A kind of spray glue and preparation method thereof

A technology of glue spraying and synthetic rubber, which is applied in the direction of adhesives, rosin adhesives, adhesive additives, etc., can solve the problems not involved in permeability, etc., achieve good construction and application performance, good comprehensive performance, and reduce the penetration time.

Active Publication Date: 2018-02-06
GUANGDONG SANVO CHEM IND TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] None of the above-mentioned patents involves the disclosure of specific instructions and beneficial effects on permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of spray glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Proportion by weight, add 4 parts of methyl acetate, 4 parts of acetone, 2 parts of dimethyl carbonate, 10 parts of 6# solvent oil, and add 20 parts of hydrogenated rosin, 10 parts of petroleum resin, terpene resin 20 parts, 10 parts of SBS thermoplastic elastomer, stir until dissolved evenly; add 0.077 parts of bentonite, 0.019 parts of nano diatomite, 0.004 parts of silane coupling agent KH-550, stir well and continue to disperse for 10 minutes, add 0.1 part of zinc acrylate , Stir well and then cool and discharge.

Embodiment 2

[0029] According to the proportion by weight, add 3 parts of ethanol, 5 parts of sec-butyl acetate, 12 parts of methylal, 20 parts of petroleum ether, and add 10 parts of hydrogenated rosin, 15 parts of terpene resin, and 5 parts of glycerin rosin parts, 15 parts of SIS thermoplastic elastomer, stir until dissolved evenly; add 1.29 parts of bentonite, 0.48 parts of nano diatomaceous earth, 0.23 parts of silane coupling agent A-171, stir well and continue to disperse for 20 minutes, add 0.3 parts of zinc acrylate, After stirring evenly, cool and discharge the material.

Embodiment 3

[0031] According to the proportion by weight, add 5 parts of cyclohexane, 15 parts of methyl acetate, 5 parts of dimethyl carbonate, 10 parts of acetone, 20 parts of 6# solvent oil, and add 15 parts of phenolic resin, rosin and glycerin under stirring 40 parts of ester, 10 parts of petroleum resin, 20 parts of neoprene rubber A3020, stir until dissolved evenly; add 3.12 parts of calcium sulfate whiskers, 1.25 parts of nano-diatomaceous earth, 0.63 parts of silane coupling agent KBM-602, stir well and continue to disperse for 30 Minutes, add 0.5 parts of zinc stearate, stir evenly, then cool and discharge.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a spray adhesive and a preparation method thereof. The spray adhesive comprises the following components in parts by weight: 10-20 parts of synthetic rubber, 30-65 parts of tackifying resin, 0.1-0.5 parts of a bridging agent, 20-55 parts of organic solvent, and 0.1-5 parts of an anti-permeation agent. The spray adhesive has the following beneficial effects that the solvent system is environment-friendly, low in smell and fast to dry after the adhesive is spayed; the construction application performance is good; the comprehensive performances is good, such as bonding strength, open time and the like are excellent.

Description

technical field [0001] The invention relates to a rubber-type adhesive, in particular to a spray glue with good anti-permeability, and also relates to a preparation method of the spray glue. Background technique [0002] At present, common spray glue is mainly composed of synthetic rubber, tackifying resin, organic solvent, additives and other materials. It has the characteristics of simple preparation process, low viscosity, good sprayability, and wide application range. It is mainly used for sofas, furniture, sponges, etc. , luggage, fabric and other fields, favored by the market. [0003] However, due to the requirements of the construction process, the viscosity of the spray glue should not be too high, and a large amount of solvent must be used for dilution in the formula design. However, when ordinary spray glue is applied to the bonding of loose materials such as fabrics, it often occurs The glue penetrates to the back of the sticky material, seriously affecting the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J193/04C09J153/02C09J145/00C09J11/04C09J11/06C09J11/08
CPCC08K2201/011C08L2205/025C08L2205/035C08L2207/04C09J11/04C09J11/06C09J11/08C09J145/00C09J153/02C09J193/04C08L57/02C08L45/00C08L53/02C08K13/02C08K3/346C08K3/34C08K5/098C08L93/04C08L61/06C08L11/00
Inventor 陈炳耀陈亮陈炳强
Owner GUANGDONG SANVO CHEM IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com