Making process of Christmas tree trunk
A preparation process and technology for Christmas trees, which can be applied to household utensils, floor fabrics, religious or sacrificial utensils, etc. It can solve the problems of complicated production and affect the decoration effect, and achieve the effect of low cost and diverse products.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] The preparation technology of Christmas tree pole, comprises the following steps:
[0025] S1, powder-baking the iron rod with the iron fork ring;
[0026] S2, stirring the styrofoam and the feel glue evenly;
[0027] S3, coating the evenly stirred glue paddle of S2 on the surface of the iron rod, and then foaming;
[0028] S4, soaking the foamed iron rod;
[0029] S5, color-sweeping the soaked iron rod to obtain the desired Christmas tree rod.
[0030] Specifically, in S1, the iron rod with the iron fork ring is first pickled to remove the surface oil, and then powder is sprayed on the surface of the iron rod with the iron fork ring to form a powder layer with a thickness of 30 μm, and then baked at 120 ° C. Bake for 30 minutes, that is, a powder baking varnish layer is formed on the iron rod with the iron fork ring. Among them, the powder baking varnish is hardware powder baking varnish, which is purchased directly from the market.
[0031] Specifically, in S2, t...
Embodiment 2
[0038] The preparation technology of Christmas tree pole, comprises the following steps:
[0039] S1, powder-baking the iron rod with the iron fork ring;
[0040] S2, stirring the styrofoam and the feel glue evenly;
[0041] S3, coating the evenly stirred glue paddle of S2 on the surface of the iron rod, and then foaming;
[0042] S4, soaking the foamed iron rod;
[0043] S5, color-sweeping the soaked iron rod to obtain the desired Christmas tree rod.
[0044] Specifically, in S1, the iron rod with the iron fork ring is first pickled to remove the surface oil, and then powder is sprayed on the surface of the iron rod with the iron fork ring to form a powder layer with a thickness of 200 μm, and then baked at 250 ° C. Bake for 8 minutes, that is, a powder baking varnish layer is formed on the iron rod with the iron fork ring.
[0045] Specifically, in S2, the weight ratio of the styrofoam to the feel glue is 1:1.
[0046] Specifically, in S3, foaming was performed for 30 m...
Embodiment 3
[0050] The preparation technology of Christmas tree pole, comprises the following steps:
[0051] S1, powder-baking the iron rod with the iron fork ring;
[0052] S2, stirring the styrofoam and the feel glue evenly;
[0053] S3, coating the evenly stirred glue paddle of S2 on the surface of the iron rod, and then foaming;
[0054] S4, soaking the foamed iron rod;
[0055] S5, color-sweeping the soaked iron rod to obtain the desired Christmas tree rod.
[0056] Specifically, in S1, the iron rod with the iron fork ring is first pickled to remove surface oil, and then powder is sprayed on the surface of the iron rod with the iron fork ring to form a powder layer with a thickness of 100 μm, and then baked at 150 ° C. Bake for 20 minutes, that is, a powder baking varnish layer is formed on the iron rod with the iron fork ring.
[0057] Specifically, in S2, the weight ratio of the styrofoam to the feel glue is 1:0.5.
[0058] Specifically, in S3, foaming was performed for 40 mi...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |