A kind of compound modifier and the drainage asphalt concrete with high anti-scattering performance prepared by it

A composite modifier and drainage asphalt technology, applied in other household appliances, ceramic products, household appliances, etc., can solve the problems of complex operation, high preparation cost, poor scattering resistance of drainage asphalt mixture, etc., to inhibit condensation, improve Effects of adhesion, good heat aging resistance and water damage resistance

Active Publication Date: 2019-03-05
BEIJING ZHONGLU PAVING TECH +2
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] In order to solve the technical problems of poor anti-scattering performance, high preparation cost and complicated operation of drainage asphalt mixed soil in the prior art, the present invention provides:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of compound modifier and the drainage asphalt concrete with high anti-scattering performance prepared by it
  • A kind of compound modifier and the drainage asphalt concrete with high anti-scattering performance prepared by it
  • A kind of compound modifier and the drainage asphalt concrete with high anti-scattering performance prepared by it

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] 1. Prepare materials

[0082] Weigh each component according to the following parts by weight ratio,

[0083]

[0084]Among them, SBS is linear 791H produced by Yueyang Petrochemical. SBR is a powdered styrene-butadiene rubber with a solid content of 80% produced by Shandong Xianyuan Chemical Industry. The solubilizer is a mixture of furfural extract oil obtained from the naphthenic crude oil produced by Zhonghai Bitumen minus the third line after furfural refining and naphthenic oil produced from Zhonghai Bitumen in a ratio of 1:1. The crosslinking agent is powdered sulfur with a content of 99.5%, produced by Maoming Petrochemical. The accelerator is a mixture of commercially available zinc oxide and commercially available zinc dibenzyl dithiocarbamate at a ratio of 1:1. The fiber is a polyester fiber BoniFiber produced by DuPont Company of the United States, the length is 6 mm, and the elongation at break is 50%. The comprehensive additive is made by mixing com...

Embodiment 2

[0091] 1. Prepare materials

[0092] Weigh each component according to the following parts by weight ratio,

[0093]

[0094] Among them, SBS is Star 4303 produced by Yanshan Petrochemical. SBR is a powdered styrene-butadiene rubber with a solid content of 80% produced by Shandong Xianyuan Chemical Industry. The solubilizer is a mixture of catalytic cracking (FCC) oil slurry produced by Zhenhai Refining & Chemical Co., Ltd. and naphthenic oil produced by Zhonghai Bitumen in a ratio of 2:1. The crosslinking agent is powdered sulfur with a content of 99.5%, produced by Maoming Petrochemical. The accelerator is a mixture of commercially available zinc oxide: zinc dibenzyl dithiocarbamate: stearic acid in a ratio of 3:1:1. The fiber is a polyester fiber produced by Ningbo Dacheng New Material Co., Ltd., its length is 8mm, and its elongation at break is 40%. The comprehensive additive is made by mixing commercially available p-phenylenediamine antioxidant 4010, ethanol, fatt...

Embodiment 3

[0101] 1. Prepare materials

[0102] Weigh each component according to the following parts by weight ratio,

[0103]

[0104] Among them, SBS is the line type 501S produced by LG. SBR is a powdered styrene-butadiene rubber with a solid content of 100% produced in Shandong Qiaolong. The solubilizer is a mixture of naphthenic crude oil produced from Zhonghai Bitumen minus the third-line furfural-refined extracted oil and naphthenic oil produced from Zhonghai Bitumen in a ratio of 1:2. The crosslinking agent is powdered sulfur with a content of 99.5%, produced by Maoming Petrochemical. The accelerator is a mixture of commercially available zinc oxide: zinc dibenzyl dithiocarbamate: stearic acid in a ratio of 4:1:1. The fibers are flocculent lignin fibers produced by JRS Company in Germany. The comprehensive additive is made by mixing commercially available p-phenylenediamine antioxidant 4010, ethanol, fatty acid, and sodium lignosulfonate in a ratio of 3:1:2.5:2.

[0105]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite modifier and a high-scattering-resistance drainage asphalt concrete prepared through the same and relates to the field of road engineering materials. The composite modifier is composed of base materials, fiber, comprehensive additives, cross-linking agent and cross-linking promoter, wherein the base materials are composed of SBS (styrene-butadiene-styrene) modifier, SBR (styrene butadiene rubber) modifier and solubilizer. The drainage asphalt concrete prepared through the composite modifier is high in scattering resistance. Through field deployment of conventional asphalt, aggregate, mineral powder and the composite modifier, a high-performance and stable-performance drainage mixture can obtained and meanwhile is more stable in properties compared with those applying modified asphalt, so that worries on storage segregation and performance degradation of the modified asphalt can be saved, and meanwhile construction deficiencies of dispersing non-uniformity of fiber deployment and grease spots can be completely avoided.

Description

technical field [0001] The invention relates to the field of road engineering, in particular to a modified additive for making drainage asphalt mixture anti-scattering and drainage asphalt concrete prepared therefrom. Background technique [0002] Drainage asphalt pavement refers to a new type of asphalt concrete surface layer with a void ratio of 18% to 25% after compaction and can form drainage channels inside the mixture. Drainage pavement can eliminate the water film formed on the road surface in rainy days and improve driving safety and comfort. sex. In order to ensure a large void ratio, the amount of coarse aggregate in the drainage asphalt mixture accounts for more than 80%. Therefore, the strength of the drainage asphalt pavement is reduced, and the aging of the asphalt will cause the mortar to crack, and the coarse aggregate in the drainage asphalt pavement The phenomenon of falling off in pieces and flying occurs, which is accelerated by external forces such as h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L53/02C04B24/26C04B26/26C04B38/00
CPCC04B26/26C04B40/0039C04B2111/00284C04B2111/0075C04B24/2676C04B24/00C04B22/02C04B22/06C04B24/16C04B24/121C04B24/02C04B24/08C04B24/18C04B16/0683C04B16/02C04B14/00C04B18/141C04B38/0038C04B38/0074Y02A30/30
Inventor 唐国奇王涵
Owner BEIJING ZHONGLU PAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More