A kind of preparation method of multilevel pore size distribution material
A pore size distribution and fiber technology, which is applied in the field of preparation of multi-level pore size distribution materials, can solve the problems of material limitation and complex synthesis steps of porous materials, and achieve the effects of simple preparation method, improved fluid passing performance, and avoiding brittleness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] A method for preparing a multi-level pore size distribution material, specifically:
[0029] (1) Preparation of coarse functionalized fibers and fine functionalized fibers:
[0030] 1) Preparation of fine functionalized fibers: the fine functionalized fibers in this example are chitosan nanofibers, and the preparation process is to dissolve chitosan in a mixed solvent of hexafluoroisopropanol and acetic acid to obtain a mass concentration of 7% spinning solution, the spinning solution is prepared by electrospinning to obtain chitosan nanofibers with a diameter of 300 nm; the mixed solvent of hexafluoroisopropanol and acetic acid is hexafluoroisopropanol It is prepared by mixing with acetic acid at a mass ratio of 3:2; the preparation conditions of the electrospinning method are: voltage 15 kV, control receiving distance 15 cm; fine functionalized fibers with a diameter between 150nm and 750nm, with polymer fiber toughness;
[0031] 2) Preparation of coarse functionali...
Embodiment 2
[0035] A method for preparing a multi-level pore size distribution material, specifically:
[0036] (1) Preparation of coarse functionalized fibers and fine functionalized fibers:
[0037] 1) Preparation of coarse functionalized fibers: the coarse functionalized fibers in this example are short glass fibers, and the preparation process is to prepare short glass fibers with a diameter distribution of 100um by pool kiln drawing; the short glass fibers are inorganic fibers The material has good rigidity;
[0038]2) Preparation of fine functionalized fibers: the fine functionalized fibers in this example are polyacrylic acid fibers, and the preparation process is to prepare polyacrylic acid fibers with a diameter of 400nm-550nm by dry spinning; the polyacrylic acid fibers are high Molecular materials, when the diameter is 400nm-550nm, it has good toughness; combined with the toughness of fine functional fibers and the rigidity of inorganic fiber materials (glass short fibers), th...
Embodiment 3
[0043] A method for preparing a multi-level pore size distribution material, specifically:
[0044] (1) Preparation of coarse functionalized fibers and fine functionalized fibers:
[0045] 1) Preparation of coarse functionalized fibers: the coarse functionalized fibers in this example are silver fibers, and the preparation process is to prepare silver fibers with a diameter distribution of 20um-40um by template method;
[0046] 2) Preparation of fine functionalized fibers: the fine functionalized fibers in this example are polylactic acid fibers, and the preparation process adopts electrospinning process to prepare polylactic acid nanofibers with a diameter of 300nm-350nm;
[0047] (2) Homogenization treatment: According to the mass ratio of the silver fiber and the polylactic acid fiber being 1:150, weigh the silver fiber and the polylactic acid fiber prepared in step (1), and put them into the opening Mixing and opening treatment is carried out in the machine to obtain homo...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com