Preparation process of cover glass of wet-type water meter

A preparation process and technology for panel glass, applied in glass manufacturing equipment, glass molding, manufacturing tools, etc., can solve problems such as easy freezing of water, damage to water meters, and crushing of glass plates, and achieve homogeneous material dispersion, Reasonable compatibility, improve the effect of corrosion resistance and high temperature resistance

Active Publication Date: 2017-05-31
天津市金凤来仪科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing wet water meter is mainly composed of a watch case, a metering part installed in the watch case, an impeller part, and a master-slave transmission magnet. The chamber of the component and the impeller component are installed in the water flow chamber. After all the components are installed, the space in the watch case is basically fixed, that is, its volume remains unchanged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] A preparation process of wet-type water surface plate glass, which comprises the following steps:

[0019] Step 1) Preparation of component A: add calcite and fluorite into a crusher in a mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 100 mesh, which is component A;

[0020] Step 2) Preparation of component B: add kaolin and diatomite into the stirred reactor in a mass ratio of 2:1, then add twice the mass of 1M hydrochloric acid, stir at 300 rpm for 5 minutes, dry at 80°C, and grind To a particle size of 100 meshes, component B is obtained;

[0021] Step 3) Preparation of component C: dolomite is sent to a calciner for calcination, the calcination temperature is 600°C, the calcination time is 10min, taken out, cooled, and then mixed with potassium hexafluoroantimonate, cerium oxide, and sodium peroxodisulfate according to 20: The mass ratio of 3:2:1 is mixed evenly, and then ground into a fine powder with ...

Example Embodiment

[0024] Example 2

[0025] A preparation process of wet-type water surface plate glass, which comprises the following steps:

[0026] Step 1) Preparation of component A: add calcite and fluorite into a crusher in a mass ratio of 2:1 for crushing, and then grind to obtain a powder with a particle size of 100 mesh, which is component A;

[0027] Step 2) Preparation of component B: add kaolin and diatomite into the stirred reactor in a mass ratio of 2:1, then add twice the mass of 1M hydrochloric acid, stir at 300 rpm for 5 minutes, dry at 80°C, and grind To a particle size of 100 meshes, component B is obtained;

[0028] Step 3) Preparation of component C: dolomite is sent to a calciner for calcination, the calcination temperature is 600°C, the calcination time is 10min, taken out, cooled, and then mixed with potassium hexafluoroantimonate, cerium oxide, and sodium peroxodisulfate according to 20: The mass ratio of 3:2:1 is mixed evenly, and then ground into a fine powder with ...

Example Embodiment

[0031] Example 3

[0032] The performance test of the panel glass prepared in Example 1-2 of the present invention takes a panel glass with a thickness of 3 mm as an example:

[0033] Table 1

[0034] group Internal compressive strength Mpa Visible light transmittance% Flexural strength MPa Example 1 5.68 99.4 11.2 Example 2 5.79 99.5 11.5

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation process of cover glass of a wet-type water meter. The preparation process comprises the following steps: step 1), preparing a component A; step 2), preparing a component B; step 3), preparing a component C; step 4), preparing a glass plate; and step 5), preparing cover glass. The preparation process of cover glass of a wet-type water meter in the invention is simple to operate, and suitable for large-scale production, and the cover glass produced is excellent in property.

Description

technical field [0001] The invention belongs to the field of instrumentation preparation, and in particular relates to a preparation process of wet water surface plate glass. Background technique [0002] A wet water meter is a water meter with a counter immersed in water. The glass on the watch is subjected to water pressure. The transmission of the sensor and the counter is a gear linkage. The existing wet water meter is mainly composed of a watch case, a metering part installed in the watch case, an impeller part, and a master-slave transmission magnet. The chamber of the component and the impeller component are installed in the water flow chamber. After all the components are installed, the space in the watch case is basically fixed, that is, its volume remains unchanged. This constant volume is convenient for water meter measurement and installation, but When the outside temperature is lower than zero degrees Celsius, the accumulated water in the watch case is easy to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C3/115C03C3/078C03B19/02C03C21/00G01F15/14
CPCC03B19/02C03C3/078C03C3/115C03C21/001C03C21/002G01F15/14
Inventor 尹梦珍杨昆徐怀洪
Owner 天津市金凤来仪科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap