Sports venue track material

A technology for sports and venues, applied in the field of track materials for sports venues, can solve the problems of incomplete improvement of the rebound rate, tensile strength and elongation at break of the plastic track, and restrict the performance of the plastic track, and achieve superior flame retardancy , high rebound rate, and the effect of improving product performance

Inactive Publication Date: 2016-09-21
梁方英
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the manufacture of plastic track, the use of polypropylene has many advantages, but only polypropylene can not completely improve the rebound rate, te

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sports venue track material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The sports track material in this embodiment consists of the following components in parts by mass: 18 parts of phenol resin, 20 parts of ammonium polyphosphate, 16 parts of hexabromobenzene, 14 parts of triethylene glycol diisocaprylate, 20 parts of carbolic acid, 16 parts of talcum powder, 14 parts of octamethyl silicone oil, 20 parts of sweet potato starch, 16 parts of calcium formate, 14 parts of chromium chloride, 20 parts of metallocene, 16 parts of zirconium boride powder, 16 parts of ferric chloride Parts, 14 parts of methyl acetate, 20 parts of citronellyl formate, 16 parts of dimethylaminoethyl acrylate, 14 parts of aziridine crosslinking agent, 20 parts of p-benzoquinone dioxime, 16 parts of diaminodiphenylmethane, 14 parts of dibasic lead phthalate, 20 parts of fluoroboric acid, 16 parts of dextrin, 14 parts of sodium methacrylate, 20 parts of methanesulfonic acid, 16 parts of sodium metabisulfite, 16 parts of polymeric alcohol amine, twelve parts 16 parts o...

Embodiment 2

[0022] The sports track material in this embodiment consists of the following components in parts by mass: 20 parts of phenol resin, 22 parts of ammonium polyphosphate, 18 parts of hexabromobenzene, 16 parts of triethylene glycol diisocaprylate, 22 parts of carbolic acid, 18 parts of talcum powder, 16 parts of octamethyl silicone oil, 22 parts of sweet potato starch, 18 parts of calcium formate, 16 parts of chromium chloride, 22 parts of metallocene, 18 parts of zirconium boride powder, 18 parts of ferric chloride 16 parts of methyl acetate, 22 parts of citronellyl formate, 18 parts of dimethylaminoethyl acrylate, 16 parts of aziridine crosslinking agent, 22 parts of p-benzoquinone dioxime, 18 parts of diaminodiphenylmethane, 16 parts of dibasic lead phthalate, 22 parts of fluoroboric acid, 18 parts of dextrin, 16 parts of sodium methacrylate, 22 parts of methanesulfonic acid, 18 parts of sodium metabisulfite, 18 parts of polymeric alcohol amine, twelve parts 18 parts of calci...

Embodiment 3

[0028]The sports track material in the present embodiment is composed of the following components in parts by mass: 22 parts of phenol resin, 24 parts of ammonium polyphosphate, 20 parts of hexabromobenzene, 18 parts of triethylene glycol diisocaprylate, 24 parts of carbolic acid, 20 parts of talcum powder, 18 parts of octamethyl silicone oil, 24 parts of sweet potato starch, 20 parts of calcium formate, 18 parts of chromium chloride, 24 parts of metallocene, 20 parts of zirconium boride powder, 20 parts of ferric chloride Parts, 18 parts of methyl acetate, 24 parts of citronellyl formate, 20 parts of dimethylaminoethyl acrylate, 18 parts of aziridine crosslinking agent, 24 parts of p-benzoquinone dioxime, 20 parts of diaminodiphenylmethane, 18 parts of dibasic lead phthalate, 24 parts of fluoroboric acid, 20 parts of dextrin, 18 parts of sodium methacrylate, 24 parts of methanesulfonic acid, 20 parts of sodium metabisulfite, 20 parts of polymeric alcohol amine, twelve parts 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a sports venue track material. The material is prepared from phenolic resin, ammonium polyphosphate, hexabromo-benzene, 2,2'-ethylenedioxydiethyl bis(2-ethylhexanoate), phenol, talcum powder, octamethyl silicone oil, sweet potato starch, calcium formate, chromic chloride, metallocene, zirconium boride powder, ferric trichloride, methyl acetate, citronellyl formate, N,N-dimethylaminoethyl acrylate, aziridine crosslinking agent, p-Benzoquinone dioxime, diaminodiphenyl-methane, dibasic lead phthalate, fluoboric acid, dextrin, sodium methallyl sulfonate, methanesulfonic acid, sodium pyrosulfite, polymeric alkylol amine, calcium dodecyl benzene sulfonate, titanium tetraisopropanolate, vinyl pyrrolidone and lauryl diethanolamine. The product has excellent flame retardance, acid and alkali resistance, mildew resistance and mold resistance and is high in rebound rate, and the product performance is improved.

Description

technical field [0001] The invention relates to a track material for sports venues, belonging to the technical field of sports. Background technique [0002] The most prominent property of polypropylene is its versatility, which is suitable for many processing methods and uses. Its value and versatility come primarily from its excellent chemical resistance, lowest density and highest melting point among bulk thermoplastics, and moderate cost. In the manufacture of plastic track, the use of polypropylene has many advantages, but only polypropylene can not completely improve the rebound rate, tensile strength and elongation at break of the plastic track. The existence of the above problems restricts the plastic track. Improved runway performance. Contents of the invention [0003] The object of the present invention is to provide a kind of track material for sports venues, in order to better realize the use function of the track materials for sports venues, so that the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L3/02C08L61/06C08L83/04C08K13/02C08K3/32C08K5/03C08K5/103C08K3/34
CPCC08L3/02C08L2201/02C08L2205/025C08L2205/035
Inventor 梁方英
Owner 梁方英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap