matrix is ​​>85, the calcium oxide content is >40%, and its particle size is 600 mesh;

[0061] (3) Environmental mineral micropowder: negative ion powder 1.8%, sepiolite 2.4%, the environmental mineral micropowder is the environmental mineral micropowder treated by doping element or transition element coating load, its whiteness > 78, particle size is 400 mesh ;

[0062] (4) Nano titanium dioxide: 1.5%;

[0063] (5) Silicate stimulating colloid: 10.3%, the preparation method of this silicate stimulating colloid: first mix 34% potassium silicate (...

Embodiment 3

[0076] 1, a kind of raw material component of calcium algae inorganic ecological paint (substance measurement unit is all by weight percentage):

[0077](1) Algae: 3.0% of white diatomite, which is loaded with titanium dioxide or bleached, and its particle size is 500 mesh;

[0078] (2) Calcium-containing inorganic matrix: calcium sulfate hemihydrate 6%, shell calcium carbonate 20%, heavy calcium powder 6%, light calcium powder 6%, the whiteness of the calcium-containing inorganic matrix is ​​> 85, and the calcium oxide content > 40%, the particle size is 500 mesh;

[0079] (3) Environmental mineral micropowder: negative ion powder 1.0%, seagullite micropowder 1.0%, attapulgite 1.0%, sepiolite 1.0%, the environmental mineral micropowder is an environmental mineral coated with doping elements or transition elements Micropowder, the whiteness of which is >78, and the particle size is 500 mesh;

[0080] (4) Nano titanium dioxide: 2.0%;

[0081] (5) Silicate stimulating colloid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an algae and calcium containing inorganic ecological coating and a preparation method thereof. The algae and calcium containing inorganic ecological coating comprises raw materials in percentage by weight as follows: 3%-8% of algae, 37%-40% of calcium containing inorganic matrixes, 1.5%-4.2% of environmental mineral powder, 1%-2% of nano titanium dioxide, 8%-12% of silicate excited colloid, 0.15%-0.4% of a retarder, 2.5%-4.25% of a dispersing agent and 30%-41% of deionized water, wherein the percentages of all the components add up to 100%. The silicate excited colloid is taken as a film forming matrix and reacts with active silicon and a calcium source component, the film forming performance, the film strength, the attachment and the wear resistance of the coating are improved, and the coating further has the characteristics of nature, environmental protection, no VOC (volatile organic compounds) pollution, various ecological functionality, simple process and excellent weather resistance.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an algal calcium inorganic ecological coating and a preparation method thereof. Background technique [0002] Now general-purpose coatings (emulsion paints) are composed of four components: (1) film-forming substances: mainly polymer emulsions; (2) pigments and fillers: mainly titanium dioxide, calcium carbonate, pigments, etc.; (3) Water; (4) Auxiliaries: mainly composed of various polymer synthetic organic substances such as film-forming aids, defoamers, thickeners, leveling agents, preservatives, and antifreeze agents. Indoor pollution caused by paints, human health hazards caused by many VOCs (volatile organic compounds) in paints, and the frequent exposure rate of unqualified batches of paints from many brands have long been known. The development of environmentally friendly and resource-saving paints is an important aspect of the paint industry. The mainstream o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00
CPCC09D1/00
Inventor 韦华童军聂松荣
Owner 湖北格林森绿色环保材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap