Application method of single body entry type ceramic wood

A technology of ceramics and monomers, applied in wood treatment, impregnation of wood, wood impregnation, etc., can solve the problems of easy deformation, mildew, corrosion, uneven polymer, and decline in waterproof performance of wood, so as to achieve the goal of not being easy to dry and crack, and preventing Good moth performance and high utilization rate

Active Publication Date: 2018-11-13
中吉亚(山东)新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, anti-corrosion and waterproof materials are used for treatment. At present, the most used is to apply anti-corrosion paint on the surface of wood products, but the anti-corrosion paint is only on the surface of the wood. Once the anti-corrosion paint on the surface of the wood is damaged, the anti-corrosion and waterproof performance of the wood will decline, and the wood will be easily damaged. Deformation, mildew, corrosion, etc., at the same time, formaldehyde, benzene, and TVOC total volatile organic compounds in paint can cause dizziness, headache, chest tightness, weakness of limbs, and coughing, etc. Long-term exposure can cause aplastic anemia, leukemia, Serious diseases such as tuberculosis and pleurisy, and even cancer, are extremely harmful to the human body and difficult to eliminate
Therefore, log products are becoming more and more popular now. In order to improve the performance of logs, timber merchants use many methods to manufacture anti-corrosion and waterproof wood. At present, the anti-corrosion wood on the market is treated with preservatives. Erosion by drilling animals, etc., but it is easily soluble in water, and it is easy to fail when exposed to water
[0004] In the past, the treatment of wood was mainly aimed at the defects of biological hazards. At present, high molecular polymers are used to make ceramic wood to enhance the properties of wood corrosion and strength, and at the same time reduce the defects of wood during drying and mechanical processing. During the preparation process, it is difficult for the polymer to penetrate into the wood, and it is easy to cause uneven penetration of the polymer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application method of single body entry type ceramic wood
  • Application method of single body entry type ceramic wood
  • Application method of single body entry type ceramic wood

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The present invention will be further described in detail below in combination with specific embodiments.

[0033] The use method of single entry type ceramic wood, ceramic wood is manufactured through the following steps:

[0034] (1) Prepare a storage container, add phenylacetic anhydride and sodium hydroxide into the storage container, stir to mix the two raw materials evenly, then add water, and then stir rapidly to make phenylacetic anhydride and sodium hydroxide use their own exothermic A reaction occurs to produce a clear, colorless solution.

[0035] (2) Put the wood into the reservoir containing the transparent and colorless solution generated in step (1), and seal the reservoir at room temperature for 10 to 24 hours, allowing the transparent and colorless solution generated in step (1) to enter the wood Inside, take out the wood after finishing;

[0036](3) Prepare a stainless steel storage tank, add diethyl ether solvent in the stainless steel storage tank,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an application method of single body entry type ceramic wood. During ceramic wood preparing, sodium phenylacetate and chloropropene prepared through the reaction of phenylacetic acid and sodium hydroxide enters wood, allyl phenylacetate is generated, then, a high-molecular polymer is generated, and a net-shaped structure is formed by the high-molecular polymer and wood fiber. The interior-exterior structure, rigidity and strength of the ceramic wood can be consistent, and the interior and exterior waterproof performance, corrosion resisting performance, mothproof performance, anti-mold performance, safety performance and size stability of the ceramic wood are guaranteed, and therefore the ceramic wood can be directly used on the premise that coating of a coat is notconducted; and when the surface of the ceramic wood is old-fashioned, the performance of the ceramic wood is not influenced after grinding.

Description

technical field [0001] The present invention relates to the use method of ceramic wood. Background technique [0002] Wood plays a great supporting role in human life. According to the different properties and characteristics of wood, people use them in different ways, such as furniture, decoration materials, building materials, artworks and so on. However, due to the composition and structure of the wood itself, it is prone to biological hazards such as decay, discoloration, and insects. At the same time, it is easy to crack, warp, and kerf defects during drying and mechanical processing. These defects reduce the quality of the wood. use value. [0003] In order to improve the use range and service time of wood products, some treatments need to be done to the wood. Usually, anti-corrosion and waterproof materials are used for treatment. At present, the most used is to apply anti-corrosion paint on the surface of wood products, but the anti-corrosion paint is only on the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/08B27K3/52
CPCB27K3/08B27K3/52B27K2240/20
Inventor 杨海景黄玉真王荣克谢煌
Owner 中吉亚(山东)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products