Hard coating film with high dyne value

A technology of hardened film and hardened layer, which is applied in the direction of coating, pretreatment surface, and device for coating liquid on the surface, etc. It can solve the problems of poor printing and coating effects, difficult to use requirements of downstream customers, and easy peeling off of coatings, etc. , to achieve good printing performance, high hardness, and improve the effect of surface adhesion

Active Publication Date: 2017-05-10
HEFEI LUCKY SCI & TECH IND
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface dyne value of existing hardened film products on the market is mostly around 32Dyne to 36Dyne, and its dyne value will show different degrees of attenuation with time and different storage conditions, resulting in poor printing and coating effects and easy coating. Falling off, it is difficult to meet the requirements of downstream customers for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hard coating film with high dyne value
  • Hard coating film with high dyne value
  • Hard coating film with high dyne value

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The components and parts by weight of the cured film coating solution are:

[0032]

[0033] Add 7 g of bisphenol A epoxy acrylic resin [manufactured by Taiwan Double Bond Chemical Co., Ltd., trade name: 127-TP20] in 14 g of aliphatic hexaacrylate resin [manufactured by Taiwan Double Bond Chemical Co., Ltd., trade name: 571] , after stirring evenly, add 5g of silica nano-additive [manufactured by BYK, trade name: NANOBYK-3651], stir again and add 0.05g of surface additive aralkyl·alkyl modified silicone [manufactured by BYK , trade name: BYK-322], 2g photoinitiator 1-hydroxycyclohexyl phenyl ketone [manufacture of Taiwan Double Bond Chemical Co., Ltd., trade name: Doublecure 184], after stirring, add 49g methyl isobutyl ketone and Diluted with 22.9 g of methyl ethyl ketone, stirred thoroughly and left to stand for 1-2 hours to obtain the hardened layer coating solution.

[0034] The coating solution for the hardening layer was coated on both sides of a PET support, ...

Embodiment 2

[0040] The components and parts by weight of the cured film coating solution are:

[0041]

[0042]Add 3g of epoxy acrylate [manufactured by Sartomer Asia Co., Ltd., trade name: CN104NS] in 12g of solvent-modified urethane acrylate resin [manufactured by Taiwan Changxing Chemical Industry Co., Ltd., trade name: DR-U092], and stir evenly Then add 2g of silicon dioxide nano-additive [manufactured by BYK, trade name: NANOBYK-3651], stir again and add 3g of surface additive polyether modified silicone [manufactured by BYK, trade name: BYK-325] , 7.0g photoinitiator 1-hydroxycyclohexyl phenyl ketone [manufacture of Taiwan Double Bond Chemical Co., Ltd., trade name: Doublecure 184], add 48.5g methyl isobutyl ketone and 31.5g propylene glycol monomethyl ether after stirring After diluting and fully stirring, let it stand for 1-2 hours to obtain the hardened layer coating solution.

[0043] The coating solution for the hardening layer was coated on both sides of a PET support body...

Embodiment 3

[0049] The components and parts by weight of the cured film coating solution are:

[0050]

[0051] Add 9 g of zinc oxide nano-additives [manufactured by BYK Chemicals, trade name: NANOBYK-3860] to 30 g of polyurethane acrylate resin [manufactured by Sartomer Asia Co., Ltd., trade name: CN750], stir evenly and add 1.5 g of surface additives [Hemings Specialty Chemical Co., trade name: Adherant ADK], 7g photoinitiator 2-hydroxyl-2-methyl-1-phenyl-1-propanone [manufactured by Taiwan Double Bond Chemical Co., Ltd., trade name: Doublecure 1173], after stirring evenly, add 52.5g of isopropanol for dilution, fully stir and then let it stand for 1-2h to obtain the hardened layer coating solution.

[0052] The coating solution for the hardening layer was coated on both sides of a PET support, the thickness of the PET support was 125 microns, and the control coating thickness was 3.5 microns. After testing, the viscosity of the above-mentioned coating liquid is 3.4mPa.s, the solid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hard coating film with a high dyne value, comprising a PET supporter, and a hard coating layer formed by solidifying after coating hard coating layer coating on at least one surface of the PET supporter, wherein the hard coating layer coating has the following components in parts by weight: 15-50 parts of matrix resin, 2-10 parts of oxide particles, 0.05-5.0 parts of surface additive, 0.05-7.0 parts of photoinitiator and 40-80 parts of solvent. The dyne value of the hard coating film provided by the invention can reach 38Dyne-46Dyne, thus being capable of meeting operating requirements of customers on subsequent ITO coating technology and ink printing technology.

Description

technical field [0001] The present invention relates to coating compositions, especially a hardened film having a high factor value. Background technique [0002] Hardened film is a film product obtained by surface hardening treatment on a PET support. The product has good optical properties, excellent scratch resistance, heat resistance and appearance quality. Mainly used in the touch screen industry, widely used in touch panels, liquid crystal displays, instrument panels, mobile phones, tablet computers, digital cameras, notebook computers and industrial displays, etc. At present, there are many kinds of hardened film products on the market, and the common hardness ranges from 1H to 4H, which are mass-produced. In the subsequent processing, in addition to the basic performance requirements, the surface hardened layer is also required to have good adhesion to the ink to ensure excellent printing. As a result, in the hardened film products for ITO coating, in order to achi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D175/14C09D167/06C09D7/12C08J7/04B05D3/02
CPCB05D3/0254C08J7/0427C08J2367/02C08J2463/10C08J2467/06C08J2475/14C08K3/22C08K3/36C08K2003/2296C08K2201/011C08L2205/03C09D7/61C09D163/10C09D167/06C09D175/14C08L71/00C08L63/10C08K2003/2227
Inventor 徐倩倩王辉刘玉磊史良赵俊武胡鑫
Owner HEFEI LUCKY SCI & TECH IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap