Ultrathin water storage device

An ultra-thin, carbon black technology, applied in the field of water storage treasures, which can solve the problems of unable to fill the mold cavity normally, unevenness, and early vulcanization of the rubber compound.

Inactive Publication Date: 2016-07-27
浙江华和塑胶科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The average wall thickness of the traditional rubber liner is about 1.5mm, and the average thickness of the ultra-thin rubber is 1.25mm. Therefore, during injection production, the rubber material is more likely to vulcanize early in a short period of time, so that the entire mold cavity cannot be filled normally, and the ejection Uneven after molding, or directly useless products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An ultra-thin water storage treasure, which is characterized in that it includes the following components: 10-18% of ordinary butyl rubber, 30-50% of halogenated butyl rubber, 30-48% of carbon black, 2-3% of resin, and internal mold release Agent 0.1-1%, flow aid 1.5-3.5%. Wherein the carbon black is N774 carbon black, and the resin is 1055 resin, which is characterized in that the resin is 1055 resin, the flow aid is KL808, and the internal release agent is IF99.

[0015] The hardness of the above-mentioned ultra-thin water storage treasure is 55-72 Shore (A), 300% constant elongation strength ≥ 7.2MPa, tear strength ≥ 8.5MPa, elongation at break ≥ 320%, permanent deformation at break ≤ 10% , tear strength ≥ 37KN / M, specific gravity 31.11-1.13g / cm3, size ≤ 0.20mm, product weight 175-205. The fluidity of the product is improved, and the Mooney viscosity of the rubber material is 55-65.

Embodiment 2

[0017] An ultra-thin water storage treasure, which is characterized in that it includes the following components: 12-16% of ordinary butyl rubber, 35-45% of halogenated butyl rubber, 35-45% of carbon black, 2.2-2.8% of resin, and internal mold release Agent 0.3-0.8%, flow aid 2-3%. Wherein the carbon black is N774 carbon black, and the resin is 1055 resin, which is characterized in that the resin is 1055 resin, the flow aid is KL808, and the internal release agent is IF99.

[0018] The hardness of the above-mentioned ultra-thin water storage treasure is 58-68 Shore (A), 300% constant elongation strength ≥ 7.2MPa, tear strength ≥ 8.5MPa, elongation at break ≥ 320%, permanent deformation at break ≤ 10% , tear strength ≥ 37KN / M, specific gravity 31.11-1.13g / cm3, size ≤ 0.20mm, product weight 180-200. The fluidity of the product is improved, and the Mooney viscosity of the rubber material is 58-62.

Embodiment 3

[0020] An ultra-thin water storage treasure, which is characterized in that it includes the following components: 14% of ordinary butyl rubber, 40% of halogenated butyl rubber, 39% of carbon black, 2.5% of resin, 0.5% of internal mold release agent, and 2.5% of flow aid %. Wherein the carbon black is N774 carbon black, and the resin is 1055 resin, which is characterized in that the resin is 1055 resin, the flow aid is KL808, and the internal release agent is IF99.

[0021] The hardness of the above-mentioned ultra-thin water storage treasure is 62-65 Shore (A), 300% constant elongation strength ≥ 7.2MPa, tear strength ≥ 8.5MPa, elongation at break ≥ 320%, permanent deformation at break ≤ 10% , tear strength ≥ 37KN / M, specific gravity 31.11-1.13g / cm3, size ≤ 0.20mm, product weight 185-195. The fluidity of the product is improved (whether the flow performance can be expressed in numbers), and the Mooney viscosity of the rubber is 60.

[0022] The above-mentioned specific embod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ultrathin water storage device, which belongs to the technical field of water storage devices. The ultrathin water storage device is prepared from the following components by weight percent: 10 to 18 percent of ordinary butyl rubber, 30 to 50 percent of halogenated butyl rubber, 30 to 48 percent of carbon black, 2 to 3 percent of resin, 0.1 to 1 percent of internal releasing agent, and 1.5 to 3.5 percent of flow promoter. The ultrathin water storage device is high in scorching resistance and good in mobility; when in injection production, rubber materials are unlikely to vulcanize early in a short time, a whole mold cavity can be fully filled, and an inferior product is avoided.

Description

technical field [0001] The invention belongs to a water storage treasure, in particular to a household ultra-thin water storage treasure. Background technique [0002] The average wall thickness of the traditional rubber liner is about 1.5mm, and the average thickness of the ultra-thin rubber is 1.25mm. Therefore, during injection production, the rubber material is more likely to vulcanize early in a short period of time, so that the entire mold cavity cannot be filled normally, and the ejection After the mold is uneven, or it is a useless product directly. Contents of the invention [0003] Aiming at the above-mentioned problems in the prior art, the purpose of the present invention is to provide a technical solution for an ultra-thin water storage treasure. [0004] An ultra-thin water storage treasure, which is characterized in that it includes the following components: 10-18% of ordinary butyl rubber, 30-50% of halogenated butyl rubber, 30-48% of carbon black, 2-3% of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L23/22C08K3/04
CPCC08L23/283C08L2205/03C08L23/22C08K3/04
Inventor 谢东
Owner 浙江华和塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap