Manufacturing method of x80 pipeline steel spiral welded pipe

A technology for spiral welded pipes and manufacturing methods, which is applied in the manufacture of spiral submerged arc welded pipes and the manufacture of X80 pipeline steel spiral welded pipes. Effects of heat input, toughness improvement, and grain size reduction

Inactive Publication Date: 2017-08-29
CHINA UNIV OF PETROLEUM (EAST CHINA) +3
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The critical coarse-grained zone can lead to a significant decrease in the impact toughness of the welded heat-affected zone, making the overall performance of the welded joint lower than the requirements of the relevant standards. In actual production, most of the low values ​​in the Charpy impact test are below 50J

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of x80 pipeline steel spiral welded pipe
  • Manufacturing method of x80 pipeline steel spiral welded pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Such as figure 2 As shown, the manufacturing method of X80 pipeline steel spiral welded pipe adopts the X80 pipeline steel coil with a wall thickness of 21.4mm, and its chemical composition (weight percentage) is as follows: C 0.04~0.07, Si 0.15~0.25, Mn 1.68~1.78, Nb0. 04~0.05, Ti 0.01~0.02, Cu 0.12~0.22, Cr 0.20~0.28, Mo 0.10~0.20, Ni 0.10~0.20, P<0.015, S<0.005, N<0.006, Fe is the balance; made pipe diameter It is a Φ1422mm X80 pipeline steel spiral welded pipe, and the process steps are as follows:

[0022] 1. Uncoiling and leveling of X80 pipeline steel coils: Uncoil the X80 pipeline steel coils with an uncoiler and level them with a leveler;

[0023] 2. Edge milling: rough milling first, milling off the width of the plate edge by 5-10mm; then fine milling, as attached figure 2 As shown, the groove on the outer side of the pipe wall is the outer groove, the groove on the inner side is the inner groove 6, and the straight edge between the two grooves is the blun...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
depthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of mechanical equipment manufacturing and particularly relates to a manufacturing method for a spiral submerged arc welded pipe. A manufacturing method for an X80 pipeline steel spiral welded pipe includes the following technological steps that uncoiling and flattening of an X80 pipeline steel plate coil are conducted; edge milling is conducted; pre-bending is conducted; forming is conducted; pre-welding is conducted; internal welding is conducted; external welding is conducted; pipe end expanding is conducted; and product inspection is conducted. Brand new design is conducted on a welding groove type, and therefore energy of a welding line of an inner weld bead and energy of a welding line of an outer weld bead are distributed again, the energy of the welding line of the outer weld bead is improved, and the energy of the welding line of the inner weld bead is reduced. The grain size in a critical coarse-grain area in a heat-affected area can be obviously reduced due to the reduction of the energy of the welding line of the inner weld bead, scattering of distribution of chain-shaped M-A components is facilitated, meanwhile, the size of the M-A components can be reduced, and therefore the toughness of the welding heat-affected area is obviously improved. In addition, although the filling amount of the outer weld bead is increased to some extent, a double-wire tandem sequence is changed into a three-wire tandem sequence for welding, the welding speed can be ensured, and the production efficiency cannot be reduced.

Description

technical field [0001] The invention belongs to the field of mechanical equipment manufacturing, and in particular relates to a method for manufacturing a spiral submerged arc welded pipe, which is used for oil and gas transportation and is suitable for the manufacture of X80 pipeline steel spiral welded pipes of Φ1422mm×21.4mm. Background technique [0002] With the implementation of pipeline projects such as the West-to-East Gas Pipeline Project, pipeline steel has developed rapidly in China since 2000. At present, the manufacturing level of domestic pipeline steel has been at the forefront of the world. At this stage, the gas pipelines being laid are mainly made of X80 pipeline steel. The performance indicators of the X80 pipeline steel parent material currently produced can meet the standard requirements, but there are still many problems in the welding process; moreover, in oil and gas pipelines, the weld length accounts for a large proportion, so welding The performan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00B21C37/08
CPCB21C37/08B23P15/00
Inventor 李学达刘振伟林学强付超范玉然孙建波
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com