A preparation of a silver carbonate modified molybdenum selenide composite photocatalyst
A technology of molybdenum diselenide and silver carbonate, which is applied in the field of material synthesis and photocatalysis, can solve the problems of molybdenum diselenide photocatalytic efficiency, stability and repeated use, and achieve good photocatalytic activity and catalytic activity improvement Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment example 1
[0045] Preparation of a silver carbonate-modified molybdenum diselenide composite photocatalyst.
[0046] Weigh Na 2 MoO 4 1.7g, dissolve in 60mL aqueous solution, stir well; then add 1.6g Se powder into the solution, stir well; then add NaBH 4 0.2595g, stir evenly; put the solution into a reaction kettle for hydrothermal reaction, the reaction temperature is 200°C, and the reaction time is 48h. After the reaction is completed, wash by centrifugation, first wash with ethanol for 4 times, then wash with water for 2 times, the centrifugation speed is 10000rpm, and the time is 6min. Finally, dry in an oven at 60°C and grind to obtain molybdenum diselenide.
[0047] Weigh 0.1g of molybdenum diselenide and disperse it in 50mL of water, add 0.616g of silver nitrate, stir evenly; then add 0.191g of sodium carbonate, and ultrasonicate for 1h. The product is centrifugally washed and dried to obtain a silver carbonate-modified molybdenum diselenide composite photocatalyst.
Embodiment example 2
[0049] Silver carbonate-modified molybdenum diselenide composite photocatalyst degrades methyl orange under visible light irradiation.
[0050] The silver carbonate-modified molybdenum diselenide composite photocatalyst prepared by the method of Example 1 was subjected to the experiment of degrading methyl orange. The concentration of methyl orange solution is 1×10 -5 mol L -1 Take 50 mg of composite material powder, place in 100 mL of the above-mentioned methyl orange solution, stir in a dark room for 60 minutes, then place the solution in a visible light source where ultraviolet light is filtered out, take 5 mL of methyl orange solution every 10 minutes, The characteristic peak of methyl orange in the solution was measured by UV-Vis spectrophotometer.
[0051] Obtain the degradation curve of silver carbonate modified molybdenum diselenide composite photocatalyst visible light degradation methyl orange by implementation case 2, see figure 2 . From figure 2 It can be se...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap