A preparation process of multiple coupling superhydrophobicity on the surface of 304 stainless steel

A technology of 304 stainless steel and preparation process, which is applied in the field of multi-coupling super-hydrophobic preparation technology on the surface of 304 stainless steel, can solve the problems of poor hydrophobicity on the surface of 304 stainless steel, and achieve the effects of prolonging durability, saving resources and reducing energy consumption.

Active Publication Date: 2021-01-05
CHANGCHUN UNIV OF SCI & TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems existing in the prior art, the present invention provides a 304 stainless steel surface multi-coupled super-hydrophobic preparation process, which solves the problem of poor hydrophobicity of the prepared 304 stainless steel surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation process of multiple coupling superhydrophobicity on the surface of 304 stainless steel
  • A preparation process of multiple coupling superhydrophobicity on the surface of 304 stainless steel
  • A preparation process of multiple coupling superhydrophobicity on the surface of 304 stainless steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017]The present invention will be further described in detail below in conjunction with the drawings and embodiments.

[0018]Such asfigure 1 As shown, a 304 stainless steel surface multiple coupling superhydrophobic preparation process, the preparation process includes the following steps:

[0019]Step 1: Initial grinding treatment: Grind the substrate on 600 mesh, 1000 mesh, 1500 mesh, and 2000 mesh sandpaper in order to make the surface smooth;

[0020]Step 2: Polishing treatment: Polish the pre-grinded substrate on a polishing machine to make the surface of the substrate smooth; then place the polished substrate in deionized water for ultrasonic cleaning for 4 minutes and then use deionized water Rinse for 30s;

[0021]Step 3: Perform the first sandblasting on the surface of the substrate: Put the substrate in the spraying room for sandblasting. The sandblasting parameters are: sandblasting pressure 0.55MPa, sandblasting grit is 120 mesh; after the first sandblasting Carry out ultrasonic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a 304 stainless steel surface multielement coupling super-hydrophobic preparation method, and belongs to the field of metal part and material surface super hydrophobicity. The304 stainless steel surface multielement coupling super-hydrophobic preparation method is capable of solving the adverse hydrophobic problem of the surface of prepared 304 stainless steel. The 304 stainless steel surface multielement coupling super-hydrophobic preparation method comprises following steps: polishing, a first time of sandblasting, monopulse deposition, a second time of sandblasting,and drying. The 304 stainless steel surface multielement coupling super-hydrophobic preparation method is capable of obtaining grading scale structures (submillimeter grade, and micrometer-nanometergrade) of the 304 stainless steel hydrophobic surface, wherein the scale of a cauliflower-like protruding main structure formed through monopulse deposition on a matrix is micrometer-nanometer grade,the scale of second time sandblasting formed surface destroyed cauliflower-like protrudings and protruding gaps is submillimeter grade; a rough structure formed through the first time of sandblastingis capable of increasing the bonding force of the coating layer with the matrix, a rough structure formed through the second time of sandblasting is capable of forming a multi-scale multi-stage microstructure on coating surfaces, and surface hydrophobicity is improved.

Description

Technical field[0001]The invention relates to the field of preparation of super-hydrophobicity on the surface of metal parts and materials, in particular to a preparation process of multi-coupled super-hydrophobicity on the surface of 304 stainless steel.Background technique[0002]In modern industrial production and daily life, stainless steel has played an irreplaceable role. Due to its good mechanical properties, low temperature resistance, corrosion resistance, abrasion resistance and excellent process performance, it has been widely used in various industries, including automobiles, kitchen appliances, ships, aviation industry and medical equipment. With the development of industrial modernization, people's requirements for the use performance and process performance of stainless steel materials continue to increase. The traditional surface properties of stainless steel can no longer meet the requirements of multifunctional composite. At present, surface modification treatment of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D3/12C25D5/18C25D5/36C25D5/48
CPCC25D3/12C25D5/18C25D5/36C25D5/48
Inventor 李晶杜锋付强潘理达周璎珞郭旭东赵海洋
Owner CHANGCHUN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap