A kind of preparation method of surface-modified g-c3n4

Abstract

The invention belongs to the fields of materials and catalysis and relates to a preparation method of surface-modified g-C3N4. The preparation method comprises the following steps: firstly, creatively carrying out direct high-temperature reaction on sodium halide, potassium halide or a mixture of sodium halide and potassium halide and g-C3N4; introducing water in the reaction process and enabling the modified g-C3N4 to contain hydroxide radicals; modifying corresponding metal ions on the surface of the modified g-C3N4. The method has the characteristics of simple operation, easiness in realization, low-priced and easily-obtained reaction raw materials, environment friendliness, high yield of the modified g-C3N4 and the like; in addition, abundant hydroxide radicals and porous structures on the surface of the modified g-C3N4 surface can generate abundant hydroxyl free radicals under visible light; the characteristics lay a foundation for actual application of the modified g-C3N4 in the field of photocatalysis.

Description

technical field [0001] The invention belongs to the field of material and catalysis science, in particular to a surface-modified g-C 3 N 4 method of preparation. The method is through a simple high-temperature reaction method, in g-C 3 N 4 Hydroxyl groups are formed on the surface of the material and loaded with metal ions. This method is implemented for the first time. Through this method, large quantities of surface-modified g-C can be rapidly and batch-prepared 3 N 4 , has broad prospects in the fields of solar cells, heterogeneous catalysis, and degradation of organic matter. Background technique [0002] g-C 3 N 4 (Graphitic Carbon Nitride, abbreviated as g-C 3 N 4 ) is an organic semiconductor material with a graphite-like structure. Since it was discovered in 2009 that it has photocatalytic hydrogen evolution activity, it has been extensively studied due to its stable physical and chemical stability, small band gap (2.7eV), and easy preparation method. Ho...

AI Technical Summary

Problems solved by technology

However, since g-C prepared by the traditional one-pot method 3 N 4 The shortcomings of small specific surface area, narrow visible light absorption range, and low catalytic activity limit its application in the field of catalysis, so people have carried out a lot of research on its modification, including morphology design, metal ion doping, and organic molecule copolymerization. , Construction of semiconductor heterojunctions, etc., have made some progress

However, since g-C 3 N 4 High physical and chemical stability, but there are few studies on its surface modification, and the abundant amine defect groups on its surface can provide the possibility for modification research