A kind of preparation method of cinnabar relief painting

A technique of cinnabar and embossing, which is applied in the special technique of art painting and decorative art, etc., which can solve the problems affecting the touch and appearance of products, rough relief painting surface, unsatisfactory hardness, etc., and achieve obvious layering, bright and uniform color, and hardness Improved effect

Inactive Publication Date: 2020-03-31
贵州筑信达创科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cinnabar has the reputation of "soft ruby". At present, it is not uncommon for cinnabar to be used in the production of relief paintings. The surface of most cinnabar relief paintings is relatively rough, and there are tiny air bubbles, which seriously affect the touch and appearance of the product, and its hardness is not ideal. , easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of preparation method of cinnabar relief painting is characterized in that, comprises the following steps:

[0019] (1) Raw material preparation: use cinnabar, ocher and earth red, mix them and put them into a pulverizer for 10 minutes, pass through a 200-mesh sieve, put them into a high-speed mixer and stir for 5 minutes, and control the temperature at 40°C and humidity during the stirring process 65%, and add 30% of its weight epoxy resin;

[0020] (2) Relief model treatment: use purified water to wash and soak for 20 minutes, the soaking temperature is 30°C, take out the model after soaking, use ultrasonic cleaning for 3 minutes, and dry the moisture on the surface;

[0021] (3) Drying: Pour the raw materials into a mold, dry in a closed environment at a temperature of 40°C for 2 hours, and then cool at room temperature.

[0022] The cinnabar, ocher and earth red are mixed according to the weight ratio of 20:1:0.1.

[0023] The cinnabar, ocher and earth red ...

Embodiment 2

[0028] A kind of preparation method of cinnabar relief painting is characterized in that, comprises the following steps:

[0029] (1) Raw material preparation: use cinnabar, ocher and earth red, mix them and put them into a pulverizer for 20 minutes, pass through a 300-mesh sieve, then put them into a high-speed mixer and stir for 10 minutes, and control the temperature at 50°C and humidity during the stirring process 75%, and add 50% of its weight epoxy resin;

[0030] (2) Relief model treatment: use purified water to wash and soak for 30 minutes, the soaking temperature is 40°C, take out the model after soaking, use ultrasonic cleaning for 5 minutes, and dry the moisture on the surface;

[0031] (3) Drying: Pour the raw materials into a mold, dry in a closed environment at a temperature of 45°C for 3 hours, and then cool at room temperature.

[0032] The cinnabar, ocher and earth red are mixed according to the weight ratio of 20:3:0.5.

[0033] The cinnabar, ocher and eart...

Embodiment 3

[0038] A kind of preparation method of cinnabar relief painting is characterized in that, comprises the following steps:

[0039] (1) Raw material preparation: use cinnabar, ochre and earth red, mix them and put them into a pulverizer for 15 minutes, pass through a 240-mesh sieve, put them into a high-speed mixer and stir them for 8 minutes, and control the temperature at 45°C and humidity during the stirring process 70%, and add 35% of its weight epoxy resin;

[0040] (2) Relief model treatment: use purified water to wash and soak for 25 minutes, the soaking temperature is 35°C, take out the model after soaking, use ultrasonic cleaning for 5 minutes, and dry the moisture on the surface;

[0041] (3) Drying: Pour the raw materials into a mold, dry in a closed environment at a temperature of 43°C for 2.5 hours, and then cool at room temperature.

[0042] The cinnabar, ocher and earth red are mixed according to the weight ratio of 20:1:0.4.

[0043] The cinnabar, ocher and ear...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of cinnabar artware, and particularly relates to a method for preparing a cinnabar relief painting. Cinnabar, ochre and terra rossa are mixed and smashed,a proper amount of epoxy resin is added, and raw materials of relief are prepared; and the raw materials are placed in a specially cleaned relief painting mould, and the cinnabar relief painting is prepared through drying. Especially, the matching design of the raw materials is combined with proper regulation and control on technological parameters, so that the color and luster of the cinnabar painting are bright and even, the cinnabar relief painting is glossy and obvious in sense of depth, and has eastern classical charm, the hardness of the cinnabar relief painting is greatly improved, andthe cinnabar relief painting is not likely to be damaged.

Description

technical field [0001] The invention belongs to the technical field of cinnabar handicrafts, in particular to a method for preparing cinnabar relief paintings. Background technique [0002] Cinnabar, formerly known as "cinnabar", is the main raw material for mercury refining, also known as "mercury sand"; because of its red color, it is commonly known as "cinnabar", "dan chestnut", "red dan" and "cinnabar stone"; its chemical composition Mercury sulfide is a trigonal crystal system, the crystals are plate-like or soil-like, and the crystal clusters are often diamond-shaped twin crystals, large-grained single crystals, translucent or opaque, bright red, vermilion, light red, dark red or red, brittle, and brittle to Light-sensitive, high refractive index, hardness 2-2.5, specific gravity 8.09-8.2, weight, brittle, easily broken in flake form, shimmering luster in powder form, and tasteless. Cinnabar has the reputation of "soft ruby". At present, it is not uncommon for cinnaba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44D2/00
CPCB44D2/005
Inventor 周建中王志进
Owner 贵州筑信达创科技有限公司