Preparing process of alginate fiber fleece type fabric

A seaweed fiber and preparation technology, applied in the textile field, can solve the problems of dissolution, difficulty in popularization, and low market share

Inactive Publication Date: 2018-07-31
三问家居股份有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Seaweed fiber technology has become increasingly mature in the textile industry. How to dissolve sodium alginate to form spinning viscous solution and prepare spinning stock solution has become stable, but the price and people's awareness have not made seaweed fiber popularize. At present, the market share is not high, so there are not many yarn fa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 1) Seaweed fiber yarn: prepare a sodium alginate solution with a mass fraction of 5%, add 2% chitosan powder with hydrophilic negatively charged functional groups, then add an organic solvent of ethanol-water-acetone and stir well to obtain sodium alginate Spinning liquid, and then carry out wet spinning and spinning, the spinning temperature is controlled at 65°C, the spinning speed is controlled at 50m / min, the viscosity activation energy of the spinning liquid is controlled at 18kJ / mol, and seaweed fiber yarn with antibacterial function is obtained ;

[0037] 2) Weft knitting: Use a loop-cutting terry machine with a tube diameter of 762mm, machine size 22 needles / 25.4mm, number of channels 60F, weft knitting with bottom yarn and surface yarn; bottom yarn: 20% polyester filament FDY75D / 96F; face yarn: 80% seaweed fiber yarn and modified polyester filament blended, of which 21s 10wt% seaweed fiber yarn, 90wt% modified polyester filament DTY 150 / 288F matte flat, seawee...

Embodiment 2

[0042] 1) Seaweed fiber yarn: prepare a sodium alginate solution with a mass fraction of 10%, add 5% chitosan powder with hydrophilic negatively charged functional groups, then add an organic solvent of ethanol-water-acetone and stir well to obtain sodium alginate Spinning solution, and then carry out wet spinning and spinning, the spinning temperature is controlled at 75°C, the spinning speed is controlled at 70m / min, the viscosity activation energy of the spinning solution is controlled at 20kJ / mol, and seaweed fiber yarn with antibacterial function is obtained ;

[0043] 2) Weft knitting: use a loop-cutting terry machine with a tube diameter of 762mm, machine size 22 needles / 25.4mm, number of channels 60F, weft knitting with bottom yarn and surface yarn; bottom yarn: 20% polyester filament FDY75D / 96F; face yarn: 80% seaweed fiber yarn and modified polyester filament mixed weaving, wherein 40s of 30wt% seaweed fiber yarn, 70wt% modified polyester filament DTY 150 / 288F matte...

Embodiment 3

[0048] 1) Seaweed fiber yarn: prepare a sodium alginate solution with a mass fraction of 12%, add 8% chitosan powder with hydrophilic negatively charged functional groups, then add an organic solvent of ethanol-water-acetone and stir well to obtain sodium alginate Spinning liquid, and then carry out wet spinning spinning, the spinning temperature is controlled at 80°C, the spinning speed is controlled at 90m / min, the viscosity activation energy of the spinning liquid is controlled at 25kJ / mol, and seaweed fiber yarn with antibacterial function is obtained ;

[0049] 2) Weft knitting: use a loop-cutting terry machine with a tube diameter of 762mm, machine size 22 needles / 25.4mm, number of channels 60F, weft knitting with bottom yarn and surface yarn; bottom yarn: 20% polyester filament FDY75D / 96F; face yarn: 80% seaweed fiber yarn and modified polyester filament mixed weaving, of which 40s 40wt% seaweed fiber yarn, 60wt% modified polyester filament DTY 150 / 288F matte flat, sea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Barrel diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparing process of an alginate fiber fleece type fabric. The process includes the following steps of A, conducting jet spinning on a sodium alginate solution to obtain alginate fiber yarn; B, conducting weft knitting and weaving on 20 wt% of bottom yarn and 80 wt% of surface yarn, wherein the bottom yarn is polyester filament yarn, and the surface yarn is prepared by blending alginate fiber yarn and modified polyester filament yarn; C, sequentially conducting unwinding, grey cloth carding and hemming on the fabric obtained in the step B, and then dyeing the hemmed fabric through positive ion red 3R; D, sequentially conducting washing, dewatering, drying, carding and ball rolling on the fabric obtained in the step C to obtain the alginate fiber fleece type fabric.In the preparing process of the alginate fiber fleece type fabric, the berber fleece fabric is obtained by blending the polyester filament yarn and the alginate fiber yarn, and the alginate fiber fleece type fabric is good in dyeing effect and high in color fastness by selecting specific dyes.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a preparation process of a seaweed fiber fleece fabric. Background technique [0002] In the cold winter, keeping warm is an eternal topic in the cold winter, and various home textile products made of lamb velvet fabric are a very good choice. Lamb velvet fabrics have been on the market for many years, but most of the improvements and updates in terms of hand feel, pattern or composite technology have greatly failed to meet the needs of customers. [0003] Seaweed fiber is a kind of man-made fiber, which is favored by people for its natural, environmental protection, and easy degradation characteristics. It also has functions such as far infrared, negative ions, and flame retardancy. It should make full use of renewable resources and save non-renewable petroleum resources. One must have the consciousness and consciousness that one should have. Seaweed fiber technology has beco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04B1/04D06P3/854D01F9/04D01F1/10
CPCD01F1/103D01F9/04D04B1/04D06P3/8228D10B2331/04D10B2401/13
Inventor 王耀民
Owner 三问家居股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com