A kind of TPV composition and preparation method thereof

A composition, polypropylene technology, applied in the directions of adhesive additives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of degumming, insufficient bonding strength, etc. The effect of surface polarity, good absorption effect

Active Publication Date: 2022-05-31
会通新材料(上海)有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, it is necessary for the present invention to provide a TPV composition and a preparation method thereof. With PP and EPDM as the base, a plasticizer and a crosslinking agent are added therein, and other auxiliary agents are used to obtain a TPV composition with high packaging Adhesive bonding strength, which solves the degumming problem caused by the insufficient bonding strength of the existing TPV and ABS coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of TPV composition and preparation method thereof
  • A kind of TPV composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] In order to facilitate the understanding of the present invention, the present invention will be described more fully below with reference to specific embodiments. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein. Rather, these embodiments are provided so that a thorough and complete understanding of the present disclosure is provided.

[0030] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The terms used herein in the description of the present invention are for the purpose of describing specific embodiments only, and are not intended to limit the present invention.

[0031] Components in the following examples and comparative examples:

[0032] Component A: homopolymer PP, grade 1100N, melting index 11g / 10min, purchased from Shenhua Chemical;

[0033] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a TPV composition and a preparation method thereof, which consists of 30-40 parts of polypropylene, 20-30 parts of EPDM rubber, 20-30 parts of plasticizer, 10-20 parts of filler, lubricating 0.2-1 part of agent, 0.2-1 part of cross-linking agent, 0.5-2 part of auxiliary cross-linking agent, 0.3-0.5 part of antioxidant and 1-5 parts of porous adsorbent. In the present invention, special additives are added to the formulation, so that the prepared TPV composition has high encapsulation bonding strength.

Description

technical field [0001] The invention belongs to polymer materials, in particular to a TPV composition and a preparation method thereof. Background technique [0002] ABS (acrylonitrile-butadiene-styrene terpolymer) resin is a thermoplastic material with high rigidity and high toughness. Its surface has high gloss and can be used for high-gloss black appearance parts. However, in some products, it is necessary to use secondary injection of soft rubber to improve the soft touch and anti-slip effect of the product, such as the application in the camera base. [0003] Due to the characteristics of vulcanized rubber, TPV has a touch similar to that of human skin, and is widely used in various fields. However, the basic materials of TPV are PP and EPDM, both of which are non-polar materials. The commonly used plasticizers are also non-polar paraffin oil or naphthenic oil, which is difficult to form a good surface bonding effect with ABS. For example, in Chinese patent CN10349742...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/16C08L91/00C08K13/06C08K9/06C08K7/26C08K3/26C08K5/098C08K5/14C09J123/12C09J123/16C09J11/04C09J11/08C09J11/06
CPCC08L23/12C08L23/16C09J123/12C09J123/16C09J11/04C09J11/08C09J11/06C08K2201/006C08K2003/265C08L2205/03C08L91/00C08K13/06C08K9/06C08K7/26C08K3/26C08K5/098C08K5/14
Inventor 宋剑峰官冰周海周润发李荣群
Owner 会通新材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More