Substrateless magnetic glittering pigment and preparation method and application thereof

A flashing pigment, no substrate technology, applied in the direction of inorganic material magnetism, magnetic materials, inorganic pigment treatment, etc., can solve the problems that cannot meet the requirements of decorative applications, achieve a significant color-dependent effect, economical and reliable, and a wide range of applications wide effect

Active Publication Date: 2018-03-16
HUNAN NELKIN MATERIAL TECH CO LTD
View PDF31 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the magnetic pearlescent pigment is black and cannot meet the requirements of most decorative applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Substrateless magnetic glittering pigment and preparation method and application thereof
  • Substrateless magnetic glittering pigment and preparation method and application thereof
  • Substrateless magnetic glittering pigment and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Prepare the following materials in parts by weight: 100 parts of sendust powder with an average particle size of 60 μm obtained by mechanical crushing (in this sendust powder, the mass fraction of silicon is 9.7%, and the mass fraction of aluminum is 5.8%, the mass fraction of iron is 84.5%), 120 parts of solvent ethanol, 0.2 part of ball milling aid stearic acid, 1500 parts of diameters are 5mm stainless steel balls. Put the prepared material into a sand mill and grind for 10 hours to obtain the primary powder; then dry the primary powder in a vacuum oven and heat-treat it at 750°C for 2 hours under an argon atmosphere to obtain the secondary powder; then the secondary powder Through a 100-mesh sieve, the average particle size is 51um, and the bulk density is 0.51g / cm 3 , a finished baseless magnetic glitter pigment with an aspect ratio of 32. Mix 10g of the above-mentioned substrateless magnetic glitter pigment with 90g of standard NC-acrylate paint, apply the result...

Embodiment 2

[0066] Prepare the following materials in parts by weight: 100 parts of sendust powder with an average particle size of 60 μm obtained by mechanical crushing (in this sendust powder, the mass fraction of silicon is 9.7%, and the mass fraction of aluminum is 5.8%, the mass fraction of iron is 84.5%), 250 parts of solvent ethanol, 0.3 part of ball milling aid stearic acid, 2500 parts of diameters are 5mm hard chrome balls. Put the prepared material into a sand mill and grind for 10 hours to obtain the primary powder; then dry the primary powder in a vacuum oven and heat-treat it at 780°C for 2 hours under an argon atmosphere to obtain the secondary powder; then the secondary powder Through a 100-mesh sieve, the average particle size is 68um, and the bulk density is 0.38g / cm 3 , The finished baseless magnetic glitter pigment with an aspect ratio of 42.

Embodiment 3

[0068] Prepare the following materials in parts by weight: 100 parts of FeSiCr alloy powders with an average particle size of 12um (in this FeSiCr alloy powders, the massfraction of silicon is 12%, and the massfraction of chromium is 1.8%, the mass fraction of iron is 86.2%), 120 parts of solvent D-80 mineral spirits, 0.2 part of ball milling aid stearic acid, 1500 parts of diameters are 3mm stainless steel balls. Put the prepared material into a planetary ball mill and grind for 5 hours to obtain the primary powder; then dry the primary powder in a vacuum oven and heat-treat it at 450°C for 2 hours under an argon atmosphere to obtain the secondary powder; then pass the secondary powder through The 100 mesh sieve obtained an average particle size of 35um and a bulk density of 0.46g / cm 3 , The finished baseless magnetic glitter pigment with an aspect ratio of 22.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
bulk densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides base-material-free magnetic flash pigment .The base-material-free magnetic flash pigment is flaky powder made of a metal soft magnetic material, the average particle size of the base-material-free magnetic flash pigment is 5-200 micrometers, the apparent density is 0.2-1.0 g / cm<3>, and the diameter-thickness ratio is 10-100 .The base-material-free magnetic flash pigment has high permeability and a remarkable angle-dependent optical effect and can be used for decoration and resisting electromagnetic interference .The invention further provides a preparing method and application of the base-material-free magnetic flash pigment.

Description

technical field [0001] The invention relates to the technical field of pigments, in particular to a substrate-less magnetic flash pigment and its preparation and application. Background technique [0002] Glitter pigments are angle-dependent effect pigments, which can appear in different lightness, chroma, and hue colors with different viewing angles, and have a three-dimensional texture. [0003] Angle-following effect refers to metallic flake pigments (especially aluminum powder) and / or metal-like flake pigments (especially mica-based pearlescent pigments) due to their metallic luster and characteristics parallel to the coated object, when containing transparent pigments In the carrier, the gloss and color depth of the glitter pigment will change with the incident angle and viewing angle of the incident light. The glitter pigments are arranged in different layers in the coating film. When the incident light hits each layer of flaky powder, it will be weakened differently ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09C3/04C09C1/62H01F1/147H01F1/20
CPCC09C1/62C09C1/622C09C3/041C09C3/043H01F1/14766H01F1/20
Inventor 戴雨兰
Owner HUNAN NELKIN MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap