Antibacterial cotton clothes fabric and preparation method thereof

An antibacterial fabric, cotton-padded technology, applied in chemical instruments and methods, fabric surface trimming, textile material treatment, etc., can solve the problems of gentle washing, fear of insect bites, like fading, etc., to achieve soft hand feel and avoid discomfort. Sensation, the effect of improving drape

Inactive Publication Date: 2018-04-06
TIANCHANG EARTHQUAKE OFFICE
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Disadvantages, it is very easy to wrinkle, and it likes to fade, the washing must be gentle, it is also easy to embrittle, and it is also very afraid of insect bites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial cotton clothes fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An antibacterial fabric for cotton clothes is formed by laminating two layers of blended yarn fabrics through an antibacterial coating coated on the surface of the blended yarn fabrics.

[0029] The blended yarn fabric is made of cotton fiber, hemp fiber, nylon fiber and viscose fiber blended, wherein the weight fraction ratio of superfine polyester fiber is 45%, the weight fraction ratio of cotton fiber is 15%, milk fiber The weight fraction ratio of cupro ammonia fiber is 25%, and the weight fraction ratio of cupro ammonia fiber is 15%.

[0030] The antibacterial coating is formed by coating the blended yarn fabric with an antibacterial coating agent and drying. The antibacterial coating agent includes the following components by weight fraction: tea extract, loquat leaf extract, aloe extract, Pomegranate Peel Extract

[0031] Tea Extract 10%

[0032] Loquat Leaf Extract 15%

[0033] Aloe Vera Extract 25%

[0034] Pomegranate Peel Extract 5%

[0035] The solid co...

Embodiment 2

[0047] An antibacterial fabric for cotton clothes is formed by laminating two layers of blended yarn fabrics through an antibacterial coating coated on the surface of the blended yarn fabrics.

[0048] The blended yarn fabric is made by blending cotton fiber, hemp fiber, nylon fiber and viscose fiber, wherein the weight fraction ratio of cotton fiber is 35-45%, and the weight fraction ratio of hemp fiber is 10-25%, The weight fraction ratio of hemp fiber is 35-45%, and the weight fraction ratio of viscose fiber is 10-25%.

[0049] The antibacterial coating is formed by coating the antibacterial coating agent on the blended yarn fabric and drying.

[0050] The antibacterial coating agent comprises the following components in weight fraction ratio:

[0051] Tea Extract 10%

[0052] Loquat Leaf Extract 15%

[0053] Aloe Vera Extract 25%

[0054] Pomegranate Peel Extract 5%

[0055] The solid content of described antibacterial coating agent is 30%, and viscosity is 1600.

[...

Embodiment 3

[0067] An antibacterial fabric for cotton clothes is formed by laminating two layers of blended yarn fabrics through an antibacterial coating coated on the surface of the blended yarn fabrics.

[0068] The blended yarn fabric is made of cotton fiber, hemp fiber, nylon fiber and viscose fiber blended, wherein the weight fraction ratio of superfine polyester fiber is 50%, the weight fraction ratio of cotton fiber is 15%, milk fiber The weight fraction ratio of cupro ammonia fiber is 25%, and the weight fraction ratio of cupro ammonia fiber is 10%.

[0069] The antibacterial coating is formed by coating the blended yarn fabric with an antibacterial coating agent, and the antibacterial coating agent includes the following components by weight fraction:

[0070] Tea Extract 10%

[0071] Loquat Leaf Extract 15%

[0072] Aloe Vera Extract 25%

[0073] Pomegranate Peel Extract 5%

[0074] The solid content of the antibacterial coating agent is 35.5%, and the viscosity is 1500.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial cotton clothes fabric which is prepared by laminating two layers of blended yarn fabrics by virtue of an antibacterial coating applied to the surface of the blended yarn fabrics. The blended yarn fabrics are made from cotton fibers, jute fibers, polyamide fibers and viscose acetal fibers, and have excellent applicability. Meanwhile, the two layers of blended yarns are adhered together by creatively adopting the natural antibacterial coating for a technology for adhering pressure-sensitive adhesives, bacteria breeding of cotton clothes is inhibited, andexcellent environment-friendly, antibacterial and odor resistance effects are achieved.

Description

technical field [0001] The invention relates to a fabric, which belongs to the field of textiles, in particular to an antibacterial cotton fabric and a preparation method thereof. Background technique [0002] Cotton clothes are generally made of blended fabrics. Why blend it? In layman's terms, because the properties of the fabrics themselves are different, the effect of blending not only reduces the cost, but also improves the performance of the fabrics and maximizes the strengths and avoids weaknesses. For example, polyester is wear-resistant, heat-resistant, corrosion-resistant and light-resistant, which means that it is not easy to wrinkle, not torn, not easy to fade. Nor does it shrink. But the disadvantage is that it is not breathable, it is not good for the skin, and it has static electricity. Pure cotton has the advantages of moisture absorption, moisturizing, heat resistance and hygiene. It is good for the skin, not easy to generate static electricity, can kee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02B32B23/02B32B27/02B32B27/34B32B7/12D03D15/00D06B3/10D06C7/02D06M13/00D06M15/00D06M15/11D06M16/00D06M101/04D06M101/06D06M101/34D03D15/217D03D15/225D03D15/283D03D15/47
CPCD03D15/00D06B3/10D06C7/02D06M13/00D06M15/00D06M15/11D06M16/00B32B5/024B32B5/08B32B5/26B32B7/12B32B9/02B32B9/047D06M2101/34D06M2101/04D06M2101/06D10B2331/02D10B2201/02D10B2201/01D10B2201/24B32B2262/04B32B2262/0261B32B2262/065B32B2262/062
Inventor 不公告发明人
Owner TIANCHANG EARTHQUAKE OFFICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap