Seawater-corrosion-resistant bituminous pavement material and preparation method thereof

An asphalt pavement and seawater-resistant technology, which is applied in the field of pavement materials, can solve the problems such as the decrease in the strength of asphalt pavement materials, and achieve the effect of good seawater corrosion resistance and high strength

Active Publication Date: 2016-11-16
河北北方公路工程建设集团有限公司
View PDF16 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the invention is to solve the problem that the strength of conventional asphalt pavement materials decreases after being soaked in salt water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seawater-corrosion-resistant bituminous pavement material and preparation method thereof
  • Seawater-corrosion-resistant bituminous pavement material and preparation method thereof
  • Seawater-corrosion-resistant bituminous pavement material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Asphalt pavement materials, including the following components by weight: 10 parts of asphalt, 5 parts of hemihydrate gypsum, 15 parts of Portland cement, 5 parts of silicon dioxide, 3 parts of silicon carbide ceramic powder, 400-800 mesh glass hollow 1 part of microbeads, 3 parts of paraffin, 6 parts of 200-400 mesh diatomite, 20 parts of fly ash, 0.5 parts of antifungal agent, 0.5 parts of surfactant, and 50 parts of water.

[0022] The preparation method of asphalt pavement material, comprises the steps:

[0023] Step 1, weigh hemihydrate gypsum, Portland cement, silicon dioxide, and carry out pre-dispersion;

[0024] In the second step, mix the above-mentioned hemihydrate gypsum, portland cement and silicon dioxide evenly;

[0025] The 3rd step, weigh silicon carbide ceramic powder, glass hollow microspheres, paraffin, diatomaceous earth, fly ash, mix evenly;

[0026] In step 4, the mixture obtained in steps 2 and 3 is uniformly mixed with antifungal agent, surfac...

Embodiment 2

[0028] Asphalt pavement materials, including the following components by weight: 15 parts of asphalt, 20 parts of hemihydrate gypsum, 20 parts of Portland cement, 10 parts of silicon dioxide, 5 parts of silicon carbide ceramic powder, 400-800 mesh glass hollow 3 parts of microbeads, 6 parts of paraffin, 12 parts of 200-400 mesh diatomite, 40 parts of fly ash, 2 parts of antifungal agent, 2 parts of surfactant, and 100 parts of water.

[0029] The preparation method of asphalt pavement material, comprises the steps:

[0030] Step 1, weigh hemihydrate gypsum, Portland cement, silicon dioxide, and carry out pre-dispersion;

[0031] In the second step, mix the above-mentioned hemihydrate gypsum, portland cement and silicon dioxide evenly;

[0032] The 3rd step, weigh silicon carbide ceramic powder, glass hollow microspheres, paraffin, diatomaceous earth, fly ash, mix evenly;

[0033] In step 4, the mixture obtained in steps 2 and 3 is uniformly mixed with antifungal agent, surfa...

Embodiment 3

[0035] Asphalt pavement materials, including the following components by weight: 12 parts of asphalt, 8 parts of hemihydrate gypsum, 18 parts of Portland cement, 8 parts of silicon dioxide, 4 parts of silicon carbide ceramic powder, 400-800 mesh glass hollow 2 parts of microbeads, 5 parts of paraffin, 8 parts of 200-400 mesh diatomite, 30 parts of fly ash, 1 part of antifungal agent, 1 part of surfactant, and 80 parts of water.

[0036] The preparation method of asphalt pavement material, comprises the steps:

[0037] Step 1, weigh hemihydrate gypsum, Portland cement, silicon dioxide, and carry out pre-dispersion;

[0038] In the second step, mix the above-mentioned hemihydrate gypsum, portland cement and silicon dioxide evenly;

[0039] The 3rd step, weigh silicon carbide ceramic powder, glass hollow microspheres, paraffin, diatomaceous earth, fly ash, mix evenly;

[0040] In step 4, the mixture obtained in steps 2 and 3 is uniformly mixed with antifungal agent, surfactant,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to a seawater-corrosion-resistant bituminous pavement material and a preparation method thereof, and belongs to the technical field of pavement materials. The seawater-corrosion-resistant bituminous pavement material is prepared from, by weight, 10-15 parts of bitumen, 5-20 parts of hemihydrate gypsum, 15-20 parts of Portland cement, 5-10 parts of silicon dioxide, 3-5 parts of silicon carbide ceramic powder, 1-3 parts of glass hollow microspheres, 3-6 parts of paraffin, 6-12 parts of kieselguhr, 20-40 parts of coal ash, 0.5-2 parts of antimold, 0.5-2 parts of a surface active agent and 50-200 parts of water. By means of reasonable combination of the components, the bituminous pavement material has the advantages of being good in seawater corrosion resistance and high in strength.

Description

technical field [0001] The invention relates to a seawater corrosion-resistant asphalt pavement material and a preparation method thereof, belonging to the technical field of pavement materials. Background technique [0002] Asphalt concrete is a mixture formed by fully mixing asphalt materials with a certain viscosity and appropriate dosage and mineral aggregates of a certain grade. Asphalt concrete, as an asphalt pavement material, has to bear the repeated action of running vehicle loads and the long-term impact of environmental factors during its use. Therefore, while asphalt concrete has a certain bearing capacity, it must also have good durability against natural factors. That is to say, it should be able to show sufficient stability in high temperature environment, crack resistance in low temperature condition, good water stability, long-lasting anti-aging and good anti-skid property to ensure asphalt pavement Good service function. [0003] Many roads close to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B24/36C04B111/24
CPCC04B28/14C04B2111/0075C04B2111/24C04B24/36C04B7/02C04B14/06C04B14/324C04B14/24C04B14/08C04B18/08C04B2103/40C04B2103/69
Inventor 李杰
Owner 河北北方公路工程建设集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products