Application of modified calcium carbonate in quartz stone plates

A quartz stone plate and calcium carbonate technology, which is applied in the application field of modified calcium carbonate in quartz stone plate, can solve the problems of poor compatibility and poor dispersion of quartz stone plate, and achieve improved mechanical properties and good dispersion , good modification effect

Inactive Publication Date: 2018-01-12
贺州钟山县双文碳酸钙新材料有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a modified calcium carbonate and its preparation method to solve the existing problems of calcium carbonate such as hydrophilic and oleophobic, poor dispersibility, poor compatibility with quartz stone plates, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of modified calcium carbonate in quartz stone plates
  • Application of modified calcium carbonate in quartz stone plates

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of described modified calcium carbonate, comprises the following steps:

[0037] S1: Select marble, limestone, etc. transported from the material field to clean and remove impurities, dry the stone to remove surface moisture, and then use a crusher to crush the stone to obtain calcium carbonate fragments;

[0038] S2: transporting the broken calcium carbonate obtained in step S1 into a vertical mill and synchronously adding grinding aids and grinding to obtain calcium carbonate fine stone powder;

[0039] S3: classifying the calcium carbonate fine stone powder prepared in step S2 with a classifier to obtain calcium carbonate powder of 400-600 mesh;

[0040] S4: Add the calcium carbonate powder obtained in step S3 into a high-speed mixer, then add sodium dioctyl succinic acid sulfonate, stannous chloride, and magnesium oxide, raise the temperature to 92-103°C, and heat at 1100-1300r / Stir at a high speed of 24-28min at a speed of 24-28min to prepa...

Embodiment 1

[0045] An application of modified calcium carbonate in quartz stone plates, wherein the quartz stone plates, in parts by weight, include the following raw materials: 30 parts of modified calcium carbonate, 15 parts of methylphenyl silicone resin prepolymer, 40 parts of inorganic silicon fillers, 20 parts of additives;

[0046] The modified calcium carbonate, in parts by weight, includes the following raw materials: 156 parts of calcium carbonate crushed matter, 4.5 parts of grinding aid, 4 parts of dioctyl sodium sulfosuccinate, 0.5 part of tin protochloride, magnesium oxide 0.1 part, 0.7 part of sodium diethylenetriaminepentacarboxylate, 0.1 part of acrylate regulator, 0.5 part of 3-aminopropyltriethoxysilane, 1.8 part of bis(2-ethylhexyl) phthalate , 0.4 parts of modified polyacrylate, 0.3 parts of hexenylbisstearamide, 0.4 parts of 2-(2'-hydroxy-3',5'-di-tert-phenyl)-5-chlorinated benzotriazole, 0.1 part of polyacrylamide, 0.5 part of calcium soap stabilizer;

[0047] The...

Embodiment 2

[0059] An application of modified calcium carbonate in quartz stone slabs, the quartz stone slabs, in parts by weight, include the following raw materials: 26 parts of modified calcium carbonate, 8 parts of methylphenyl silicone resin prepolymer, 35 parts of inorganic silicon fillers, 10 parts of additives;

[0060] The modified calcium carbonate, in parts by weight, includes the following raw materials: 143 parts of calcium carbonate crushed matter, 3.6 parts of grinding aid, 3.2 parts of dioctyl sodium sulfosuccinate, 0.3 part of stannous chloride, magnesium oxide 0.1 part, 0.5 part of sodium diethylenetriaminepentacarboxylate, 0.1 part of acrylate regulator, 0.4 part of 3-aminopropyltriethoxysilane, 1.2 part of bis(2-ethylhexyl) phthalate , 0.3 parts of modified polyacrylate, 0.2 parts of hexenylbisstearamide, 0.2 parts of 2-(2'-hydroxy-3',5'-di-tert-phenyl)-5-chlorinated benzotriazole, 0.1 part of polyacrylamide, 0.3 part of calcium soap stabilizer;

[0061] The inorgani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses an application of modified calcium carbonate in quartz stone plates. A quartz stone plate comprises the following raw materials in parts by weight: 25-36 parts of modified calcium carbonate, 8-20 parts of a methyl phenyl silicone resin prepolymer, 32-45 parts of an inorganic silicon filler and 10-30 parts of an auxiliary agent. The quartz stone plate is prepared by compression moulding by using the modified calcium carbonate, the methyl phenyl silicone resin prepolymer, the inorganic silicon filler and the auxiliary agent in a corresponding proportion. The modified calcium carbonate is added into the quartz stone plate, has small probability of agglomeration phenomenon, and has good dispersibility, and the various mechanical properties of the modified calcium carbonate are increased notably.

Description

【Technical field】 [0001] The invention belongs to the technical field of preparation of quartz stone plates, and in particular relates to the application of modified calcium carbonate in quartz stone plates. 【Background technique】 [0002] As the latest artificial building material, artificial quartz stone has incomparable advantages of natural stone such as high strength, high hardness, high temperature resistance, corrosion resistance, anti-aging, easy cleaning, wear resistance, pure material, and no radiation. Today, as natural stone is being exhausted as a non-renewable resource, artificial quartz stone is the best substitute. At the same time, artificial quartz stone can use waste glass as raw material, thus realizing resource reuse while protecting the environment. These advantages make Artificial quartz stone has become an upstart in the architectural decoration industry, and is widely used in cabinets, bathrooms, floors and wall decorations in offices and large shopp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32C04B14/28C04B20/04C04B20/02
Inventor 唐文易双
Owner 贺州钟山县双文碳酸钙新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap