Antireflection and self-cleaning thin film and preparation method thereof

A self-cleaning, anti-reflection technology, applied in final product manufacturing, sustainable manufacturing/processing, photovoltaic power generation, etc., can solve problems such as difficulty in adapting to wind sand, hail, solar panel surface contamination, and affecting the efficiency of battery modules. , to achieve good self-cleaning ability, degrade surface organic contamination, and improve the effect of capturing ability

Active Publication Date: 2016-04-20
SHANGHAI ADVANCED RES INST CHINESE ACADEMY OF SCI
View PDF9 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] It is worth noting that although the above-mentioned nanostructure anti-reflection coating has excellent optical properties, its submicron structure has poor mechanical properties, and it is difficult to adapt to the severe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antireflection and self-cleaning thin film and preparation method thereof
  • Antireflection and self-cleaning thin film and preparation method thereof
  • Antireflection and self-cleaning thin film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] This embodiment provides a method for preparing an anti-reflection self-cleaning film, including: using imprinting technology and surface modification technology to process a three-dimensional pattern structure with a micron size on the transparent flexible film, so that the transparent flexible film has anti-reflection self-cleaning properties. Clean performance.

[0058] As an example, the embossing technology includes one of UV embossing, thermal embossing, thermal curing embossing, and micro-contact embossing, wherein the thermal embossing includes flat-bed embossing, roll-to-plate embossing, and A type of roll-to-roll embossing.

[0059] As an example, the UV embossing includes: coating a UV-curable glue on a transparent flexible film, then embossing the cured glue with a mold with a micron structure pattern, and separating the template from the substrate after being irradiated and cured by a UV lamp, that is Obtain the anti-reflection self-cleaning film.

[0060...

Embodiment 2

[0097] This embodiment provides a method for preparing an anti-reflection self-cleaning film, wherein, in this embodiment, the preparation process of the anti-reflection self-cleaning film prepared by a two-step hot pressing method is as follows:

[0098] Step 1), the clean ETFE film is embossed by means of roll-to-roll or roll-to-plate hot pressing, the hot pressing temperature is 120°C, and the surface structure of the roller is jagged (sawtooth period is 50 μm, height is 30 μm), The pressure between the two rollers is 10MPa, and the temperature and pressure of the instrument reach the set value.

[0099] Step 2), preheat the clean ETFE film on a heating plate at 50°C for 15s, and roll it at a speed of 7m / min to obtain an anti-reflection self-cleaning film, such as Figure 5c shown.

[0100] Step 3), the anti-reflection self-cleaning film prepared in step 2) (specifically ETFE anti-reflection hydrophobic film), the fourth hot-melt adhesive, solar cell glass cover plate, the...

Embodiment 3

[0102] This embodiment provides a method for preparing an anti-reflection self-cleaning film, wherein, in this embodiment, the preparation process of the anti-reflection self-cleaning film prepared by a two-step hot pressing method is as follows:

[0103] Step 1), use roll-to-roll or roll-to-plate hot pressing to emboss the clean ETFE film, the hot pressing temperature is 120°C, and the structure of the roller surface is sawtooth (the sawtooth period is 50 μm, and the height is 25 μm), The pressure between the two rollers is 10MPa, and the temperature and pressure of the instrument reach the set value.

[0104] Step 2), preheat the clean ETFE on a heating plate at 50°C for 15s, and roll it at a speed of 7m / min to obtain an anti-reflection self-cleaning film, such as Figure 5c shown.

[0105] Step 3), the backboard material (polyester film with waterproof vapor performance, its structure is a three-layer film composite material, wherein, the lower film is a resin containing f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Water contact angleaaaaaaaaaa
Roll angleaaaaaaaaaa
Login to view more

Abstract

The invention provides an antireflection and self-cleaning thin film and a preparation method thereof. According to the preparation method, a solid figure structure of a micron size is processed on a transparent flexible thin film through adopting imprinting technologies and surface modification technologies, so that the transparent flexible thin film has antireflection and self-cleaning performance; the antireflection and self-cleaning thin film is integrated on the window layer of a solar battery assembly, and as a result, the surface reflection of the window layer can be effectively inhibited, and the number of photons entering the absorption layer of a battery can be increased; and therefore, the photoelectric conversion efficiency of the battery can be improved, and especially, the efficiency of the battery can be improved more significantly when sunlight obliquely enters the battery. A super hydrophobic film or a super hydrophilic film can be selected as the antireflection and self-cleaning thin film of the invention; since the super hydrophobic film has a high water contact angle, when the super hydrophobic film tilts, water droplets are very easy to roll down and take away surface pollutants, and therefore, a self-cleaning effect can be realized; and based on the photocatalysis, the super hydrophilic film can degrade surface organic contaminations, and therefore, a self-cleaning effect can be also realized.

Description

technical field [0001] The invention belongs to the field of functional films, in particular to an anti-reflection self-cleaning film and a preparation method thereof. Background technique [0002] With the continuous consumption of fossil energy and the aggravation of environmental pollution, solar energy, as a clean and renewable new energy, has been valued by countries all over the world. Solar photovoltaic power generation is a technology that uses the photoelectric effect of semiconductors to directly convert light energy into electrical energy, and is one of the main new energy technologies. [0003] The large-scale promotion of photovoltaic power generation mainly depends on the improvement of its own efficiency and cost reduction. On the one hand, the efficiency can be improved by researching and optimizing the material of the semiconductor absorbing layer, adjusting the interface and energy band of the material, thereby broadening the absorption spectrum, improving...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/0232H01L31/0236H01L31/18B82Y40/00
CPCB82Y40/00H01L31/02327H01L31/02366H01L31/1876H01L31/0232H01L31/0236H01L31/18Y02E10/50Y02P70/50
Inventor 李东栋王敏马朋莎陈小源鲁林峰殷敏程伟杰刘东方方小红
Owner SHANGHAI ADVANCED RES INST CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap