Stable modified asphalt

A modified asphalt and stability technology, applied in building components, building insulation materials, buildings, etc., can solve the problems of poor rutting resistance, prone to cracking, insufficient demand, etc., to improve flexibility and elasticity, good rutting resistance ability, excellent road performance

Inactive Publication Date: 2016-09-28
青岛千帆高新技术有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The purpose of modification is to improve the road properties of asphalt: high temperature stability, low temperature crack resistance, fatigue resistance, improve the adhesion of asphalt, improve the aging resistance of asphalt, but there is still demand for modified asphalt on the market Insufficient, poor rutting resistance, prone to cracking, so further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A kind of stability modified bitumen, it is made from the raw material of following parts by weight:

[0009] 4 parts of stearic acid, 3 parts of castor oil, 6 parts of oleic acid, 3 parts of palmitic acid, 0.8 parts of sodium lactate, 0.6 parts of phenylethylphenol polyoxypropylene polyoxyethylene ether, 2 parts of nano-silica, SBS block copolymerization 3 parts of rubber powder, 8 parts of epoxy soybean oil, 0.7 parts of graphite powder, 0.1 part of chlorinated polyethylene, 0.2 parts of coupling agent, 25 parts of asphalt, 1 part of surfactant, 1 part of antioxidant, two 4 parts of toluene.

Embodiment 2

[0011] A kind of stability modified bitumen, it is made from the raw material of following parts by weight:

[0012] 8 parts of stearic acid, 4 parts of castor oil, 9 parts of oleic acid, 5 parts of palmitic acid, 2.4 parts of sodium lactate, 1.2 parts of phenylethylphenol polyoxypropylene polyoxyethylene ether, 4 parts of nano-silica, SBS block copolymerization 6 parts of compound, 15 parts of rubber powder, 13 parts of epoxy soybean oil, 1.8 parts of graphite powder, 0.2 parts of chlorinated polyethylene, 0.5 parts of coupling agent, 35 parts of asphalt, 4 parts of surfactant, 2 parts of antioxidant, two 6 parts of toluene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to stable modified asphalt. The stable modified asphalt is prepared by, by weight, 4-8 parts of stearic acid, 3-4 parts of castor oil, 6-9 parts of oleic acid, 3-5 parts of hexadecanoic acid, 0.8-2.4 parts of sodium lactate, 0.6-1.2 parts of phenethyl phenol polypropylene oxide polyoxyethylene ether, 2-4 parts of nano silicon oxide, 3-6 parts of SBS segmented copolymer, 10-15 parts of rubber powder, 8-13 parts of epoxidized soybean oil, 0.7-1.8 parts of graphite powder, 0.1-0.2 part of chlorinated polyethylene, 0.2-0.5 part of coupling agent, 25-35 parts of asphalt, 1-4 parts of surfactant, 1-2 parts of antioxidant and 4-6 parts of dimethylbenzene. The stable modified asphalt is good in anti-rut capacity under high temperature, high in flexibility and elasticity, stable in performance, excellent in pavement performance and convenient to use.

Description

technical field [0001] The invention relates to a stability modified asphalt. Background technique [0002] Many changes have taken place in modern highways and roads. The traffic volume and driving frequency have increased sharply. The axle load of freight vehicles has continued to increase. Lanes and one-way driving are generally practiced. Coupled with the severe challenges of the climate, it is required to further improve the performance of the road surface to meet current usage requirements. Modified asphalt refers to the addition of rubber, resin and other high molecular polymers, finely ground rubber powder or other fillers and other external admixtures (external admixtures), and evenly mixed with asphalt, so that the properties of asphalt can be improved. asphalt mixture. The purpose of modification is to improve the road properties of asphalt: high temperature stability, low temperature crack resistance, fatigue resistance, improve the adhesion of asphalt, improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L91/00C08L71/02C08L53/02C08L21/00C08L23/28C08K13/02C08K5/09C08K5/098C08K3/36C08K3/04
CPCC08L95/00C08K2201/011C08K2201/014C08L2205/025C08L2205/035
Inventor 徐茂航
Owner 青岛千帆高新技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products