A kind of modified calcium carbonate with enhanced wear resistance and preparation method thereof

A technology of calcium carbonate and wear resistance, which is applied in the field of modified calcium carbonate and its preparation, can solve the problems such as the narrowing of the temperature window of nano calcium carbonate, defects, cracks, etc., to increase the dispersion performance and compatibility performance, reduce the external The effect of friction and strong binding force

Active Publication Date: 2016-03-30
浙江环星纳米科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of dispersants and surface modifiers greatly reduces the temperature window of nano-calcium carbonate, because commonly used dispersants and coupling agents are easy to decompose at high temperatures, causing bubbles, cracks, defects, deformation, etc., thus Affect the appearance, heat resistance and mechanical properties of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified calcium carbonate with enhanced wear resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A modified calcium carbonate with enhanced wear resistance is prepared from the following raw materials in parts by weight (kg): calcium carbonate 85, quartz powder 2, epoxy resin 5, glycerol triacetate 4, nylon 666, molybdenum disulfide 3. Copper oxide 2, crushed nut shell 2, high wear-resistant carbon black 1, brown corundum 2, turpentine 4, liquid paraffin 2, modified titanium dioxide 3;

[0016] The modified titanium dioxide is made of the following raw materials in parts by weight (kg): aluminum hydroxide 2, nano titanium dioxide 50, silicon carbide 4, methyl methacrylate 5, antimony trioxide 3, terephthalic acid 3, horse Dioctyl maleate 3, ethylene glycol 5, water 50; the preparation method is to first add methyl methacrylate, nano-titanium dioxide, aluminum hydroxide, ethylene glycol, and water and stir evenly to form a suspension. D...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A modified calcium carbonate with enhanced wear resistance is disclosed. The modified calcium carbonate is characterized in that: the modified calcium carbonate is prepared from raw materials 85-90 parts by weight of calcium carbonate, 2-3 parts by weight of quartz powder, 5-7 parts by weight of epoxy resin, 4-6 parts by weight of glycerol triacetate, 6-8 parts by weight of nylon 66, 3-4 parts by weight of molybdenum disulfide, 2-3 parts by weight of copper oxide, 2-3 parts by weight of smashed nut shell, 1-1.5 parts by weight of high-wear-resistance carbon black, 2-3 parts by weight of brown aluminium oxide, 4-6 parts by weight of turpentine, 2-4 parts by weight of liquid paraffin and 3-4 parts by weight of modified titanium dioxide; by addition of the high-wear-resistance carbon black, the molybdenum disulfide and other wear-resistant lubricants, a filling material has a self-lubricating property so as to reduce external friction, thus achieving an effect of wear resistance; and by adoption of the modified titanium dioxide, the dispersion property and the compatibility are enhanced, thus generating strong binding force and not reducing the comprehensive properties of products. The modified calcium carbonate is used as additives for plastics, rubber and coating, and the like.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a modified calcium carbonate with enhanced wear resistance and a preparation method thereof. Background technique [0002] Calcium carbonate is a very important functional inorganic filler, which is widely used in industrial fields such as plastics, rubber, coatings and papermaking. In the application field of calcium carbonate, most products belong to the category of polymers, such as plastics, rubber, adhesives, coatings, etc., and occupy an important market share. [0003] Modifiers play an important role in the performance and application of nano calcium carbonate. For example, the addition of dispersant can reduce the agglomeration of nanoparticles and improve the dispersion; the addition of surface modifier can improve the compatibility of nano-calcium carbonate in the polymer system. It can be seen that dispersants and surface modifiers are crucial for the application o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/02C09C3/06C09C3/10C09C3/08C09C3/00
Inventor 王俊华朱传路
Owner 浙江环星纳米科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap