Concrete corrosion-resistant preservative and application thereof

A kind of preservative and concrete technology, applied in concrete corrosion-resistant preservative and its application field, to achieve good wear resistance, good anti-salt spray, and solve the effect of pollution

Active Publication Date: 2018-07-06
CENT RES INST OF BUILDING & CONSTR CO LTD MCC GRP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to make full use of colored tailings slag resources, extract active ingredients therefrom, make a concrete corrosion-resistant and anti-corrosion agent, and add it to concrete to improve the performance of concrete and improve the use effect of concrete structures. At the same time Turn waste into wealth and reduce environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete corrosion-resistant preservative and application thereof
  • Concrete corrosion-resistant preservative and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This example provides a concrete corrosion-resistant anti-corrosion agent and its preparation method. The colored tailings slag extract is extracted from the tailings slag of a non-ferrous metal mine in Gansu by chemical leaching, and the extract includes amorphous dioxide Silicon, calcium oxide, aluminum oxide and rare metal oxides, the weight ratio of each component in the extract is: amorphous silicon dioxide 70%, calcium oxide 10%, aluminum oxide 8%, rare metal Oxide 8%, other balance.

[0017] The above-mentioned colored tailings slag extract is crushed to form a mixture of ultrafine particles with a particle size of 5-30 nm, and the concrete corrosion-resistant and anti-corrosion agent of the present invention is obtained.

[0018] The shelf life of the material is half a year, and it should be stored in a cool, ventilated, dry place, protected from the sun and rain, and the storage temperature is 5~35°C.

Embodiment 2

[0020] The concrete anti-corrosion and anti-corrosion agent obtained in Example 1 is added to the concrete by external mixing, the ratio of admixture is based on the cement in the concrete, and 1 part of cement is mixed with 5-10% of the concrete anti-corrosion and anti-corrosion agent of the present invention to make the anti-corrosion and anti-corrosion The agent is evenly dispersed in the concrete; after hydration reaction with ordinary Portland cement, an inorganic composite compact body is formed. After testing, the performance index of concrete adding the corrosion-resistant and anti-corrosion agent of the present invention is as follows:

[0021]

[0022] The concrete can be applied to anticorrosion, waterproof, anti-seepage, anti-carbonation, etc. of reinforced concrete structures such as marine engineering, port terminals, bridges and tunnels, coastal engineering, water conservancy and hydropower, and other industrial and civil buildings, so as to improve the servic...

Embodiment 3

[0024] This example provides a concrete anti-corrosion and anti-corrosion agent and its preparation method. Using the tailings slag of the non-ferrous metal deposits in Northwest China, the colored tailings slag extract is extracted from the tailings slag by chemical leaching, and the extract includes different Shaped silica, calcium oxide, aluminum oxide and rare metal oxides, the weight ratio of each component in the extract is: amorphous silica 75-80%, calcium oxide 5-6%, trioxide Dialuminum 5-6%, rare metal oxide 5-7%, other balance.

[0025] The above-mentioned colored tailings slag extract is crushed to form a mixture of ultrafine particles with a particle size of 50-80 nm, and the concrete corrosion-resistant and anti-corrosion agent of the present invention is obtained. The shelf life of the material is half a year, and it should be stored in a cool, ventilated, dry place, protected from the sun and rain, and the storage temperature is 5~35°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a concrete corrosion-resistant preservative which comprises raw materials selected from colored tailings extracts, wherein the colored tailings extracts contain amorphous silica, calcium oxide, aluminum oxide and rare metal oxide; proportions of various substances in the colored tailings extracts are as follows: 70-80% of amorphous silica, 5-10% of calcium oxide, 5-10% of aluminum oxide, 5-8% of rare metal oxide and the balance of other substances; the colored tailings extracts are ultrafine nano-particles having a particle diameter of 1-100 nm. An application method ofthe concrete corrosion-resistant preservative provided by the invention comprises the following steps: adding a corrosion-resistant preservative into a concrete material in an amount of 5%-20% by weight of 1 part of cement, uniformly dispersing the corrosion-resistant preservative into the concrete, stirring for hydration reaction with the cement, and solidifying to form a concrete structure withgood corrosion resistance, preservative property and durability.

Description

technical field [0001] The invention relates to a corrosion-resistant and anti-corrosion agent for concrete, in particular to a corrosion-resistant and anti-corrosion agent made of colored tailings slag extract, which can improve the resistance to seawater erosion and harmful chemical substances of concrete when added to concrete. Increase the strength and aging resistance of concrete, and can be widely used in reinforced concrete structures such as marine engineering, port terminals, bridges and tunnels, coastal engineering, water conservancy and hydropower, and other industrial and civil buildings to improve the service life of concrete structures. Background technique [0002] Pollution from the development of non-ferrous metal minerals is very common in our country, and the harm caused is even more shocking. Generally speaking, some unusable "tailings" will be produced in the mining of various mineral resources, which will pollute the natural environment such as air and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B22/06C04B103/60
CPCC04B40/0039C04B2103/60C04B14/06C04B22/064C04B14/303C04B14/30C04B28/04
Inventor 王东林何鸣赵希娟韩宇栋王玮徐雪萍
Owner CENT RES INST OF BUILDING & CONSTR CO LTD MCC GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com