A kind of silicon dioxide for toothpaste with antibacterial properties and preparation method thereof

A technology of silicon dioxide and toothpaste, applied in the direction of silicon dioxide, silicon oxide, medical preparations containing active ingredients, etc., can solve the problems of low loading rate, easy loss of silver and zinc ions, etc., and achieve high loading rate and toothpaste production. Convenience, the effect of simplified toothpaste formulation

Active Publication Date: 2019-04-30
GUANGZHOU FEIXUE MATERIAL TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve technical problems such as the low loading rate of the existing silica / silver-zinc antibacterial agent composite material and the easy loss of silver-zinc ions, the invention provides a method for preparing silica for toothpaste with antibacterial properties. In the process of preparing precipitated silica, silver-zinc ions are added to make them evenly dispersed and tightly combined, and then a layer of shell is further wrapped around the inner core to ensure that the silver-zinc ions are not easily lost and released slowly during use. At the same time, the Silica also maintains good tooth friction cleaning performance, suitable for toothpaste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of silicon dioxide for toothpaste with antibacterial properties and preparation method thereof
  • A kind of silicon dioxide for toothpaste with antibacterial properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, silicon dioxide for toothpaste with antibacterial properties of the present invention and its preparation

[0026] S1, adding 6m of sodium sulfate solution with a mass percentage concentration of 3% in the reaction tank 3 , then add sodium silicate solution 10m 3 and a concentration of 1.0mol / L zinc sulfate solution 2m 3 , heated up to 60°C, and stirred at a speed of 20Hz at 1.0m 3 Add sulfuric acid at a flow rate of / h, keep the reaction temperature at 60°C, add sulfuric acid dropwise until the pH value at the end of the reaction is 8.0, and obtain a silica / antibacterial agent composite inner core mixture;

[0027] S2. Heat up the silicon dioxide / antibacterial agent composite inner core mixture to 80°C, stir at a speed of 35Hz at 10m 3 Add sodium silicate solution 7m at a flow rate of / h 3 , while at 1.0m 3 Add sulfuric acid at a flow rate of / h and keep the reaction temperature at 80°C. After adding the sodium silicate solution, continue to add sulf...

Embodiment 2

[0029] Embodiment 2, silicon dioxide for toothpaste with antibacterial properties of the present invention and its preparation

[0030] S1, adding 8m of sodium sulfate solution with a mass percentage concentration of 6% in the reaction tank 3 , then add sodium silicate solution 11m 3 And concentration is 3.0mol / L silver nitrate solution 4m 3 , heated up to 70°C, and stirred at a speed of 30Hz at 2.0m 3 Add sulfuric acid at a flow rate of / h, keep the reaction temperature at 70°C, add sulfuric acid dropwise until the pH value at the end of the reaction is 9.0, and obtain a silica / antibacterial agent composite inner core mixture;

[0031] S2. Heat up the silicon dioxide / antibacterial agent composite inner core mixture to 90°C, stir at 40Hz at a speed of 14m 3 / h flow rate into sodium silicate solution 9m 3 , while at 2.0m 3Add sulfuric acid at a flow rate of / h and keep the reaction temperature at 90°C. After adding the sodium silicate solution, continue to add sulfuric aci...

Embodiment 3

[0033] Embodiment 3, silicon dioxide for toothpaste with antibacterial properties of the present invention and its preparation

[0034] S1, adding 7m of sodium sulfate solution with a mass percentage concentration of 4% in the reaction tank 3 , then add sodium silicate solution 10m 3 And the concentration is 2.0mol / L zinc sulfate solution 3m 3 , heated up to 65°C, and stirred at a speed of 25Hz at 1.5m 3 Add sulfuric acid at a flow rate of / h, keep the reaction temperature at 65°C, add sulfuric acid dropwise until the pH value at the end of the reaction is 8.5, and obtain a silica / antibacterial agent composite inner core mixture;

[0035] S2. Heat up the silicon dioxide / antibacterial agent composite inner core mixture to 85°C, stir at 35Hz at a speed of 12m 3 Add sodium silicate solution 8m at a flow rate of / h 3 , while at 1.5m 3 Add sulfuric acid at a flow rate of / h and keep the reaction temperature at 85°C. After adding the sodium silicate solution, continue to add su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
oil absorption valueaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

Provided are silicon dioxide for a toothpaste having antibacterial properties and a preparation method therefor. The method comprises: adding a sodium sulfate solution to a reaction tank, then adding a sodium silicate solution and an inorganic antibacterial agent, heating to 60-70ºC, and adding sulfuric acid while stirring till the end pH value is 8.0-9.0 to obtain a core; and heating the core to 80-90ºC, adding a sodium silicate solution and sulfuric acid while stirring, after finishing adding the sodium silicate solution, continuing dropping sulfuric acid till the pH value is 3.0-5.0, aging for 1-3 h, and then performing pressure filtration, washing, drying, and crushing to obtain the silicon dioxide for a toothpaste having antibacterial properties. The silver and zinc ions of the obtained silicon dioxide has a high loading rate, the silicon dioxide has a bacteriostasis rate of 98% or more for Bacillus coli, etc.; the silver and zinc ions would not easy to lose, the silicon dioxide has a lasting effect, also has abrasive cleaning properties, can be applied to a toothpaste as abrasive agent and a preservative, so that the toothpaste formulation is simplified.

Description

technical field [0001] The invention belongs to the technical field of silicon dioxide, and in particular relates to silicon dioxide for toothpaste with antibacterial properties and a preparation method thereof. Background technique [0002] Abrasives account for a large proportion in the toothpaste formula. Abrasives can remove dirt on the surface of teeth. Good abrasives not only have the effect of cleaning teeth and removing plaque, but also cannot cause excessive wear and tear on teeth. Silica is a spherical porous structure without sharp edges and corners that will not wear teeth too much. It has stable physical and chemical properties, strong cleaning ability, good compatibility with toothpaste systems, and can be used for the preparation of transparent toothpaste. Has been widely used in the toothpaste industry. However, the rich and porous structure of silica also makes it easy for microorganisms to multiply due to factors such as improper storage methods and enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/12A61K8/25A61K8/19A61K8/27A61Q11/00A61P1/02A61P31/02A61P31/04
CPCA61K8/19A61K8/25A61K8/27A61K2800/524A61P1/02A61P31/02A61P31/04A61Q11/00C01B33/12C01P2004/61C01P2006/19Y02A50/30
Inventor 侯灿明林英光胡非李丽峰张梦梅
Owner GUANGZHOU FEIXUE MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com