Blank of reinforced magnesia porcelain

A technology for strengthening magnesia porcelain and blanks, which is applied in the field of ceramics to achieve the effect of crisp sound and high transparency

Inactive Publication Date: 2017-05-31
湖南新辉陶瓷有限责任公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a reinforced magnesia porcelain blank with crisp sound after fir

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blank of reinforced magnesia porcelain
  • Blank of reinforced magnesia porcelain
  • Blank of reinforced magnesia porcelain

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1

[0013] The blank of the reinforced magnesia porcelain is composed of the following raw materials according to mass percentage:

[0014]

[0015]

[0016] The preparation method of the blank of the strengthened magnesia porcelain in this embodiment is to pulverize white talc, black talc, albite, potash feldspar, quartz, washed mud, and inner Mongolian soil respectively, pass through a 200-400 mesh sieve, and weigh according to mass percentage After that, add proper amount of water and stir to make.

Example Embodiment

[0017] Example 2

[0018] The blank of the reinforced magnesia porcelain of this embodiment is composed of the following raw materials according to mass percentage:

[0019]

[0020] The preparation method of the blank of the strengthened magnesia porcelain in this embodiment is to pulverize white talc, black talc, albite, potash feldspar, quartz, washed mud, and inner Mongolian soil respectively, pass through a 200-400 mesh sieve, and weigh according to mass percentage After that, add appropriate amount of water and stir to make.

Example Embodiment

[0021] Example 3

[0022]

[0023]

[0024] The preparation method of the blank of the strengthened magnesia porcelain in this embodiment is to pulverize white talc, black talc, albite, potash feldspar, quartz, washed mud, and inner Mongolian soil respectively, pass through a 200-400 mesh sieve, and weigh according to mass percentage After that, add appropriate amount of water and stir to make.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a blank of reinforced magnesia porcelain. The blank contains the following raw materials in percentage by mass: 58-60% of white talc, 22-24% of black talc, 0.8-1.2% of albite, 2-4% of potassium feldspar, 6-8% of quartz, 4-6% of washing sludge and 1-4% of Inner Mongolia soil. In the blank of reinforced magnesia porcelain disclosed by the invention, by adopting natural mineral raw materials and through repeated dosing experiments, the raw materials in the magnesia body are well matched, a reinforced magnesia porcelain product which has the advantages of clear sound, rare breakage and high transparency is obtained, and each performance meets the requirements of GB/T3532-1995 standard.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a blank for strengthening magnesia porcelain. Background technique [0002] Ceramics have a history of thousands of years in the history of human production, and daily-use ceramics are the oldest and most traditional ceramics among a wide variety of ceramic products. At present, the types of porcelain are very rich, and the development of vessel types and decorations is changing with each passing day, and technological innovations are emerging one after another. With the continuous improvement of people's living standards, the demand for practicality and artistic appreciation of ceramic products is more urgent. Ceramic art modeling, art decoration, and sculpture products are very rich, and various products are constantly innovated and enriched, which enriches people's artistic needs. However, artistic ceramics are limited to display and decoration, and are only for appreciatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13C04B33/04
CPCC04B33/13C04B33/04C04B2235/3418C04B2235/3472
Inventor 罗新甲
Owner 湖南新辉陶瓷有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap