Processing technology for improving transparency of plastic cup

A processing technology, plastic cup technology, applied in the direction of biochemical fiber processing, textile and paper making, fiber processing, etc., can solve the problems of complex production process, short service life, general transparency, etc., achieve excellent physical properties, long service life, processing The process is simple and controllable

Inactive Publication Date: 2019-03-15
嘉兴松尚电器有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the plastic cup products currently on the market have average transparency, generally poor toughness, short service life, complicated production process, and serious environmental pollution, thus increasing the cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A plastic cup, the plastic cup is mainly made of the following raw materials in parts by weight: 70 parts of high-density polypropylene particles, 1 part of anti-aging agent MB, 2 parts of transparent agent xylene, 2 parts of curing agent diethylenetriamine, ramie fiber 30 parts, 4 parts of nano calcium carbonate;

[0037] The high-density polypropylene particles are mainly prepared from the following raw materials in parts by weight: 30 parts of polypropylene, 10 parts of nano-silica gel, 15 parts of titanium carbide, 5 parts of thermoplastic polyester elastomer, 10 parts of modified phenolic resin, stearin Calcium acid 5 parts, antioxidant 1010 dosage 2 parts, vinyl silicone oil 3 parts.

[0038] The above-mentioned processing technology for improving the transparency of plastic cups comprises the following steps:

[0039] (1) Preparation of high-density polypropylene particles

[0040] a. Pretreatment of raw materials: adding polypropylene, nano-silica gel, titaniu...

Embodiment 2

[0053] A plastic cup, the plastic cup is mainly made of the following raw materials in parts by weight: 80 parts of high-density polypropylene particles, 3 parts of anti-aging agent MB, 6 parts of transparent agent xylene, 6 parts of curing agent triethylenetetramine, ramie fiber 35 parts, 6 parts of nano calcium carbonate;

[0054] The high-density polypropylene particles are mainly prepared from the following raw materials in parts by weight: 40 parts of polypropylene, 20 parts of nano-silica gel, 25 parts of titanium carbide, 7 parts of thermoplastic polyester elastomer, 15 parts of modified phenolic resin, stearic acid 7 parts of calcium, 4 parts of antioxidant 1076, 8 parts of vinyl silicone oil;

[0055] The above-mentioned processing technology for improving the transparency of plastic cups comprises the following steps:

[0056] (1) Preparation of high-density polypropylene particles

[0057] a. Pretreatment of raw materials: adding polypropylene, nano-silica gel, ti...

Embodiment 3

[0070] A plastic cup, the plastic cup is mainly made of the following raw materials in parts by weight: 90 parts of high-density polypropylene particles, 5 parts of antioxidant MB, 10 parts of transparent agent chloroform, 10 parts of curing agent dipropylenetriamine, 40 parts of ramie fiber Parts, 8 parts of nano calcium carbonate;

[0071] The high-density polypropylene particles are mainly prepared from the following raw materials in parts by weight: 50 parts of polypropylene, 30 parts of nano-silica gel, 40 parts of titanium carbide, 10 parts of thermoplastic polyester elastomer, 20 parts of modified phenolic resin, stearic acid 10 parts of calcium, 6 parts of antioxidant 168, 15 parts of vinyl silicone oil;

[0072] The above-mentioned processing technology for improving the transparency of plastic cups comprises the following steps:

[0073] (1) Preparation of high-density polypropylene particles

[0074] a. Pretreatment of raw materials: adding polypropylene, nano-sil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a processing technology for improving the transparency of a plastic cup, and belongs to the technical field of production and manufacturing of plastics. According to the plastic cup, high-density polypropylene particles are used as a base material, an anti-aging agent, a transparent agent, a curing agent, ramie fibers and nano calcium carbonate are used as auxiliary materials, wherein the high-density polypropylene particles used as the base material are prepared from raw materials including polypropylene, isopropanol, titanium carbide, nano silica gel, thermoplastic polyester elastomers, modified phenolic resin, calcium stearate, deionized water and an antioxidant; and the preparation process of the plastic cup comprises the following steps: weighing of raw materials, drying of the raw materials, antibacterial treatment of fibers, mixing of the raw materials, injection molding and aftertreatment. The processing technology of the plastic cup is simple and controllable in process, low in cost and low in pollution, conforms to the idea of sustainable development and is worthy of being popularized; and the produced plastic cup has high mechanical strength, andis fine and smooth in texture, high in transparency and long in service life.

Description

technical field [0001] The invention relates to the technical field of plastic production, in particular to a processing technology for improving the transparency of plastic cups. Background technique [0002] Plastic cups are commonly used utensils for drinking water in people's lives. Based on their light texture, beautiful appearance, low cost and strong plasticity, they are deeply loved by people. [0003] Not only that, plastic cups also have the advantages of saving time and effort in processing and changing shapes, and have developed rapidly in recent years. However, the plastic cup products currently on the market have general transparency, poor toughness, short service life, complicated manufacturing process, and serious environmental pollution, which increases the cost. Contents of the invention [0004] Aiming at the defects existing in the prior art, the object of the present invention is to provide a processing technology for improving the transparency of pla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L1/02C08K13/02C08K3/26C08K3/36C08K3/14C08K5/098D06M13/50D06M101/06
CPCC08L23/12C08K2003/265C08K2201/011C08L2201/08C08L2205/035C08L2205/16C08L2207/04D06M13/50D06M16/00D06M2101/06C08L1/02C08K13/02C08K3/26C08K3/36C08K3/14C08K5/098
Inventor 董和英
Owner 嘉兴松尚电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap