Ink printing method for glass cover plate

A technology of ink printing and glass substrate, which is applied in the direction of ink, printing, printing devices, etc., can solve the problems of insufficient improvement of product effect, low reduction of total ink thickness, and insufficient shading of white ink layer, etc., to reduce the risk of air bubbles , the effect of improving light-shielding property and reducing the total thickness

Active Publication Date: 2020-03-24
JIANGXI HOLITECH TECH
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the insufficient shading of the white ink layer, it is still necessary to print about 3 layers of white ink, the reduction in the total thickness of the ink is relatively low, and the product effect is not significantly improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink printing method for glass cover plate
  • Ink printing method for glass cover plate
  • Ink printing method for glass cover plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A white ink layer with a thickness of 6-8 μm is printed on the glass substrate of the touch screen. The components of the white ink are epoxy resin, titanium dioxide, solvent, dispersant, defoamer, leveling agent, additive and modified nano zinc oxide, and the additive is 4-aminobenzoic acid, maleic acid, Mixture of p-toluenesulfonic acid and sebacic acid. In the white ink, each component is calculated in parts by weight as:

[0030]

[0031]

[0032] Among them, the solvent is a mixture of ethylene glycol ether acetate and ethyl acetate, wherein the volume ratio of ethylene glycol ether acetate and ethyl acetate is 10:2; the modified nano-zinc oxide is nano-zinc oxide processed by vinyl triethyl Oxysilane modification treatment obtains; Dispersant, defoamer and leveling agent can adopt any one in the prior art all can, the present invention does not make special requirement, in order to improve the contrast of experiment, in the specific embodiment of the presen...

Embodiment 2

[0046] A white ink layer with a thickness of 6-8 μm is printed on the glass substrate of the touch screen. The components of the white ink layer are epoxy resin, titanium dioxide, solvent, dispersant, defoamer, leveling agent, additive and modified nano-zinc oxide, and the additive is 4-aminobenzoic acid, maleic acid , a mixture of p-toluenesulfonic acid and sebacic acid. In the white ink, each component is calculated in parts by weight as:

[0047]

[0048] Among them, the solvent is a mixture of ethylene glycol ether acetate and ethyl acetate, wherein the volume ratio of ethylene glycol ether acetate and ethyl acetate is 10:3; the modified nano-zinc oxide is nano-zinc oxide processed by vinyl triethyl Oxysilane modified treatment obtained.

[0049] Each component in the additive is counted as:

[0050]

[0051] The preparation method of described white ink is:

[0052] (1) Get each ink component by the weight part quantity, the solvent is divided into two parts of A ...

Embodiment 3

[0062] A white ink layer with a thickness of 6-8 μm is printed on the glass substrate of the touch screen. The components of the white ink layer are epoxy resin, titanium dioxide, solvent, dispersant, defoamer, leveling agent, additive and modified nano zinc oxide, and the additive is 4-aminobenzoic acid, maleic acid , a mixture of p-toluenesulfonic acid and sebacic acid. In the white ink, each component is calculated in parts by weight as:

[0063]

[0064] Among them, the solvent is a mixture of ethylene glycol ether acetate and ethyl acetate, wherein the volume ratio of ethylene glycol ether acetate and ethyl acetate is 10:4; the modified nano-zinc oxide is nano-zinc oxide processed by vinyl triethyl Oxysilane modified treatment obtained.

[0065] Each component in the additive is counted as:

[0066]

[0067] The preparation method of described white ink is:

[0068] (1) Get each ink component by the weight part quantity, the solvent is divided into two parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a printing ink printing method. One to two white printing ink layers are printed on the edge of a glass substrate of a touch screen, each white printing ink layer is of a frame-shaped structure, a black printing ink layer is further printed on each white printing ink layer and is of a frame-shaped structure, the inner edge of each black printing ink layer is located on theinner side of the inner edge of the corresponding white printing ink layer, and a black frame of the touch screen is formed by areas between the inner edges of the black printing ink layers and the inner edges of the white printing ink layers. The method is characterized in that components of each white printing ink layer comprise epoxy resin, titanium dioxide, a solvent, a dispersion agent, a defoaming agent, a flatting agent, an additive and modified nano-zinc oxide; and the additive is a mixture of 4-aminobenzoic acid, maleic acid, p-toluenesulfonic acid and sebacic acid. According to the method, the total thickness of the printing ink layers is greatly reduced, the risk that bubbles are generated in the capacitance screen attachment process is reduced, and therefore the yield is increased.

Description

technical field [0001] The invention belongs to the technical field of electronic equipment production and processing, and in particular relates to an ink printing method for a glass cover plate. Background technique [0002] With the development of science and technology, touch-screen mobile phones are more and more favored by users, and the screen size of mobile phones becomes larger and larger. At present, in the capacitive screen manufacturing industry, the manufacture of the white model is more difficult than the black model. The reasons are: first, the cover plate is white, and the color of the TFT display module window is black. When the two are bonded together, there will inevitably be a bonding tolerance. According to the different equipment and process conditions of each factory, it is also different. Generally, the deviation is 0.1-0.2mm. Under this deviation, there will be a situation of large and small sides. In order to solve this problem, the industry will use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41M1/18B41M1/34C09D11/03C09D11/102
CPCB41M1/18B41M1/34C09D11/03C09D11/102
Inventor 张文清
Owner JIANGXI HOLITECH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com