What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for power poles and towers, anti-rat bites, applied in the field of power poles and towers, can solve the problems of heavy wooden poles of power poles and towers, and achieve the effects of improving oxidation resistance, hardness and toughness, and fast plasticization speed
Inactive Publication Date: 2018-09-28
HEFEI HAIYIN TOWER
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Among them, the existing power poles and towers are relatively heavy except wooden poles, so a new type of pole belt with light weight and compression resistance is needed to meet market demand
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] The anti-rat-biting special power tower formula of the present invention is made of the following raw materials in parts by weight: 100 parts of SG type resin, 2 to 4 parts of tribasic lead sulfate, 35 to 45 parts of nano calcium carbonate, 0.5-1.5 parts of lead phosphite, 1-2 parts of DOP, 1-3 parts of epoxidized soybean oil, 1-2 parts of metal soaps, 1.5-2 parts of triphenyl ester of phosphite, 0.2-0.6 parts of triazine-5UV-9 0.3-0.8 parts of polyethylene wax, 2-4 parts of ACR, 4-6 parts of CPE, 3-5 parts of calcium carbonate, 0.7-1.5 parts of capsaicinoids, 2-2 parts of o-cumyl methyl carbamate 6 parts, 1-2 parts of 2-dimethylcyclopropane carboxylate.
[0016] Further, the SG type resin is perchlorethylene resin.
[0017] Further, the calcium carbonate is light calcium carbonate.
[0018] Further, the metal soap is one of calcium stearate or zinc stearate.
Embodiment 2
[0020] A formula for anti-rat bite special power poles and towers according to the present invention is made of the following raw materials in parts by weight: 100 parts of SG resin, 3 parts of tribasic lead sulfate, 40 parts of nanometer calcium carbonate, dibasic lead phosphite 1 part, 1.5 parts of DOP, 2 parts of epoxidized soybean oil, 1.5 parts of metal soaps, 1.8 parts of triphenyl phosphite, 0.4 parts of triazine-5UV-9, 0.6 parts of polyethylene wax, 3 parts of ACR, 5 parts of CPE, 4 parts of calcium carbonate, 1 part of capsaicinoids, 4 parts of o-cumyl methyl carbamate, 1.4 parts of 2-dimethylcyclopropane carboxylate.
[0021] Further, the SG type resin is perchlorethylene resin.
[0022] Further, the calcium carbonate is light calcium carbonate.
[0023] Further, the metal soap is one of calcium stearate or zinc stearate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of power pole towers, and concretely discloses a rat-bite-preventing special power pole tower formula, which is prepared from the following raw materials in parts by weight: 100 parts of SG resin, 2 to 4 parts of tribasic lead sulfate, 35 to 45 parts of nanometer calcium carbonate, 0.5 to 1.5 parts of dibasic lead phosphite, 1 to 2 parts of DOP, 1 to 3parts of epoxidized soybean oil, 1 to 2 parts of metallic soap, 1.5 to 2 parts of triphenyl phosphite, 0.2 to 0.6 part of triazine-5UV-9, 0.3 to 0.8 part of polyethylene wax, 2 to 4 parts of ACR, 4 to6 parts of CPE, 3 to 5 parts of calcium carbonate, 0.7 to 1.5 parts of capsaicine, 2 to 6 parts of O-isopropylphenyl methyl carbamate and 1 to 2 parts of 2-dimethyl cyclopropane carboxylate. The formula provided by the invention overcomes the defects in the prior art; rat-repelling ingredients prepared from the capsaicine, the O-isopropylphenyl methyl carbamate and the 2-dimethyl cyclopropane carboxylate are added; nontoxicity and harmlessness are realized; the environment pollution cannot occur; for the best advantage, rat repelling effects can be achieved; the plastic power pole tower is prevented from being bit by rats.
Description
technical field [0001] The invention relates to the technical field of power poles and towers, in particular to a formula for preventing rodent bite special power poles and towers. Background technique [0002] The pole tower is one of the basic equipment in the overhead power distribution line. According to the materials used, it can be divided into three types: wooden poles, cement poles and metal poles. Cement rods have the advantages of long service life and small maintenance workload, and are widely used. The most used cement rod is the tip rod, the taper is generally 1 / 75, which is divided into ordinary reinforced concrete rods and prestressed reinforced concrete rods. [0003] Wherein existing electric pole tower is all heavier except wooden pole, therefore needs a kind of light-weight compression-resistant novel pole belt to satisfy market demand. Contents of the invention [0004] The purpose of the present invention is to provide a formula for rat-biting specia...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 