Chinese prickly ash viscose fiber and preparation method thereof

A viscose fiber, viscose staple fiber technology, applied in fiber treatment, short fiber formation, textile and papermaking, etc., to achieve the effect of treating eczema, excellent dyeing performance, and good dispersibility

Pending Publication Date: 2016-11-02
重庆市涪陵区宝竹寺花椒种植场
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although viscose fiber and peppercorns have their own characteristics, so far, no one has combined viscose fiber and peppercorns to make one product have the advantages of both substances.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0018] To prepare one ton of 4% Zanthoxylum viscose filaments, first prepare the mother liquor of Zanthoxylum bungeanum extract.

[0019] The preparation formula of pepper mother liquor:

[0020] Zanthoxylum bungeanum extract: 5wt%-20wt%, solubilizer (ethanol: polyethylene glycol: 1:1): 30wt%-40wt%, water: 40wt%-65wt%.

[0021] The preparation method of the mother liquor containing 10wt% Zanthoxylum bungeanum extract: in a stainless steel kettle, add 40Kg of Zanthoxylum bungeanum extract, add 120Kg of solubilizer, add 240Kg of water, stir, mix well, and set aside.

[0022] The above mother liquor is continuously blended with the spinning viscose in the pre-spinning syringe, and the blending ratio is 1 by the weight of a-Cell (a cellulose) in the total fiber weight and the mother liquor containing the Zanthoxylum bungeanum extract: 0.04, enter the R535A spinning machine (or R535, R535A semi-continuous spinning machine and continuous spinning machine) at the same time for spinn...

specific Embodiment 2

[0023] To prepare one ton of prickly ash viscose staple fiber with a content of 4%, the mother liquor of prickly ash extract is prepared first.

[0024] The preparation formula of pepper mother liquor:

[0025] Zanthoxylum bungeanum extract: 5wt%-20wt%, solubilizer (ethanol: polyethylene glycol: 1:1): 30wt%-40wt%, water: 40wt%-65wt%.

[0026] The preparation method of the mother liquor containing 10wt% Zanthoxylum bungeanum extract: in a stainless steel kettle, add 40Kg of Zanthoxylum bungeanum extract, add 120Kg of solubilizer, add 240Kg of water, stir, mix well, and set aside.

[0027] The above mother liquor is blended with the dissolved viscose in a dissolving machine. The blending ratio is 1:0.04 according to the weight of a-Cell (a cellulose) in the total weight of the fiber and the weight ratio of the Chinese prickly ash extract in the mother liquor. After being stirred, filtered, vacuum defoamed, matured, it enters the viscose staple fiber spinning machine for spinnin...

specific Embodiment 3

[0028] To prepare one ton of viscose filaments with 1% Zanthoxylum bungeanum, first prepare the mother liquor of Zanthoxylum bungeanum extract.

[0029] The preparation formula of pepper mother liquor:

[0030] Zanthoxylum bungeanum extract: 5wt%-20wt%, solubilizer (ethanol: polyethylene glycol: 1:1): 30wt%-40wt%, water: 40wt%-65wt%.

[0031] The preparation method of the mother liquor containing 10wt% Zanthoxylum bungeanum extract: In a stainless steel kettle, add 10Kg of Zanthoxylum bungeanum extract, add 30Kg of solubilizer, add 60Kg of water, stir, mix well, and set aside.

[0032] The above mother liquor is continuously blended with the spinning viscose in the pre-spinning syringe, and the blending ratio is 1 by the weight of a-Cell (a cellulose) in the total fiber weight and the mother liquor containing the Zanthoxylum bungeanum extract: 0.01, enter the R535A spinning machine (or R535, R535A semi-continuous spinning machine and continuous spinning machine) at the same t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Zanthoxylum bungeanum viscose fiber and a preparation method thereof. The fiber contains 1% to 8% of Zanthoxylum bungeanum extract based on the total dry basis weight of the fiber, and the Zanthoxylum bungeanum extract is uniformly dispersed in the inner and surface layers of the fiber. In addition to the advantages of pure natural, degradable, soft, and excellent dyeing performance of viscose fiber, the pepper viscose fiber of the present invention also has the functions of medicine and health care, and has significant effects in inhibiting bacteria, repelling mites, microorganisms, etc. At the same time, it can play an auxiliary role in preventing and treating eczema, itching, and delaying aging. In addition, it also has the effect of repelling mosquitoes.

Description

technical field [0001] The invention belongs to the field of textile industry, relates to a pepper viscose fiber, and also relates to a preparation method of the pepper viscose fiber. Background technique [0002] Viscose fiber is a regenerated cellulose fiber with the general molecular formula (C 6 h 10 o 5 )n, n is the degree of polymerization. It is made of natural cellulose such as wood, reed, and cotton linters in nature, and is made into soluble cellulose xanthate through alkalization, aging, and yellowing processes, and then dissolved in dilute lye to make viscose. Made by wet spinning. It is one of the first chemical fibers put into industrial production in the world. Viscose fiber is divided into two types: filament and staple fiber. Viscose filament is also called rayon or viscose; and viscose staple fiber has cotton type (also known as artificial cotton), wool type (called artificial wool) and medium and long fibers. Because the properties of viscose fiber ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/10D02G3/04D01D5/00D01D5/26
Inventor 常国华张正
Owner 重庆市涪陵区宝竹寺花椒种植场
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka