Vacuum insulated panel with excellent fireproof performance and production method thereof

A vacuum insulation panel, an excellent technology, applied in fire protection, chemical instruments and methods, insulation improvement, etc., can solve the problems of high equipment requirements, non-environmental protection, high production cost, etc. good burning effect

Active Publication Date: 2017-08-08
QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned technical scheme needs to press the thermal insulation powder under the condition of 850-1250kPa for 28-32 seconds to obtain the powder pressing layer, and the required pressure is as high as 8.5-12.5 atmospheres, which has extremely high requirements on equipment, and its production cost high, not environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vacuum insulated panel with excellent fireproof performance and production method thereof
  • Vacuum insulated panel with excellent fireproof performance and production method thereof
  • Vacuum insulated panel with excellent fireproof performance and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A vacuum insulation panel with excellent fire resistance, comprising a core board and a high-resistance gas film bag 3, the high-resistance gas film bag 3 is packaged outside the core board, the core board includes a core material 1 and a cladding material 2, and the cladding material 2 is packaged On the outside of the core material 1, the cladding material 2 is an inorganic cotton felt, and the surface density of the inorganic cotton felt is 50g / m 2 , the organic gum content mass fraction is 10%, and the combustion heat value is 0.17MJ / m 2 ; The total heat of combustion of the high resistance gas film bag 3 is 3.05 MJ / m 2 .

[0045] The core material 1 includes 20 parts of precipitated silicon dioxide, 50 parts of fumed silicon dioxide, 10 parts of airgel, 8 parts of inorganic fiber and 0.7 parts of vacuum stabilizer in parts by weight.

[0046] The inorganic felt is a glass fiber felt made of ultrafine glass wool.

[0047] The high-barrier gas film bag 3 is compos...

Embodiment 2

[0054] A vacuum insulation panel with excellent fireproof performance, comprising a core board and a high-resistance gas film bag, the high-resistance gas film bag is packaged outside the core board, the core board includes a core material and a cladding material, and the cladding material is packaged outside the core material. The covering material is an inorganic cotton felt, and the surface density of the inorganic cotton felt is 40g / m 2 , the organic gum content mass fraction is 10%, and the combustion heat value is 0.15MJ / m 2 ; The total heat of combustion value of the high resistance gas film bag is 2.94 MJ / m 2 .

[0055] The core material comprises 20 parts of microsilica fume, 50 parts of precipitated silicon dioxide, 10 parts of fumed silicon dioxide, 28 parts of airgel, 5 parts of inorganic fiber and 4.2 parts of vacuum stabilizer in parts by weight.

[0056] The inorganic felt is aluminum silicate fiber felt.

[0057] The high-barrier gas film bag is composed of ...

Embodiment 3

[0064] A vacuum insulation panel with excellent fireproof performance, comprising a core board and a high-resistance gas film bag, the high-resistance gas film bag is packaged outside the core board, the core board includes a core material and a cladding material, and the cladding material is packaged outside the core material. The covering material is an inorganic cotton felt, and the surface density of the inorganic cotton felt is 60g / m 2 , the organic gum content mass fraction is 15%, and the combustion heat value is 0.28MJ / m 2 ; The total heat of combustion of the high resistance gas film bag is 3.27MJ / m 2 .

[0065] The core material comprises 40 parts of precipitated silicon dioxide, 20 parts of fumed silicon dioxide, 25 parts of airgel, 5 parts of inorganic fiber and 2 parts of vacuum stabilizer in parts by weight.

[0066] The inorganic felt is calcium carbonate fiber felt.

[0067] The high-barrier gas film bag is composed of inorganic fiber film, glass fiber cloth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a vacuum insulated panel with excellent fireproof performance. The vacuum insulated panel with the excellent fireproof performance comprises a core plate and a high-resistance air film bag. The high-resistance air film bag is mounted outside the core plate in a sealed mode, the core plate comprises a core material and a coating material, the coating material is mounted outside the core material in a sealed mode, the coating material is inorganic cotton felt, the surface density of the inorganic cotton felt is 25-150 g/m<2>, and the content mass fraction of organic glue is 6-25%; and the gross combustion heat valve of the high-resistance air film bag is 2.0-3.9 MJ/m<2>, and the total layer number of thin films forming the high-resistance air film bag is smaller than or equal to six. According to the vacuum insulated panel with the excellent fireproof performance, by controlling the surface density of the inorganic cotton felt, the content of the organic glue, the thickness of the thin films with the heat seal effect and in the high-resistance air film bag, the total layer number of the thin films and the gross combustion heat valve of high-resistance air films, the vacuum insulated panel has the advantages of being excellent in fireproof performance, good in flame-retarding effect, high in stabproof strength, good in heat preservation effect, low in pressing pressure, short in pressing time, not prone to being cracked and short in curing time after mortar coating.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a vacuum insulation panel with excellent fireproof performance. Background technique [0002] At present, the materials used for building exterior wall insulation are divided into A-grade thermal insulation materials and B-grade thermal insulation materials. A-grade thermal insulation materials have good fire performance, but their thermal insulation performance, water resistance, and puncture resistance are lower than B-grade thermal insulation materials, and There are problems such as high price, complicated construction technology and short life. At present, the high-efficiency thermal insulation materials whose combustion performance can reach Class A are mainly inorganic cotton thermal insulation materials, mainly including plate thermal insulation materials of various rock wool, mineral wool, and glass wool products; while B-grade thermal insulation materials hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/80E04B1/94C04B30/00B32B9/00B32B3/04B32B37/00
CPCB32B3/04B32B5/02B32B9/00B32B37/00B32B2307/304B32B2307/3065C04B30/00E04B1/803E04B1/942C04B14/06C04B14/42C04B18/146C04B14/064C04B14/4656C04B14/38Y02A30/242Y02B80/10
Inventor 翟传伟李壮贤刘婷刘静
Owner QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap