Environment-friendly rubber sound insulation building material and preparation method thereof
A technology of building materials and environmentally friendly rubber, which is applied in the field of building materials, can solve the problems of shortening the attenuation conversion time of sound waves, reducing the specific surface area of materials, and failing to achieve sound absorption effects, etc., to achieve enhanced heat insulation effects, good safety, and mechanical properties Improved effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1.
[0031] An environmentally-friendly rubber sound-proof building material of this embodiment includes the following raw materials by weight:
[0032] 50 parts of isoprene rubber, 20 parts of fluorosilicone rubber, 3 parts of heat stabilizer, 0.5 parts of crosslinking agent, 5 parts of rare earth oxide filler, 4 parts of glass beads, 3 parts of vulcanizing agent PDM, 2 parts of silane coupling agent, 6 parts of ore powder.
[0033] The heat stabilizer in this embodiment is a mixture of zinc stearate, calcium stearate, and magnesium stearate in a weight ratio of 2:1:1.
[0034] The crosslinking agent in this embodiment is a mixture composed of diethylbenzene peroxide and di-tert-butyl peroxide in a weight ratio of 2:1.
[0035] The rare earth oxide filler in this embodiment is a mixture composed of neodymium oxide, lanthanum oxide and cerium oxide in a weight ratio of 1:1:1, and the rare earth oxide filler is powder with a particle size of 200-250 microns.
[0036] In th...
Example Embodiment
[0042] Example 2.
[0043] An environmentally-friendly rubber sound-proof building material of this embodiment includes the following raw materials by weight:
[0044] 60 parts of isoprene rubber, 30 parts of fluorosilicone rubber, 5 parts of heat stabilizer, 0.9 parts of crosslinking agent, 9 parts of rare earth oxide filler, 8 parts of glass beads, 5 parts of vulcanizing agent PDM, 4 parts of silane coupling agent, 10 parts of ore powder.
[0045] The heat stabilizer in this embodiment is a mixture of zinc stearate, calcium stearate, and magnesium stearate in a weight ratio of 2:1:1.
[0046] The crosslinking agent in this embodiment is a mixture composed of diethylbenzene peroxide and di-tert-butyl peroxide in a weight ratio of 2:1.
[0047] The rare earth oxide filler in this embodiment is a mixture composed of neodymium oxide, lanthanum oxide and cerium oxide in a weight ratio of 1:1:1, and the rare earth oxide filler is powder with a particle size of 200-250 microns.
[0048] In t...
Example Embodiment
[0054] Example 3.
[0055] An environmentally-friendly rubber sound-proof building material of this embodiment includes the following raw materials by weight:
[0056] 55 parts of isoprene rubber, 25 parts of fluorosilicone rubber, 4 parts of heat stabilizer, 0.7 parts of crosslinking agent, 7 parts of rare earth oxide filler, 6 parts of glass beads, 4 parts of vulcanizing agent PDM, 3 parts of silane coupling agent, 8 parts of ore powder.
[0057] The heat stabilizer in this embodiment is a mixture of zinc stearate, calcium stearate, and magnesium stearate in a weight ratio of 2:1:1.
[0058] The crosslinking agent in this embodiment is a mixture composed of diethylbenzene peroxide and di-tert-butyl peroxide in a weight ratio of 2:1.
[0059] The rare earth oxide filler in this embodiment is a mixture composed of neodymium oxide, lanthanum oxide and cerium oxide in a weight ratio of 1:1:1, and the rare earth oxide filler is powder with a particle size of 200-250 microns.
[0060] In th...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Wall thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap