A graphene-based water-based electrothermal coating and preparation method thereof
An electrothermal coating and graphene technology, applied in the coating field, can solve the problems of rare patents and few reports, and achieve long-term effective electrothermal heating effect, good adhesion, and good resistance to cold and heat cycles.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] A water-based electrothermal coating based on graphene, consisting of the following raw materials in parts by weight: 1 part of propylene glycol freeze-thaw stabilizer, 0.1 part of 2-amino-2-methyl-1-propanol, 0.1 part of polyoxyethylene alkyl ether 0.1 part of polymer copolymer alkylamine salt, 0.1 part of silicone defoamer, 1 part of graphene, 35 parts of calcium carbonate, 0.03 part of 1,2-benzisothiazolin-3-one (BIT), 0.04 part of 2-methyl-5-chloro-4-isothiamidazol-3-one, 0.03 part of 2-methyl-4-isothiamidazol-3-one (CMIT / MIT), 1 part of lauryl alcohol ester, 1 part of hydroxyethyl cellulose, 15 parts of polyacrylate emulsion, 45.5 parts of deionized water. The polyacrylate emulsion has a solid content of 40%, a pH of 8.0, a particle size of 0.15 microns, a viscosity of about 500 mPa.s, a minimum film-forming temperature of 18°C, and a glass transition temperature of 42°C. The graphene is produced by the mechanical exfoliation graphite method, and is a powder forme...
Embodiment 2
[0035]A water-based electrothermal paint based on graphene, which is composed of the following raw materials in parts by weight: 3 parts of propylene glycol ether, 0.2 part of dimethylethanolamine, 0.3 part of polyoxyethylene polyol ether, polymer embedded with pigment affinity group 1 part of segment copolymer solution, 0.5 part of aliphatic hydrocarbon emulsion, 5 parts of graphene, 50 parts of calcium carbonate, 0.1 part of 1,2-benzisothiazolin-3-one (BIT), 0.1 part of 2-methyl-5 - 0.1 part of chloro-4-isothiamidazol-3-one, 0.1 part of 2-methyl-4-isothiamidazol-3-one (CMIT / MIT), 3 parts of lauryl alcohol ester, 2 parts of polyurethane thickener , 25 parts of polyacrylate emulsion, 9.7 parts of deionized water.
[0036] The polyacrylate emulsion has a solid content of 45%, a pH of 8.5, a particle size of 0.20 microns, a viscosity of about 550 mPa.s, a minimum film-forming temperature of 18°C, and a glass transition temperature of 42°C.
[0037] The graphene is produced by t...
Embodiment 3
[0046] A water-based electrothermal coating based on graphene, which is composed of the following raw materials in parts by weight: 2 parts of propylene glycol, 0.15 parts of ethanolamine, 0.2 parts of polyoxyethylene polyoxyacrylic acid block copolymer, and 0.6 part of polymer copolymer alkylamine salt , 0.3 parts of non-silicone organic ester hydrocarbon, 3 parts of graphene, 42 parts of calcium carbonate, 0.1 part of 1,2-benzisothiazolin-3-one (BIT), 2-methyl-5-chloro- 0.05 parts of 4-isothiamidazol-3-one, 0.05 parts of 2-methyl-4-isothiamidazol-3-one (CMIT / MIT) tank preservative, 2 parts of lauryl alcohol ester, modified polyurea Thickener 1.5 parts, polyacrylate emulsion 20 parts, deionized water 28.05 parts.
[0047] The emulsion is a polyacrylate emulsion with a solid content of 42%, a pH of 8.3, a particle size of 0.18 microns, a viscosity of about 520mPa.s, a minimum film-forming temperature of 18°C, and a glass transition temperature of 42°C.
[0048] The graphene i...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap