Flanging method and device for tapered hole in titanium alloy plate

A technology of titanium alloy and tapered hole, which is applied in the field of flanging method and device for the tapered hole of titanium alloy plate, which can solve the problems of easy cracking of materials and lack of back pressure stress of metal, so as to ensure the quality of weld seam and improve the stress of metal State, the effect of improving the accuracy of weldments

Active Publication Date: 2017-10-20
ZHEJIANG SHENJI TITANIUM IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the lack of back pressure stress of the metal in the flanging area in the prior art, which cannot solve the problem that the material is easy to crack during flanging, the present invention proposes a flanging method and device for a tapered hole in a titanium alloy plate, which can increase the amount of conical flanging The back pressure stress of the regional plate solves the problem that the material is easy to crack when flanging, and at the same time makes the welding of the two parts precise butt joint, ensuring the quality of the weld seam

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flanging method and device for tapered hole in titanium alloy plate
  • Flanging method and device for tapered hole in titanium alloy plate
  • Flanging method and device for tapered hole in titanium alloy plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment relates to a method for flanging a tapered hole in a titanium alloy plate, comprising the following steps:

[0026] S 1 , processing of prefabricated holes 12: the plate 1 is annealed and then cleaned with acid and alkali, then dried, cut, and prepunched to obtain prefabricated holes 12;

[0027] S 2 , pre-bending processing: After obtaining the prefabricated hole 12, the plate 1 is installed on the first station of the general hydraulic press, the jacking pipe 4 is installed on the upper mold of the first station, and the first conical punch 3 is installed on the first station Lower mold, such as figure 2 As shown, the prefabricated hole 12 is set corresponding to the jacking pipe 4 and the first tapered punch 3; the universal hydraulic press is started, and the slider is lowered to drive the jacking pipe 4 to press down to pre-turn the edge of the prefabricated hole 12 to form the pre-turning hole 2. During the pre-turning process, the first conica...

Embodiment 2

[0042] The difference from Example 1 is that in this example:

[0043] The grade of the plate 1 is titanium alloy TC4, with a thickness of 1 mm and a diameter of Hot flanging after pre-flanging to form a tapered boss 5;

[0044] The material of the first tapered punch is cold mold steel Cr12MoV with a heat treatment hardness of 58-62HRC, and the material of the second tapered punch is hot mold steel H13 with a heat treatment hardness of 48-52HRC.

[0045] The hot-state flanging processing refers to that the pre-turned plate 1 is sprayed with FR-6 glass lubricant, which has protective and lubricating properties in the range of 400-1800°C. After drying, put it into an electric roller furnace and heat it to 700°C and keep it warm for 16 minutes, then immediately move to the second station, and process the tapered hole boss 5 on the plate 1 at high temperature; The pressure applied by the copper conduit not only exerts a back pressure in the deformed area of ​​the two, but also...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a flanging method and a flanging device for conical holes of titanium and titanium alloy plates in the technical field of metal forming. The flanging method comprises the following steps: pre-treating the titanium and titanium alloy plates to facilitate machining for prefabricated holes; after the prefabricated holes are machined, pre-bending the edges of the prefabricated holes through the interaction of a first conical convex die and jacking tubes; and then producing the conical holes through the interaction of a second conical convex die and guide tube parts. According to the flanging method and the flanging device, which are disclosed by the invention, the flanging quality is improved, the material loss is reduced, and the feasibility of flanging is increased to 1.5-2 times in a cold state and is higher in a heat state; and the wall thickness of the conical holes of the parts after flanging is uniform, diameters at welds are expanded, the conical holes of the guide tube parts and the conical holes of the plates are synchronously formed, and welding seams are bonded better, thus the quality of the welding seams is ensured.

Description

technical field [0001] The invention relates to a technology in the field of metal forming, in particular to a method and device for flanging a tapered hole in a titanium alloy plate. Background technique [0002] Flanging forming is a forming process in which convex and concave dies use tensile and compressive forces to form bosses or to form vertical bosses around prefabricated holes. The round hole flanging process is widely used in sheet metal forming in the automotive, aerospace and aviation industries. In recent years, in the aircraft manufacturing industry, whether it is a civil aircraft or a military aircraft, the use of titanium has doubled due to its outstanding advantages. For example, in the field of civil aviation, the United States has increased its titanium alloy consumption from 3% of Boeing 707 in the 1950s to 15% of Boeing 787 in 2010. The consumption of titanium alloy in the airliner MS-21 under development in Russia is as high as 25%. The amount of titan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21D19/00
CPCB21D19/00
Inventor 陈修琳袁秦峰陈岩
Owner ZHEJIANG SHENJI TITANIUM IND