A kind of preparation method of laminated chip type magnetic bead

A multi-layer chip, magnetic bead technology, applied in the application of magnetic film to substrate, inductance/transformer/magnet manufacturing, coil manufacturing, etc., can solve the problems of low efficiency, large shrinkage, long production cycle, etc. The effect of improving production efficiency, reducing magnet shrinkage and shortening production cycle

Active Publication Date: 2018-10-16
GUANGDONG FENGHUA BANGKE ELECTRONIC CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of long production cycle, low efficiency and large shrinkage caused by the production of laminated chip magnetic beads by the wet casting process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of laminated chip type magnetic bead

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1: A laminated chip magnetic bead, its structure is as follows figure 1 As shown, the lower substrate 1 and the upper substrate 9 are produced by a dry casting process, the intermediate dielectric films 4 and 7 are produced by a wet casting process, and the lower terminal 2, the upper terminal 8, the coil 5, and the printing points 3 and 6 They are printed alternately by two screen printing machines. The preparation method comprises the steps of:

[0041] (1) Preparation of slurry:

[0042] Evenly mix the ferrite powder with uniform magnetic permeability and organic solvent, add dispersant, plasticizer and defoamer at the same time, mix the slurry evenly through high-energy ball milling; then add binder and perform secondary ball milling, The mass percentage of each substance is: 56% of ferrite magnetic powder, 5% of PVB adhesive, 35% of organic solvent, 1% of dispersant, 2% of plasticizer, and 1% of defoamer;

[0043] (2) Dry casting:

[0044] Use a high...

Embodiment 2

[0065] Embodiment 2: A laminated chip magnetic bead, its structure is as follows figure 1 As shown, the lower substrate 1 and the upper substrate 9 are produced by a dry casting process, the intermediate dielectric films 4 and 7 are produced by a wet casting process, and the lower terminal 2, the upper terminal 8, the coil 5, and the printing points 3 and 6 They are printed alternately by two screen printing machines. The preparation method comprises the steps of:

[0066] (1) Preparation of slurry:

[0067] Evenly mix the ferrite powder with uniform magnetic permeability and organic solvent, add dispersant, plasticizer and defoamer at the same time, mix the slurry evenly through high-energy ball milling; then add binder and perform secondary ball milling, The mass percentage of each substance is: ferrite magnetic powder 44%, PVB adhesive 8%, organic solvent 45%, dispersant 1%, plasticizer 1%, defoamer 1%;

[0068] (2) Dry casting:

[0069] A high-precision steel belt cast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of electronic components, in particular to a preparation method of a laminated magnetic bead. A dry casting process is adopted for producing an upper substrate and a lower substrate of the laminated magnetic bead; a wet casting process is adopted for producing an internal dielectric film, and an internal coil of the laminated magnetic bead is manufactured by combining a screen printing process; and an isostatic pressing method is adopted by subsequent procedures, thereby ensuring the consistency of magnet shrinkage rates of a dry method and a wet method. The problems of a long production cycle and low efficiency are solved; and meanwhile, the quality problem of a laminated magnetic bead stress jumper is also solved. According to the preparation method, the magnet shrinkage rate of the magnetic bead is reduced, the production efficiency is improved and the production cycle of the magnetic bead is shortened to within 12 days from 15 days.

Description

technical field [0001] The invention relates to the field of electronic components, in particular to a method for preparing laminated chip magnetic beads. Background technique [0002] The magnetic bead is an inductor filled with a magnetic core. It uses its impedance to increase rapidly at high frequencies and the electromagnetic loss mechanism of magnetic materials to suppress and absorb high-frequency noise, thereby achieving the purpose of anti-electromagnetic interference. Multilayer chip magnetic bead is a high-tech product developed in recent years. With the development of industrial automation, especially the development of modern communication industry (such as mobile phones and other portable terminal products), the multilayer chip magnetic bead is characterized by its Good magnetic shielding, miniaturization and other advantages have become key products in the field of electronic components. Its applications range from mobile devices, computers, servers, personal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/28H01F41/04
CPCH01F41/0233H01F41/042H01F41/28
Inventor 李孔俊高泮嵩
Owner GUANGDONG FENGHUA BANGKE ELECTRONIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com