Method for reclaiming ferric oxide from coal ash and coal gangue

A technology of coal gangue and fly ash, which is applied in the field of solid waste recycling, can solve the problems of land occupation by residue stacking, low added value of residue utilization, and large amount of residue, so as to realize recycling and solve the problem of low added value of residue utilization , the effect of high purity

Active Publication Date: 2008-09-03
北京蔚然欣科技有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can solve the problem of land occupation and environmental pollution caused by the residual residue after alumina extraction, and can solve the problems of large amount of residue and low added value of residue utilization in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Grind the fly ash and make the particle diameter less than 200 mesh, preferably between 200-400 mesh. The ground fly ash was mixed with Na 2 CO 3 Mix and stir according to the ratio of fly ash: sodium carbonate=1:1;

[0035] 2. Calcining the mixture formed in the previous step at a temperature of 800° C. for 50 minutes.

[0036] 3. Add appropriate amount of water to the sintered product, sintered product: water = 1:50. After leaching at 60°C for 2 hours, it was filtered.

[0037] 4, feed CO into the concentrated filtrate gained in step 3 2 , filtered after carbon separation for 2 hours to obtain H 2 SiO 3 and Al(OH) 3 mixture.

[0038] 5. Add industrial hydrochloric acid to the filter residue obtained in steps 3 and 4, the solid-to-liquid ratio is 1:5, and react for 50 minutes at a temperature of 60°C. Filter after the reaction, the resulting filter residue is silica gel, and the filtrate is AlCl 3 with FeCl 3 mixture.

[0039] 6. AlCl obtained in step 5 ...

Embodiment 2

[0044] 1. Grind the gangue to make the particle diameter 240 mesh. The coal gangue after grinding is mixed with Na2CO3 by coal gangue: sodium carbonate=1: 3 ratio mixing, stirring;

[0045] 2. Calcining the mixture formed in the previous step at a temperature of 900° C. for 25 minutes.

[0046] 3. Add an appropriate amount of water to the sintered product, the Na in it 2 SiO 3 and NaAlO 2 is dissolved in water. Sintered product: water = 1:85. After leaching for 1 hour at a temperature of 80°C, filter.

[0047] 4, feed the CO obtained in step 2 into the concentrated filtrate gained in step 3 2 , filtered after carbon separation for 2 hours to obtain H 2 SiO 3 and Al(OH) 3 mixture.

[0048] 5. Add industrial hydrochloric acid to the filter residue obtained in steps 3 and 4, the solid-to-liquid ratio is 1:5, and react for 400 minutes at a temperature of 70°C. Filter after the reaction, the resulting filter residue is silica gel, and the filtrate is AlCl 3 with FeCl 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method of recovering an iron oxide from a fly ash and a gangue. The method adopts the process of grinding and roasting the fly ash and the gangue, the process of immersing and carbon dioxide decomposing the alumina, the process of acidizing and separating the silica and the process of obtaining iron oxide by the method of hydroxide precipitation. The purity of the iron oxide made by the method is high and the extraction rate of the iron oxide in the fly ash and the gangue can reach to 86 percent. The whole process is carried out under the pressure condition, so the method has low requirements to the equipment. The method solves the problems of land occupation and environment pollution caused by residue stacking after alumina extraction, also solves the problems of large amount of residue and low added value of the residue. The whole process realizes recycling of resources and can not cause new pollution to the surrounding environment.

Description

technical field [0001] The invention belongs to the technical field of solid waste recovery and utilization, and in particular relates to a method for recovering iron oxide from fly ash and coal gangue. Background technique [0002] Coal-based solid waste includes fly ash and coal gangue, which come from the mining, processing and utilization of coal. Coal gangue is a rock associated with coal, which is removed during coal mining and coal washing. Fly ash is coal combustion waste, which is the solid waste residue discharged from coal-fired power plants. At present, the total stockpile of coal-based solid waste in my country has exceeded 2 billion tons, and it is still increasing at a rate of about 100 million tons per year, which not only occupies a large amount of land resources, but also seriously pollutes the environment. [0003] In the near future, comprehensive utilization of fly ash and coal gangue must be implemented, and the goal of zero discharge of waste must be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G49/06
Inventor 潘爱芳杨胜科马润勇
Owner 北京蔚然欣科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com