Preparation method of organic phosphatizing flame-retardant automobile anti-abrasion material
An anti-wear material and organophosphorus technology, applied in the field of materials, can solve the problems of poor fire and flame retardancy, poor matrix compatibility, etc., and achieve good fire and flame retardant performance, good lubricating performance, and reduce the effect of agglomeration
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] A method for preparing an organic phosphating flame-retardant automobile wear-resistant material, comprising the following steps:
[0020] (1) Take 1 part by weight of calcium ricinoleate, add it to 7 times the weight of absolute ethanol, stir evenly, add 5 parts by weight of trimethylolpropane, and keep stirring at 70°C for 20 minutes to obtain alkane base alcohol dispersion;
[0021] (2) Take 2 parts by weight of ammonium polyphosphate, mix with 4 parts by weight of oleic acid, heat and stir at 60°C for 1 hour, mix with the above-mentioned alkyl alcohol dispersion, add 0.13 parts by weight of sodium methoxide, and send it to Into the reaction kettle, feed nitrogen gas, heat and stir at 95°C for 30 minutes, discharge the material, and cool to normal temperature to obtain phosphating lubricating ester;
[0022] (3) Take 2 parts by weight of tetrakis hydroxymethyl phosphorus sulfate, add it to tetrahydrofuran which is 4 times its weight, stir evenly, add 0.8 parts by we...
PUM
Property | Measurement | Unit |
---|---|---|
peak heat release rate | aaaaa | aaaaa |
oxygen index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap