Chicken manure moulded solid fuel

A solid fuel and chicken manure technology, which is applied in the field of solid waste recycling, can solve problems such as cracking, easy mildew, and secondary pollution, and achieve good economic benefits, wide application range, and clean protection

Inactive Publication Date: 2016-07-20
刘良贵
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most technologies adopt the method of pressing first and then drying to produce solid fuel, but it is easy to crack during the drying process, reducing its strength, and it is also easy to break during transportation
The fuel produced by most of the technologies has not undergone desulfurization, deodorization and anti-mildew process, so the fuel is prone to odor and mildew, and even causes serious secondary pollution when used, making it difficult to use and store
In addition, some researchers add binders in the raw material preparation process, which increases production costs and is not conducive to large-scale industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A chicken manure molded solid fuel, the composition of which includes in parts by weight: 55 parts of dried chicken manure, 7 parts of anthracite, 30 parts of coke, 3 parts of quicklime, 1.5 parts of sodium carbonate, 1 part of potassium chloride, and 3 parts of 35% alcohol part, 0.2 part of rosin.

Embodiment 2

[0021] A chicken manure molded solid fuel, the composition of which includes in parts by weight: 85 parts of dried chicken manure, 2 parts of anthracite, 10 parts of coke, 1 part of quicklime, 1 part of sodium carbonate, 0.5 parts of potassium chloride, 2 parts of 35% alcohol part, 0.5 part of rosin.

Embodiment 3

[0023] A chicken manure molded solid fuel, the composition of which includes in parts by weight: 75 parts of dried chicken manure, 5 parts of anthracite, 25 parts of coke, 2 parts of quicklime, 1.2 parts of sodium carbonate, 0.8 parts of potassium chloride, 2.5 parts of 35% alcohol part, 0.4 part of rosin.

[0024] The chicken manure molding solid fuel of embodiment 1-3 all adopts following preparation method to make, specifically comprises:

[0025] (1) Dry the chicken manure, control its water content to be no higher than 13%, then pulverize it, control the particle diameter of the dried chicken manure particles between 4-5mm, weigh and screen the qualified dry chicken manure particles according to the amount, that is Winner ingredient A;

[0026] (2) Pulverize anthracite, coke, and quicklime separately, and the particle size of the obtained particles is not greater than 3mm. Weigh and mix the three materials that pass the screening to obtain auxiliary material B;

[0027]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a chicken manure moulded solid fuel, which comprises the following components in parts by weight: 55 to 85 parts of dry chicken manure, 2 to 7 parts of anthracite, 10 to 30 parts of coke, 1 to 3 parts of quicklime, 1 to 1.5 parts of sodium carbonate, 0.5 to 1 part of potassium chloride, 2 to 3 parts of alcohol (35%), and 0.2 to 0.5 part of rosin. The agricultural waste (chicken manure) is converted into valuable resources. The provided solid fuel is clean and environment-friendly and is the best substitute of fossil energy.

Description

technical field [0001] The invention belongs to the field of solid waste recycling, in particular to a solid fuel formed from chicken manure. Background technique [0002] With the large-scale development of chicken breeding industry in my country, a large amount of chicken manure is produced. Traditional methods of treating chicken manure, such as composting and fermentation capacity, are difficult to realize the harmless treatment and resource utilization of chicken manure, and reduce the amount of chicken manure. Much more than a reasonable amount of usage and the processing power of the surrounding environment. [0003] In recent years, domestic and foreign literature and patents have reported the technology of preparing fuel from plant straw and animal dung. Most technologies adopt the method of first pressing and then drying to produce solid fuel, but it is easy to crack during the drying process, reducing its strength, and it is also easy to break during transportatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10L5/42
CPCY02E50/10Y02E50/30
Inventor 刘良贵
Owner 刘良贵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com