Paper made through stearic acid modified nanometer titanium dioxide, and preparation method thereof
A technology of nano-titanium dioxide and stearic acid, applied in the field of filled paper
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] A kind of paper made of stearic acid modified nano-titanium dioxide is prepared according to the following steps:
[0029] (1) First make aluminum sulfate into an aqueous solution with a mass concentration of 5%, impregnate the filter paper for 1 min, and place the filter paper at 100 o C under drying number;
[0030] (2) Put stearic acid with a concentration of 5% in ethanol, add nano-titanium dioxide in the ratio of nano-titanium dioxide: stearic acid = 1:1, and disperse it in stearic acid-ethanol solution to obtain stearic acid containing nano-titanium dioxide - ethanol solution, pulling and dipping the filter paper impregnated with aluminum sulfate mentioned in step (1) in the ethanol solution of stearic acid-nano-titanium dioxide for several times; after that, air-drying for 24 hours to obtain.
Embodiment 2
[0032] A kind of paper made of stearic acid modified nano-titanium dioxide is prepared according to the following steps:
[0033] (1) First make aluminum sulfate into an aqueous solution with a mass concentration of 20%, impregnate the filter paper for 3 minutes, and place the filter paper at 105 o Drying number at C; (2) Put 9% stearic acid in ethanol, add nano-titanium dioxide in the ratio of nano-titanium dioxide: stearic acid = 1:4, disperse in stearic acid-ethanol solution, and oscillate for 8 minutes Obtain the stearic acid-ethanol solution containing nano-titanium dioxide, and coat the prepared stearic acid-ethanol solution on the surface of the filter paper with a paint scraper, and the coating amount should be controlled to be 8g / m 2 ; Afterwards, the impregnated filter paper was dried at 105° C. for 15 minutes in a constant-temperature blast drying oven to obtain a final product.
PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
boiling point | aaaaa | aaaaa |
refractive index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com