A method for regulating the surface wettability of pa2200 material 3D printing parts by laser irradiation

A technology of PA2200 and laser irradiation, which is applied to 3D object support structures, additive processing, metal processing equipment, etc., can solve the problems of easy peeling off of coatings, pollution of molded parts, and has not yet appeared, so as to achieve simple and controllable processes high effect

Inactive Publication Date: 2019-05-17
BEIJING UNIV OF TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The plasma method can effectively regulate the surface wettability of PA-based moldings, but it affects the surface functionalization of moldings
[0005] 2. Surface coating modification method: use physical methods to prepare a cross-linked hydrophilic coating on the surface of PA-type material moldings, which can effectively control the surface wettability of PA-type material moldings, but the coating is easy to fall off
[0006] 3. The method of introducing functional groups: introducing specific functional groups for the amide bonds in PA materials to control the surface wettability of molded parts, which can effectively control the surface wettability of PA materials molded parts, but it pollutes the surface of molded parts , and the change of the wettability of the surface of the molded part cannot last for a long time
[0007] 4. Laser irradiation method: In recent years, various lasers have been used to irradiate the surface of PA-type molded parts, which can effectively control the surface wettability of PA-type material molded parts. Compared with other methods, laser irradiation method has the advantages of It can accurately treat the surface of molded parts, control the processing area and depth, non-contact, pollution-free, and not introduce impurity ions, etc., but there is no report on the surface wettability of 3D printed molded parts controlled by laser irradiation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for regulating the surface wettability of pa2200 material 3D printing parts by laser irradiation
  • A method for regulating the surface wettability of pa2200 material 3D printing parts by laser irradiation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Below in conjunction with accompanying drawing, specific embodiment of the present invention is described in further detail:

[0024] The first step: use SLS technology to prepare 3D printed parts of PA2200 material

[0025] This step is to prepare 3D prints of PA2200 materials. The specific process is divided into data preparation, printing, and subsequent cleaning:

[0026] 1) Data preparation: Use the magics software to prepare the model in STL format. After the model is ready, use the RP Tools slicing software to slice the model. After slicing, import it into the PSW software and save it as an eosjz file, and then import this file into the 3D printer EOS P396 machine PSW software and load this file, the data preparation process is completed;

[0027] 2) Printing: Before printing, the printer needs to pre-spread 9mm of powder and preheat for 2 hours. After the preheating is completed, it can be printed. During the printing process, the printer prints layer by layer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for regulating surface wettability of a 3D printing piece made of a PA2200 material by laser irradiation, and belongs to the field of laser processing, 3D printing technologies and medical application. A laser irradiation method has the advantages that the surface of a molded piece can be accurately processed, the processing area and depth are controlled, pollutionis avoided due to non-contact, and impurity ions cannot be introduced. The method is implemented by means of the following device: a laser, a compound eye beam homogenizing lens, a lens and a sampletable are placed in sequence along the laser transmission direction of the laser. The 3D printing piece is prepared from the PA2200 material, an optical path is designed by adopting KrF excimer laserof which the wavelength is 248nm, so as to obtain a laser irradiation light spot area 1 to 2.7cm<2>, the single pulse energy density of the laser is set as 37 to 259mJ / cm<2>, the frequency is 2 to 5Hz, the pulse number is 200 to 500, and the 3D printing piece made of the PA2200 material is irradiated. After laser irradiation, the surface contact angle of the printing piece is changed from 120 degrees to 70 degrees, hydrophily is changed from hydrophobicity, and the surface wettability of the 3D printing piece made of the PA2200 material can be effectively and rapidly regulated.

Description

technical field [0001] The invention relates to the fields of laser processing, 3D printing technology and medical applications, and in particular designs a method for regulating the surface wettability of 3D printed parts of PA2200 material by laser irradiation. Background technique [0002] PA2200 is a polymer material, composed of pure PA12, white in color, with good mechanical properties and biocompatibility. At present, PA2200 materials are used in laser selective sintering (SLS) 3D printing technology. PA2200 printed parts based on this technology have a wide range of applications in the medical field, including medical devices: biological scaffolds, sutures, syringes, dialysis equipment components and Implants: balloon catheters, vascular grafts, hard tissue implants, etc. Selective laser sintering (SLS) is a powder-spreading 3D printing layered forming technology. It has the characteristics of high manufacturing precision, fast printing speed, and the ability to cus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C71/04B29C71/00B29C64/379B33Y40/00
Inventor 蒋毅坚魏小波曾勇闫胤洲赵艳
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products