Metallographic corrosive agent for as-extruded Mg-Li alloy and using method of metallographic corrosive agent

A magnesium-lithium alloy and metallographic corrosion technology, which is applied in the field of metallographic etchants for extruded magnesium-lithium alloys, and can solve the problems of blurred metallographic structure, poor corrosion resistance of magnesium-lithium alloys, and difficult to precisely control the etching time. , to achieve the effect of clear and complete metallographic structure and clearly discernible grain boundaries

Active Publication Date: 2017-02-15
BEIJING INSTITUTE OF PETROCHEMICAL TECHNOLOGY
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the commonly used metallographic etchant is mainly composed of nitric acid, sulfuric acid and water, but this metallographic etchant has strong corrosiveness, and the corrosion resistance of magnesium-lithium alloy is very poor, so the existing metallographic etchant is used The etching of magnesium-lithium alloys by phase corrosive agents is not only difficult to control the etching time accurately, but also makes the metallographic structure blurred and difficult to observe and analyze.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metallographic corrosive agent for as-extruded Mg-Li alloy and using method of metallographic corrosive agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A metallographic etchant for an extruded magnesium-lithium alloy is prepared by uniformly mixing 20ml of glacial acetic acid with a mass fraction of 98%, 20ml of picric acid with a mass fraction of 50%, and 60ml of ethanol with a mass fraction of 98%.

[0024] Specifically, at room temperature, use a plastic straw to absorb the metallographic etchant of the extruded magnesium-lithium alloy described in Example 1 of the present invention, and drop it onto the polished surface of the extruded magnesium-lithium alloy A for metallographic analysis. Corrosion, the metallographic corrosion time is 5-15s, and then clean the eroded extruded magnesium-lithium alloy A with clean water, and use a cotton ball dipped in absolute ethanol to clean the surface of the extruded magnesium-lithium alloy A after cleaning. Wipe it, and then use a hair dryer to dry its surface, so that the metallographic corrosion of the extruded magnesium-lithium alloy A can be realized. The metallographic s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metallographic corrosive agent for an as-extruded Mg-Li alloy and a using method of the metallographic corrosive agent. The metallographic corrosive agent is prepared by mixing 98% by mass of glacial acetic acid, 50% by mass of picric acid and 98% by mass of ethyl alcohol, and preferably the volume ratio of glacial acetic acid to picric acid to ethyl alcohol is 20:20:60, so that metallographic corrosion of the as-extruded Mg-Li alloy can be finished conveniently and fast, and the as-extruded Mg-Li alloy subjected to metallographic corrosion has the clearest and most complete metallographic structure and clear and distinguishable grain boundaries, which is conducive to observing and analyzing the metallographic structure.

Description

technical field [0001] The invention relates to the field of metallographic corrosion of magnesium-lithium alloys, in particular to a metallographic etchant for extruded magnesium-lithium alloys and a method for using the same. Background technique [0002] Magnesium-lithium alloy is the lightest metal material used in actual industrial production, and it has the characteristics of high specific strength, high specific stiffness, and good cutting performance, so it is widely used in many fields such as electronic appliances, aerospace, national defense and military industry . [0003] Extruded magnesium-lithium alloy is the most commonly used magnesium-lithium alloy. Due to the different material composition, extrusion strength and heat treatment process used in the processing process, there are great differences in the metallographic structure of the processed extruded magnesium-lithium alloy, which makes the properties of the extruded magnesium-lithium alloy appear differ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F1/22G01N1/32
CPCC23F1/22G01N1/32
Inventor 陈飞张玉林于佩航韦银河陈佳欣
Owner BEIJING INSTITUTE OF PETROCHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap