Waterborne one-component negative oxygen ion white paint for wood ware and preparation method of white paint

A negative oxygen ion, one-component technology, applied in the field of wood white paint, can solve the problem of not being able to release negative oxygen ions, etc., and achieve the effect of excellent scratch resistance, high hardness, and easy construction

Inactive Publication Date: 2018-06-29
吕跃文
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing wood white paints cannot release negative oxygen ions, even if a small part can release negative oxygen ions, the amount released is very small, usually only 0-50 / cm 3 , cannot meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne one-component negative oxygen ion white paint for wood ware and preparation method of white paint
  • Waterborne one-component negative oxygen ion white paint for wood ware and preparation method of white paint
  • Waterborne one-component negative oxygen ion white paint for wood ware and preparation method of white paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Present embodiment provides a kind of water-based one-component negative oxygen ion woodware white paint, and it is made up of following components by weight percentage:

[0030]

[0031] Wherein, the sum of the weight percentages of the above components is 100%.

[0032] Preferably, in this embodiment, the negative oxygen ion additive can adopt H003 type negative oxygen ion additive, T22 type negative oxygen ion additive, TK113 type negative oxygen ion additive, NP01 type negative oxygen ion additive and 30000 type negative oxygen ion additive one or several.

[0033] The preparation method of the water-based one-component negative oxygen ion woodware white paint of the present embodiment is as follows:

[0034] (1) Add 5% to 10% pure water by weight, 0.2% to 0.3% leveling agent by weight, and 0.2% to 0.5 % defoamer and 1% to 2% negative oxygen ion additive by weight;

[0035] (2) After the pure water, leveling agent, defoamer and negative oxygen ion additives in...

Embodiment 2

[0041] The water-based one-component negative oxygen ion woodware white paint of the present embodiment is by the water-based acrylic acid dispersion of 60wt%, the pure water of 6.3wt%, the leveling agent of 0.2wt%, the negative oxygen ion additive of 1wt%, 0.3wt% Defoamer, 8wt% coalescent, 0.2wt% pH adjuster, 20wt% titanium dioxide, 2wt% wax / dumb powder, 2wt% thickener.

[0042] Preferably, in this embodiment, the water-based acrylic dispersion can be imported from the United States; the pure water can be self-made pure water; the leveling agent can be BYK-346 leveling agent; the negative oxygen ion additive can be Hutt International H003 type negative oxygen ion additive; defoamer can use BYK-023 defoamer; film-forming aid can use Dowanol DPM film-forming aid; The white powder can be DuPont R706 titanium dioxide; the thickener can be Viscalex LO 30 thickener from BASF.

[0043] The preparation method of the water-based one-component negative oxygen ion woodware white paint ...

Embodiment 3

[0051] Compared with embodiment 2, the difference of the water-based one-component negative oxygen ion wood white paint of the present embodiment is that the negative oxygen ion additive adopted is different. What present embodiment adopted is that the weight percent is the T22 type negative oxygen ion additive of Beijing Tianzhiyan Health Technology Co., Ltd. of 1%; All the other components and weight percent are identical with embodiment 2.

[0052] The preparation method of the water-based one-component negative oxygen ion wood white paint of the present embodiment is the same as that of Example 2.

[0053] The various test parameters of the water-based one-component negative oxygen ion wood white paint product of the present embodiment are as shown in table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses waterborne one-component negative oxygen ion white paint for wood ware and a preparation method of the white paint. The waterborne one-component negative oxygen ion white paintfor wood ware is prepared from components in percentage by weight as follows: 55%-65% of waterborne acrylic dispersoid, 5%-10% of pure water, 0.2%-0.3% of a leveling agent, 1%-2% of a negative oxygenion additive, 0.2%-0.5% of a defoaming agent, 5%-10% of a coalescing agent, 0.1%-0.3% of a pH regulator, 15%-25% of titanium dioxide, 1%-3% of wax powder or matt powder and 2%-3% of a thickener, wherein the sum of weight percentages of all the components is 100%.

Description

technical field [0001] The present invention relates to a kind of wood white paint, specifically relate to a kind of water-based one-component negative oxygen ion wood white paint and preparation method thereof. Background technique [0002] The level of negative oxygen ion concentration is closely related to people's health, and people need negative oxygen ions all the time, especially in today's increasingly serious pollution. According to research by environmental scientists, when the concentration of negative oxygen ions in the air is below 20 per cubic centimeter, people will feel tired and dizzy; when the number of negative oxygen ions in the air per cubic centimeter is between 1,000 and 10,000 When the number of negative oxygen ions in the air per cubic centimeter is more than 10,000, people will feel refreshed, comfortable and comfortable; and when the negative oxygen ions in the air per cubic centimeter When the number of ions is as high as 100,000 or more, it can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/18C09D7/61
Inventor 吕跃文
Owner 吕跃文
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com