Hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst as well as preparation method and application thereof

A hexagonal boron nitride and graphitization technology, applied in the field of photocatalysis, can solve the problems of weak separation ability of photogenerated carriers, poor photocatalytic activity, and low specific surface area, achieve fast pre-adsorption of pollutants, increase migration speed, The effect of increasing the specific surface area

Active Publication Date: 2017-05-31
HUNAN UNIV
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the energy gap of pure phase graphitized carbon nitride is about 2.7 eV, which can only use sunlight below 460 nm, and the polymerization product is a dense block particle, which has low specific surface area, weak separation ability of photogenerated carriers, and photocatalytic Poor activity and other problems limit the wide application of this material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst as well as preparation method and application thereof
  • Hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst as well as preparation method and application thereof
  • Hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the present invention, the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst uses graphitized carbon nitride as a carrier, and the graphitized carbon nitride carrier is modified Layered hexagonal boron nitride.

[0035] In this embodiment, the mass percentage of hexagonal boron nitride in the hexagonal boron nitride-modified graphitized carbon nitride composite photocatalyst is 0.22%.

[0036] The preparation method of the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the above-mentioned present embodiment comprises the following steps:

[0037](1) Mix 1 mg hexagonal boron nitride and 1 g dicyandiamide in an agate mortar, and grind continuously for 30 min to obtain the precursor of the mixture.

[0038] (2) Put the mixture precursor of hexagonal boron nitride and graphitized carbon nitride precursor obtained...

Embodiment 2

[0042] A hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the present invention, the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst uses graphitized carbon nitride as a carrier, and the graphitized carbon nitride carrier is modified Layered hexagonal boron nitride.

[0043] In this embodiment, the mass percentage of hexagonal boron nitride in the hexagonal boron nitride-modified graphitized carbon nitride composite photocatalyst is 0.44%.

[0044] The preparation method of the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the above-mentioned present embodiment comprises the following steps:

[0045] (1) Mix 2 mg of hexagonal boron nitride and 1 g of dicyandiamide in an agate mortar, and grind continuously for 30 min to obtain the precursor of the mixture.

[0046] (2) Put the mixture precursor of hexagonal boron nitride and graphitized carbon nitride precursor o...

Embodiment 3

[0053] A hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the present invention, the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst uses graphitized carbon nitride as a carrier, and the graphitized carbon nitride carrier is modified Layered hexagonal boron nitride.

[0054] In this embodiment, the mass percentage of hexagonal boron nitride in the hexagonal boron nitride-modified graphitized carbon nitride composite photocatalyst is 0.88%.

[0055] The preparation method of the hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst of the above-mentioned present embodiment comprises the following steps:

[0056] (1) Mix 4 mg hexagonal boron nitride and 1 g dicyandiamide in an agate mortar, and grind continuously for 30 min to obtain the precursor of the mixture.

[0057] (2) Put the mixture precursor of hexagonal boron nitride and graphitized carbon nitride precursor obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst as well as a preparation method and application thereof. According to the composite optical catalyst, by taking graphitized carbon nitride as a carrier, laminated hexagonal boron nitride modifies the graphitized carbon nitride carrier. The preparation method comprises the following steps: mixing the hexagonal boron nitride with a graphitized carbon nitride precursor; and calcining the mixed precursor to obtain the hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst. The hexagonal boron nitride modified graphitized carbon nitride composite optical catalyst disclosed by the invention has the advantages of being environmentally friendly, fully free of metal doping, large in specific surface area, high in photoproduction electron-hole separating efficiency, high in optical catalytic activity, good in stability, corrosion-resistant and the like. The preparation method has the advantages of being simple, low in cost of raw materials, less in energy consumption, easy to control conditions and the like. The composite optical catalyst disclosed by the invention is used for degrading dye wastewater and has the advantages of being simple in application method, stable in optical catalytic performance, high in corrosion resistance, high in dye wastewater degrading efficiency.

Description

technical field [0001] The invention belongs to the technical field of photocatalysis, and in particular relates to a hexagonal boron nitride modified graphitized carbon nitride composite photocatalyst and a preparation method and application thereof. Background technique [0002] With the increasingly serious energy crisis and environmental pollution problems, new energy technologies and new environmental purification technologies have attracted much attention. As a green technology, photocatalytic technology has made great progress in recent years. Photocatalytic reactions can not only split water to generate clean hydrogen energy, but also show great potential in photodegradation of environmental pollution. Photocatalytic purification technology has the advantages of small secondary pollution, low operating cost, and the use of solar energy to provide reaction driving force. It has broad application prospects in wastewater purification treatment and air purification. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J35/10C02F1/30
CPCC02F1/30B01J27/24C02F2101/308C02F2305/10B01J35/61B01J35/39Y02W10/37
Inventor 袁兴中蒋龙波梁婕王侯吴志斌张进陈晓红李辉曾光明
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com