Acid soluble mineral fiber fine bridging agent, bridging fluid and preparation method thereof

A mineral fiber and plugging agent technology, applied in chemical instruments and methods, drilling compositions, etc., can solve the problems of time-consuming and labor-consuming, complicated preparation of plugging agent for bridge plugging, and inability to fully guarantee high temperature resistance, etc., to achieve Good plugging effect

Active Publication Date: 2016-07-06
XINJIANG LUMING TECH CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention provides a kind of acid-soluble mineral fiber thin bridge plug leakage agent and leakage prevention liquid and its preparation method, which overcomes the deficiencies of the above-mentioned prior art, It can effectively solve the problems of complex preparation of existing bridge plugging agents, time-consuming and labor-consuming, inability to fully guarantee high temperature resistance, high pressure and high acid solubility, and poor plugging effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, the acid-soluble mineral fiber fine bridging plugging agent, the raw material contains 30 to 40 parts of limestone, 18 to 30 parts of mica, 10 to 20 parts of asbestos, and 3 to 15 parts of vermiculite in parts by weight. 1 to 5 parts of cotton wool, 1 to 15 parts of acidified fiber, 1 to 10 parts of one-way pressure sealant, 1 to 5 parts of delayed expansion agent, and 0.1 to 2 parts of viscosity reducer; wherein: The particle size of limestone is 0.045mm to 2.5mm, the particle size of mica is 1.4mm to 2.5mm, and the particle size of vermiculite is 0.3mm to 2.0mm.

Embodiment 2

[0030] Embodiment 2, the acid-soluble mineral fiber fine bridge plugging agent, raw materials contain 30 or 40 parts of limestone, 18 or 30 parts of mica, 10 or 20 parts of asbestos, and 3 or 15 parts of vermiculite by weight. 1 or 5 parts of cotton wool, 1 or 15 parts of acidifiable fiber, 1 or 10 parts of one-way pressure sealant, 1 or 5 parts of delayed expansion agent, 0.1 or 2 parts of viscosity reducer; wherein: The particle size of limestone is 0.045mm to 2.5mm, the particle size of mica is 1.4mm to 2.5mm, and the particle size of vermiculite is 0.3mm to 2.0mm.

Embodiment 3

[0031] Example 3, the acid-soluble mineral fiber fine bridge plugging agent is obtained according to the following preparation method: in the first step, the required amount of limestone, mica, asbestos, vermiculite, cotton wool, acidifiable fiber, unidirectional The pressure sealing agent, delayed expansion agent and viscosity reducer are added into the mixer for primary mixing, and after the primary mixing, a primary mixture with fibers floating on the surface is obtained; in the second step, the primary mixture is subjected to secondary mixing in the mixer. First-stage stirring, during the second-stage stirring, a fan is used to send a small wind into the mixer at the same time, after the second-stage stirring, the secondary mixture is obtained, and the third step is to carry out the third-stage stirring of the secondary mixture in the mixer. During the first-stage stirring, a fan is used to send strong wind into the mixer at the same time, and after the third-stage stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of auxiliaries for oil-gas exploration drilling in oil fields, in particular to an acid soluble mineral fiber fine bridging agent, a bridging fluid and a preparation method thereof.In raw materials of the acid soluble mineral fiber fine bridging agent, the particle size of limestone is 0.045mm-2.5mm, the particle size of mica is 1.4mm-2.5mm, and the particle size of vermiculite is 0.3mm-2.0mm. After the acid soluble mineral fiber fine bridging agent is added into plugging slurry under conditions of deep wells, ultradeep wells, high temperature, high density and high pressure, normal fluidity of drilling fluid can be kept; due to high acid solubility, when strong acid is injected for oil-gas exploitation after leakage stoppage, the acid soluble mineral fiber fine bridging agent is dissolved, so that pollution-free smooth oil-gas exploitation is guaranteed; the bridging fluid obtained by adoption of the acid soluble mineral fiber fine bridging agent is applicable to various leakage layers and excellent in leakage stopping effect.

Description

technical field [0001] The invention relates to the technical field of drilling aids for oil and gas exploration in oil fields, and relates to an acid-soluble mineral fiber fine bridge plug plugging agent and plugging fluid and a preparation method thereof. Background technique [0002] The occurrence of lost circulation brings great difficulties to the exploration and development of oil and gas resources. It will not only consume drilling time and lose mud, but also may cause a series of complicated situations such as pipe sticking, blowout, and well collapse. In severe cases, the wellbore will be scrapped , resulting in significant economic losses. The damage caused by lost circulation to oil and gas exploration, drilling and development operations can be summarized as follows: 1. Lost circulation delays drilling operation time and prolongs drilling cycle; 2. Lost circulation directly causes huge material and economic losses; 3. Reservoir Loss will damage the production l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/467
CPCC09K8/426C09K8/467C09K2208/04C09K2208/08
Inventor 张国发
Owner XINJIANG LUMING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap