Carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst as well as preparation method and application thereof

A denitrification catalyst and carbon nanotube technology, applied in the field of pollution prevention and control, can solve the problems of narrow active window, poor water and sulfur resistance, etc., and achieve the effect of enhancing water and sulfur resistance and slowing down the poisoning effect

Active Publication Date: 2018-11-30
TAIYUAN UNIV OF TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Recently, Chinese patent (CN201610671758.7) reported that compared with supported CuO / γ-Al 2 o 3 , Cu prepared by calcination of CuAl hydrotalcite-like precursor x AlO y With better low temperature NH 3 - SCR catalytic activity, but problems such as narrow activity window and poor water and sulfur resistance performance still need to be further optimized and solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst as well as preparation method and application thereof
  • Carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst as well as preparation method and application thereof
  • Carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Take 20ml respectively and the concentration is 0.5 mol L -1 Aqueous solution of aluminum nitrate nonahydrate and 20ml concentration of 1.0 mol L -1 Add the copper nitrate trihydrate aqueous solution to the beaker, and stir with a magnetic stirrer for 10min to make it evenly mixed, and transfer the prepared salt solution to the dropping funnel 1 for later use;

[0037] (2) Take 200ml and make the concentration 1.00 mol L -1 aqueous sodium hydroxide solution, which is transferred to the dropping funnel 2 for later use;

[0038] (3) Take 8ml and the concentration is 30 g L -1The oxidized carbon nanotube dispersion liquid is placed in a beaker, and the sodium hydroxide aqueous solution and the mixed salt solution are dropped into the above dispersion liquid at the same time under magnetic stirring, and the pH value during the titration process is monitored in real time with an acidity meter, and the titration speed is controlled to make the whole reaction During the...

Embodiment 2

[0042] (1) Take 20ml respectively and the concentration is 0.5 mol L -1 Aqueous solution of aluminum nitrate nonahydrate and 30ml concentration of 1.0 mol L -1 Add the copper nitrate trihydrate aqueous solution to the beaker, and stir it with a magnetic stirrer for 10 min to make it evenly mixed, and transfer the prepared salt solution to the dropping funnel 1 for later use;

[0043] (2) Take 200ml and make the concentration 1.00 mol L -1 aqueous sodium hydroxide solution, which is transferred to the dropping funnel 2 for later use;

[0044] (3) Take 25ml and the concentration is 30 g L -1 The oxidized carbon nanotube dispersion liquid is placed in a beaker, and the sodium hydroxide aqueous solution and the mixed salt solution are dropped into the above dispersion liquid at the same time under magnetic stirring, and the pH value during the titration process is monitored in real time with an acidity meter, and the titration speed is controlled to make the whole reaction proce...

Embodiment 3

[0048] (1) Weigh 20ml respectively to a concentration of 0.5 mol L -1 The concentration of aluminum nitrate nonahydrate aqueous solution and 40ml is 1 mol L -1 Copper nitrate trihydrate was mixed into the beaker, and stirred with a magnetic stirrer for 10 min to make it evenly mixed, and the prepared salt solution was transferred to the dropping funnel for use

[0049] (2) Take 200ml and make the concentration 1.00 mol L -1 aqueous sodium hydroxide solution, which is transferred to the dropping funnel for use;

[0050] (3) Take 60ml of concentration to be 30 g L -1 The oxidized carbon nanotube dispersion liquid is placed in a beaker, and the sodium hydroxide aqueous solution and the mixed salt solution are dropped into the above dispersion liquid at the same time under magnetic stirring, and the pH value during the titration process is monitored in real time with an acidity meter, and the titration speed is controlled to make the whole reaction During the process, the pH va...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst as well as a preparation method and application thereof and belongs to the technical field ofpollution control. The carbon nanotube doped copper-aluminum compound metal oxide denitration catalyst (CuAl-LDO / CNTs) is prepared by dropwise adding an aluminum nitrate and copper nitrate mixed solution and an NaOH alkaline solution into a dispersion solution mixed with modified carbon nanotubes, controlling the synthesis pH value within the range of 4.50-5.50, and carrying out hydrothermal crystallization, suction filtration washing and drying to prepare a carbon nanotube doped CuAl hydrotalcite precursor (CuAl-LDH / CNTs); and then, roasting the carbon nanotube doped CuAl hydrotalcite precursor at a nitrogen atmosphere. Denitration activity test and sulfur resistance evaluation prove that the catalyst CuAl-LDO / CNTs has high NH3-SCR activity and N2 selectivity as well as strong water and sulfur resistance in a low-temperature region (180-300 DEG C).

Description

technical field [0001] The invention relates to a catalyst and a preparation method thereof, in particular to a catalyst for low-temperature NH 3 - CuAl-LDO / CNTs denitrification catalyst for SCR reaction, belonging to the technical field of pollution prevention and control. Background technique [0002] Along with the treatment and research of coal-fired flue gas, the catalytic denitrification technology of coal-fired flue gas has been developed rapidly. Ammonia Selective Catalytic Reduction (NH 3 -SCR) has become the most promising coal-fired flue gas denitrification technology in commerce due to its high efficiency, good selectivity, and low cost. However, the mature V 2 o 5 -WO 3 / TiO 2 The high working temperature of denitrification catalysts (300-400 ℃) cannot well meet the denitrification technical requirements of small and medium-sized industrial boilers. Therefore, the development of efficient, stable and environmentally friendly low-temperature denitrificatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/72B01D53/86B01D53/56
CPCB01D53/8628B01D2258/0283B01J23/72
Inventor 吴旭孟浩刘江宁侯本辉次超
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com