A kind of coaxial cable sheath or insulating layer composition and preparation method thereof

A technology of coaxial cable and insulating layer, applied in the direction of coaxial cable, conductor/cable insulation, coaxial cable/analog cable, etc. It solves the problem of high cost and achieves the effect of low material cost, improved performance and improved mechanical properties.

Inactive Publication Date: 2017-12-08
SHENZHEN SUIRONG COAXIAL CABLE TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention aims at the problems that the existing coaxial cable fluoroplastic sheath has high cost and the existing polyethylene sheath and insulating layer have low temperature resistance, and provides a coaxial cable sheath or insulating layer composition The invention and its preparation method effectively improve the high temperature resistance of the sheath layer and the insulating layer, so that the temperature resistance can reach 260°C, and can be used in harsh working environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coaxial cable sheath or insulating layer composition and preparation method thereof
  • A kind of coaxial cable sheath or insulating layer composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] A preparation method of a coaxial cable disclosed by the invention comprises the following steps:

[0039] step one:

[0040] Form the insulating layer outside the inner conductor to obtain an insulating core wire. The specific steps are as follows:

[0041] 24-30 parts by weight of HDPE 6944, 23-28 parts by weight of LDPE 1253, 20-25 parts by weight of LLDPEDNDA-7144 and 30-43 parts by weight of HDPE 2911 are put into a high-speed mixer and mixed to prepare polyethylene base material;

[0042] 0.5-1.5 parts by weight of TMPTMA, 0.5-1.5 parts by weight of DCP, 0.5-1.2 parts by weight of PETA and 0.5-1.2 parts by weight of TPGDA are put into a high-speed mixer and mixed to prepare a crosslinking agent;

[0043] Take 90-110 parts by weight of polyethylene base material and 2-4 parts by weight of cross-linking agent, put them into a high-speed mixer and mix them to obtain cross-linked material granules for insulating layer;

[0044] Adding 1.5-2.0 parts by weight of a nu...

Embodiment 1

[0067] The preparation method of a kind of coaxial cable that present embodiment provides, comprises the following steps:

[0068] step one:

[0069] Form the insulating layer outside the inner conductor to obtain an insulating core wire. The specific steps are as follows:

[0070] 30 parts by weight of HDPE 6944, 23 parts by weight of LDPE 1253, 20 parts by weight of LLDPE DNDA-7144 and 43 parts by weight of HDPE 2911 are put into a high-speed mixer and mixed to prepare a polyethylene base material;

[0071] 1.0 parts by weight of TMPTMA, 1.0 parts by weight of DCP, 0.5 parts by weight of PETA and 0.5 parts by weight of TPGDA are dropped into a high-speed mixer and mixed to prepare a crosslinking agent;

[0072] Take 100 parts by weight of polyethylene base material and 2.5 parts by weight of crosslinking agent, put them into a high-speed mixer and mix them to obtain crosslinked material granules for insulating layer;

[0073] Adding 1.5 parts by weight of a nucleating agen...

Embodiment 2

[0086] This embodiment provides a method for preparing a coaxial cable. Most of the steps in this embodiment are the same as those in Embodiment 1, the specific differences are:

[0087] In step one, 26 parts by weight of HDPE 6944, 26 parts by weight of LDPE 1253, 23 parts by weight of LLDPEDNDA-7144 and 36 parts by weight of HDPE 2911 are put into a high-speed mixer and mixed to prepare a polyethylene base material;

[0088] In step 3, 26 parts by weight of HDPE 6944, 26 parts by weight of LDPE 1253, 23 parts by weight of LLDPEDNDA-7144 and 36 parts by weight of HDPE 2911 were put into a high-speed mixer and mixed to prepare a polyethylene base material.

[0089] The resulting coaxial cable is designated as S2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a coaxial cable sheath or insulating layer composition and a preparation method thereof. The raw materials of the sheath or insulating layer composition include the following weight components: 90-110 parts by weight of polyethylene base material: including: HDPE 6944 24-30 parts by weight, LDPE 1253 23-28 parts by weight, LLDPE DNDA-7144 20-25 parts by weight, HDPE 2911 30-43 parts by weight; crosslinking agent 2-4 parts by weight: including TMPTMA 0.5-1.5 parts by weight , DCP 0.5-1.5 parts by weight, PETA 0.5-1.2 parts by weight, TPGDA 0.5-1.2 parts by weight. The invention aims to solve the problems of high cost and heavy specificity in the existing fluoroplastic sheath of the coaxial cable, and the low temperature resistance of the existing polyethylene sheath and insulating layer.

Description

technical field [0001] The invention belongs to the technical field of coaxial cable materials, and in particular relates to a coaxial cable sheath or insulating layer composition and a preparation method thereof. Background technique [0002] The cable jacket is the protective layer of the cable against various erosions. In daily use, cables are often subjected to thermal loads (continuous or discontinuous changes in the lowest or highest temperature limits), mechanical loads (flexibility, wear resistance, tensile load and resistance to treading) or chemical corrosion (with Thinner, liquid medium and oil contact), it is necessary to set up a sheath to protect the cable. In some specific places, the sheath is required to have a certain high temperature resistance. Existing coaxial cables often use FEP, PFA and other fluorine As a sheath material, plastic has good high temperature resistance, but fluoroplastics have some disadvantages: the high material cost leads to high pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More