A kind of interweaving fabric of mercerized cotton and mulberry silk and its preparation method
A technology of mulberry silk and mercerized cotton is applied in the field of textile fabrics, which can solve the problems of discoloration, easy pilling, yellowing and embrittlement of silk, and achieve the effects of increasing yarn feeding tension, improving weaving efficiency and fast feeding speed.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0021] An interwoven fabric of mercerized cotton and mulberry silk, comprising the following components and the parts by weight of each component: 98 parts of mercerized cotton, 73 parts of combed cotton, and 23 parts of mulberry silk. The reasonable ratio of mulberry silk, combed cotton and mercerized cotton in the present invention complements the advantages and disadvantages of mulberry silk and mercerized cotton, so that the fabric of the present invention has the characteristics of good luster, high strength and soft hand feeling.
[0022] The preparation method of the interwoven fabric of mercerized cotton and mulberry silk is set forth below, and the steps are as follows: (1) Preparation of mercerized cotton yarn: Cotton spinning is combed, singeing, mercerized, and twisted to form mercerized cotton yarn. Pima cotton is obtained through the compact spinning process for cotton spinning. (2) Preparation of combed cotton: the cotton fiber is processed by a cotton blender, ...
Embodiment 2
[0024] This embodiment refers to Example 1, and the fabric is different in that the components included and the parts by weight of each component are as follows: 100 parts of mercerized cotton, 75 parts of combed cotton, and 25 parts of mulberry silk. The difference in the preparation process is that in the mercerizing step of step (1), firstly, fine-pore silica gel is applied to the cotton spinning surface, and then the temperature in the alkali dipping tank of the mercerizing machine is controlled to be lower than 3°C, and then the cotton spinning The yarn is mercerized through a mercerizing machine. This method is the first in the industry of the present invention, not only has high mercerizing efficiency, but also has good mercerizing effect. Because cotton spinning is relatively loose and has many gaps, the mercerizing agent adhesion rate of cotton spinning is too low when mercerizing, and it is too late to fully expand the fibers when the yarn is running, and the merceri...
Embodiment 3
[0026] This embodiment refers to Example 1, and the fabric is different in that the components included and the parts by weight of each component are as follows: 102 parts of mercerized cotton, 77 parts of combed cotton, and 27 parts of mulberry silk. The difference in the preparation process is that, as figure 1 and 2 As shown, in the step of reeding in step (4), the warp thread is passed through the warp dropper 1, the heddle, and the reed successively; the both sides of the dropper wire 1 are respectively provided with a chute 12 and a slide bar 11 that are paired in structure, and then A plurality of warp droppers 1 are seamlessly connected through the chute 12 and the slide bar 11 to increase the yarn-entry tension of the warp yarn. The chute 12 and the slide bar 11 are longitudinally slidably connected, and the chute 12 and the slide bar 11 are transversely clamped. Both the chute 12 and the sliding bar 11 may be configured in a tapered structure to facilitate lateral ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| decomposition temperature | aaaaa | aaaaa |