A kind of titanium series polyester catalyst and the method for producing copolyester thereof

A technology of titanium-based polyester and catalyst, which is applied in the field of titanium-based polyester catalyst and the production of copolyester by using the catalyst, can solve the problems of high equipment requirements, yellowing of polyester products, complicated preparation process, etc., and achieve intrinsic viscosity High, reduce side reactions, improve the effect of solubility

Active Publication Date: 2020-08-21
JIANGSU JINGHONG NEW MATERIAL TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For germanium-based catalysts, due to the scarcity of germanium resources in nature, germanium-based catalysts are expensive and rarely used in polyester production
For a long time, titanium-based catalysts have become the most researched type of polyester catalysts due to their high catalytic activity and safety and environmental protection. However, titanium-based catalysts also have disadvantages such as poor stability and yellowing of polyester products.
[0004] CN103539928A discloses a production method of a titanium-based polyester catalyst, but its preparation process is relatively complicated, and is only used in the synthesis of PET; CN103709383 provides a titanium-based catalyst, using nano-silica as a carrier, and ethylene glycol Titanium is used as a catalytic active center, but the polyester chip b value prepared by it is relatively large; CN1962720B provides a method for preparing a titanium-based catalyst, but the preparation process requires vacuum distillation, which requires high equipment, and the catalyst is only used in Production of PET

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation of titanium series polyester catalyst A:

[0025] Add 56.8 g (0.2 mol) of tetraisopropyl titanate and 124 g (2 mol) of ethylene glycol into a reaction kettle equipped with a distillation device, mix well and stir for 5 minutes. Heating to 120°C under the protection of nitrogen produced a white solid. After reacting for 9 h, a total of 47.8 g of isopropanol was distilled out. Add 28 grams (0.2 moles) of trimethyl phosphate, heat to 180° C. and react for 5 hours, and finally obtain milky white titanium-based polyester catalyst A.

[0026] Preparation of copolyester:

[0027] 20 kg of terephthalic acid, 7.47 kg of ethylene glycol and 3.76 kg of neopentyl glycol were made into a slurry and put into a reaction kettle for esterification at a temperature of 250°C and a pressure of 0.15 MPa. The water generated by the reaction was discharged through a rectification device. The esterification time was 180 min. After the esterification was completed, catalyst A ...

Embodiment 2

[0029] The preparation of titanium series polyester catalyst B:

[0030] Add 68 g (0.2 mol) of tetrabutyl titanate and 124 g (2 mol) of ethylene glycol into a reactor equipped with a distillation device, mix well and stir for 5 minutes. Heating to 160°C under the protection of nitrogen produced a white solid. After reacting for 9 h, a total of 58 g of n-butanol was distilled out. Then add 72.8 g (0.4 mol) of triethyl phosphate, heat to 180° C. and react for 5 hours, and finally obtain milky white titanium-based polyester catalyst B.

[0031] Preparation of copolyester:

[0032] 20 kg of terephthalic acid, 7.47 kg of ethylene glycol, and 8.67 kg of 1,4-cyclohexanedimethanol were made into a slurry and put into a reaction kettle for esterification reaction. The esterification temperature was 260°C and the pressure was 0.45Mpa. The water generated by the reaction was discharged through a rectification device. The esterification time was 140 min. After the esterification was com...

Embodiment 3

[0034] Preparation of Titanium-based Polyester Catalyst C

[0035] Add 46 g (0.2 mol) of tetraethyl titanate and 248 g (4 mol) of ethylene glycol into a reaction kettle equipped with a distillation device, mix well and stir for 5 minutes. Heated to 90°C under the protection of nitrogen to produce a white solid. After reacting for 9 h, 36 g of ethanol was distilled out. Then add 326 g (1 mole) of triphenyl phosphate, heat to 160° C. and react for 10 hours to finally obtain milky white titanium-based polyester catalyst C.

[0036] Preparation of copolyester

[0037] Put 20 kilograms of terephthalic acid, 7.8 kilograms of ethylene glycol, 5 kilograms of 1,4-cyclohexanedimethanol and 2.8 kilograms of isosorbide into a slurry and put them into the reaction kettle for esterification reaction. The esterification temperature is 245 ℃, the pressure is 0.35Mpa. The water generated by the reaction was discharged through a rectification device. The esterification time was 160 min. Afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed are a titanium-based catalyst for polyesters and a method for producing a copolyester thereby. The catalyst is obtained by the reaction of titanate, ethylene glycol and phosphate, and polyester chips are produced by utilizing the catalyst, wherein same have a chip intrinsic viscosity of 0.75-0.81 dl / g and a b value between 1 and 3.5. Copolyester products obtained by the present invention have a neutral tone, a high intrinsic viscosity and a good transparency, and same can be widely used in markets such as panels, sheets, high-performance thermal shrinkage films, and bottles.

Description

technical field [0001] The invention relates to a titanium series polyester catalyst and a method for producing copolyester by using the catalyst. Background technique [0002] Copolyester refers to the modification of polyethylene terephthalate (PET) with modified diols. After these modified diols are introduced into the PET macromolecular chain, the original structure of PET can be made It is changed to reduce the crystallization ability of PET and improve the flexibility of macromolecular chains. The modified copolyester has the characteristics of high transparency, good toughness and good heat shrinkability. It can be widely used in fields such as sheets, cosmetic bottles, heat shrinkable films, etc., and has a good market prospect. [0003] Generally, the commonly used catalysts for copolyester synthesis are: antimony, germanium, titanium, etc., among which antimony is a heavy metal catalyst, which has safety problems. In the production of food containers that are rel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/85C08G63/87C08G63/183C08G63/199C08G63/42
CPCC08G63/183C08G63/199C08G63/42C08G63/85C08G63/87
Inventor 吴培龙吴迪陆银秋
Owner JIANGSU JINGHONG NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com