A kind of preparation technology of composite fishing rod

A preparation process and fishing rod technology are applied in the field of preparation technology of composite fishing rods, which can solve the problem of not having insulating function and the like, and achieve the effects of light weight, high strength and good toughness

Active Publication Date: 2018-09-25
陈雨
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, the carbon content is about 30% or 90%. Fishing rods made of carbon fibers are light, solid, and high in tensile strength, but they do not have insulating functions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation process for a composite fishing rod, the steps are as follows:

[0030] (1) Send the composite material into the melting device, heat and melt to obtain a melt;

[0031] (2) Cut the non-woven fabric according to the set size, and immerse the cut non-woven fabric in the melt to combine the melt with the non-woven fabric;

[0032] (3) Wind the non-woven fabric soaked in melt on the core material, send it into the curing equipment for curing treatment, remove the core material after completion, paint and dry, and the drying is carried out in the steam drying equipment;

[0033] The curing process of the above-mentioned curing treatment is as follows:

[0034] The first curing stage: control the curing temperature in the curing room at 65°C, the relative humidity at 99%, and the curing time at 12 hours;

[0035] The second curing stage: control the curing temperature in the curing room at 70°C, the relative humidity at 99%, and the curing time at 15 hours; ...

Embodiment 2

[0041] A preparation process for a composite fishing rod, the steps are as follows:

[0042] (1) Send the composite material into the melting device, heat and melt to obtain a melt;

[0043] (2) Cut the non-woven fabric according to the set size, and immerse the cut non-woven fabric in the melt to combine the melt with the non-woven fabric;

[0044] (3) Wind the non-woven fabric soaked in the melt on the core material, send it to the curing equipment for curing treatment, remove the core material after completion, paint and dry.

[0045] The curing process of the above-mentioned curing treatment is as follows:

[0046] The first curing stage: control the curing temperature in the curing room at 65°C, the relative humidity at 99%, and the curing time at 12 hours;

[0047] The second curing stage: control the curing temperature in the curing room at 70°C, the relative humidity at 99%, and the curing time at 15 hours;

[0048] The third curing stage: control the curing tempera...

Embodiment 3

[0053] A preparation process for a composite fishing rod, the steps are as follows:

[0054] (1) Send the composite material into the melting device, heat and melt to obtain a melt;

[0055] (2) Cut the non-woven fabric according to the set size, and immerse the cut non-woven fabric in the melt to combine the melt with the non-woven fabric;

[0056] (3) Wind the non-woven fabric soaked in the melt on the core material, send it to the curing equipment for curing treatment, remove the core material after completion, paint and dry.

[0057] The curing process of the above-mentioned curing treatment is as follows:

[0058] The first curing stage: control the curing temperature in the curing room at 65°C, the relative humidity at 99%, and the curing time at 12 hours;

[0059] The second curing stage: control the curing temperature in the curing room at 70°C, the relative humidity at 99%, and the curing time at 15 hours;

[0060] The third curing stage: control the curing tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of a composite fishing rod. The preparation process is characterized by comprising the following steps: (1) a composite material is fed in melting equipment for heating and melting to obtain a melt; (2) non-woven fabric is tailored by a set size, and the tailored non-woven fabric is dipped in the melt, so that the melt is combined with the non-woven fabric; and (3) the non-woven fabric dipped with the melt is wound on a core to be fed in curing equipment for curing, and then, the core is removed for painting and drying. The preparation process is simple in step and controllable; and the prepared fishing rod is smooth and compact in surface, and is excellent in mechanical performance.

Description

technical field [0001] The invention relates to the technical field of fishing gear, in particular to a preparation process of a composite fishing rod. Background technique [0002] Along with the continuous improvement of people's living standards, fishing has become a kind of important entertainment and leisure activity for people, and competitive fishing is also carried out frequently like a raging fire. At present, the vast majority of fishing rods on the market are carbon fiber fishing rods, which are all made of carbon fiber longitudinal cloth tubes without shuttles, and are made by impregnating resin and curing. The amount of carbon fiber used in fishing rod production directly determines the value and grade of the fishing rod. Generally, the carbon content is about 30% to 90%. Fishing rods made of carbon fiber are light, solid, and high in tensile strength, but they do not have an insulating function. Contents of the invention [0003] The technical problem to be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/30B29C35/02B29C37/00C08L67/02C08L77/00C08L97/02C08K13/04C08K7/06C08K7/14C08K3/36B29L30/00
CPCB29C35/02B29C37/0092B29C70/30B29L2031/7002C08K2201/011C08L67/02C08L2205/035C08L2205/16C08L77/00C08L97/02C08K13/04C08K7/06C08K7/14C08K3/36
Inventor 陈雨
Owner 陈雨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka